PolyOne Geon™ SF M7000 Polyvinyl Chloride, Rigid (PVC, Rigid)

Category Polymer , Thermoplastic , Vinyl (PVC) , PVC, Rigid Grade
Manufacturer PolyOne Corporation
Trade Name Geon™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF PolyOne Geon™ SF M7000 Polyvinyl Chloride, Rigid (PVC, Rigid).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by PolyOne
Physical Properties Metric English Comments
Specific Gravity 1.33 g/cc
1.33 g/cc
ASTM D792
Linear Mold Shrinkage, Flow 0.0020 - 0.0050 cm/cm
0.0020 - 0.0050 in/in
ASTM D955
Spiral Flow 119.38 cm
47.000 in
Mechanical Properties Metric English Comments
Hardness, Shore D 79
79
ASTM D2240
Tensile Strength, Yield 41.4 MPa
6000 psi
Type I, 51 mm/min; ASTM D638
Elongation at Break 35 %
35 %
Type I, 51 mm/min; ASTM D638
Tensile Modulus 2.28 GPa
331 ksi
Type I, 51 mm/min; ASTM D638
Flexural Strength 62.7 MPa
9090 psi
ASTM D790
Flexural Modulus 2.31 GPa
335 ksi
ASTM D790
Izod Impact, Notched 1.10 J/cm

@Thickness 3.18 mm,
Temperature -18.0 °C
 2.06 ft-lb/in

@Thickness 0.125 in,
Temperature -0.400 °F
 Injection Molded; ASTM D256A
2.70 J/cm

@Thickness 3.18 mm,
Temperature 0.000 °C
 5.06 ft-lb/in

@Thickness 0.125 in,
Temperature 32.0 °F
 Injection Molded; ASTM D256A
6.40 J/cm

@Thickness 3.18 mm,
Temperature 23.0 °C
 12.0 ft-lb/in

@Thickness 0.125 in,
Temperature 73.4 °F
 Injection Molded; ASTM D256A
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 67.2 °C

@Thickness 3.18 mm
 153 °F

@Thickness 0.125 in
 Unannealed; ASTM D648
71.1 °C

@Thickness 3.18 mm
 160 °F

@Thickness 0.125 in
 Annealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 60.0 °C

@Thickness 3.18 mm
 140 °F

@Thickness 0.125 in
 Unannealed; ASTM D648
70.0 °C

@Thickness 3.18 mm
 158 °F

@Thickness 0.125 in
 Annealed; ASTM D648
UL RTI, Electrical 90.0 °C
194 °F
UL 746
UL RTI, Mechanical with Impact 85.0 °C
185 °F
UL 746
UL RTI, Mechanical without Impact 90.0 °C
194 °F
UL 746
Flammability, UL94 V-0
V-0
5VA
5VA
V-0

@Thickness 1.80 mm
 V-0

@Thickness 0.0709 in
 ALL; UL 94
5VA

@Thickness 1.80 mm
 5VA

@Thickness 0.0709 in
 ALL; UL 94
5VA

@Thickness 1.60 mm
 5VA

@Thickness 0.0630 in
 All Colors
Processing Properties Metric English Comments
Melt Temperature 199 - 210 °C
390 - 410 °F
Descriptive Properties Value Comments
Features General Purpose
High Flow
High Impact Resistance
Forms Pellets
Generic Material PVC, Rigid
Generic Name Polyvinyl Chloride, Rigid (PVC, Rigid)
Processing Method Injection Molding
Regional Availability Africa & Middle East
Asia Pacific
Europe
North America
South America
RoHS Compliance RoHS Compliant
Uses Construction Applications
Electrical/Electronic Applications
General Purpose
Telecommunications