Ineos Nova 474 High Performance Styrenic Enhanced Polystyrene (discontinued **)
| Category | Polymer , Thermoplastic , Polystyrene (PS) |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ineos Nova 474 High Performance Styrenic Enhanced Polystyrene
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Custom ColorsApplications: Injection molding, Alternative to engineering resinsPerformance grades of polystyrene are engineered to have specific properties. These products can be custom colored. NOVA Chemicals can accurately match your color needs with its leading edge color technology. Injection Speed: FastColored material may differ in some properties. All molded samples were an 1/8 inch thick unless noted.Information provided by NOVA Chemicals.INEOS NOVA began October 1 2007 as an expansion of the 50:50 joint venture between NOVA Chemicals and INEOS to include North American assets.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0040 - 0.0060 cm/cm | 0.0040 - 0.0060 in/in | ASTM D955 |
| Melt Flow | 3.0 g/10 min @Load 5.00 kg, Temperature 200 °C |
3.0 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 34.0 MPa | 4930 psi | 2.0 in/min; ASTM D638 |
| Elongation at Break | 40 % | 40 % | 2.0 in/min; ASTM D638 |
| Flexural Strength | 48.0 MPa | 6960 psi | 0.1 in/min; ASTM D790 |
| Flexural Modulus | 2.48 GPa | 360 ksi | 0.1 in/min; ASTM D790 |
| Izod Impact, Notched | 0.910 J/cm | 1.70 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 85.0 °C | 185 °F | RTI |
| Deflection Temperature at 1.8 MPa (264 psi) | 91.0 °C | 196 °F | ASTM D648 |
| Vicat Softening Point | 103 °C | 217 °F | ASTM D648 |
| Flammability, UL94 | HB | HB | 0.058 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | <= 260 °C | <= 500 °F | |
| Rear Barrel Temperature | 182 - 204 °C | 360 - 399 °F | |
| Middle Barrel Temperature | 210 - 232 °C | 410 - 450 °F | |
| Front Barrel Temperature | 216 - 238 °C | 421 - 460 °F | |
| Melt Temperature | 216 - 238 °C | 421 - 460 °F | |
| Mold Temperature | 27.0 - 54.0 °C | 80.6 - 129 °F | |
| Drying Temperature | 68.0 °C | 154 °F | |
| Dry Time | 2 hour | 2 hour | |
| Back Pressure | 0.345 MPa | 50.0 psi |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics LNP LUBRICOMP DFL32 PC
- PolyOne Geon™ Vinyl Flexible B6DB1 Polyvinyl Chloride, Flexible (PVC, Flexible)
- LNP Lubricomp® GFL-4034 EM M Polysulfone, Milled Glass Fiber Reinforcement, PTFE Lubricant (discontinued **)&
- Mitsubishi Xantar® F 22 R Polycarbonate
- Saint-Gobain Normount® V4600 Energy-Dissipating High-Performance Polyurethane Foam with Acrylic Adhesive
- Dow DOWLEX™ NG 2085 Linear Low Density Polyethylene, Ethylene-Octene Copolymer
- Arkema Group LOTRYL® 28 BA 175 Copolymer Ethylene - Butyl Acrylate
- BASF Basantol® 415 Bordeaux Liquid
- Polyplastics Duracon® TD-20 Acetal Co-polymer (POM), High impact, Flexible
Copyright © lookpolymers.com All Rights Reserved