Wellman Wellamid® GF20-60 XE-N 20% Glass Fiber Reinforced Nylon 6, Lubricated & Heat Stabilized

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 20% Glass Fiber Filled
Manufacturer Wellman Engineering Resins
Trade Name Wellamid®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Wellman Wellamid® GF20-60 XE-N 20% Glass Fiber Reinforced Nylon 6, Lubricated & Heat Stabilized.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Typical Applications: Radio and TV components, dishwasher roller carriages, chain saw oil reservoirs, gears, housings, door & window latches, power hand tool housings, high temperature devices.Data provided by the manufacturer, Wellman Inc.
Physical Properties Metric English Comments
Density 1.27 g/cc
0.0459 lb/in³
ISO 1183
Water Absorption 1.3 %
1.3 %
Approximate 24 hr.
Linear Mold Shrinkage 0.0020 - 0.0060 cm/cm
0.0020 - 0.0060 in/in
ISO 294-4
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 135 MPa
19600 psi
ISO 527
Elongation at Break 4.0 %
4.0 %
ISO 527
Flexural Yield Strength 195 MPa
28300 psi
ISO 178
Flexural Modulus 5.80 GPa
841 ksi
ISO 178
Izod Impact, Notched 0.700 J/cm
1.31 ft-lb/in
ISO 180
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 200 °C
392 °F
ISO 75
Flammability, UL94 HB

@Thickness 0.790 mm
HB

@Thickness 0.0311 in
From Wellman QC Laboratory Testing; UL 94
Processing Properties Metric English Comments
Rear Barrel Temperature 260 - 282 °C
500 - 540 °F
Middle Barrel Temperature 254 - 277 °C
490 - 530 °F
Front Barrel Temperature 249 - 271 °C
480 - 520 °F
Nozzle Temperature 249 - 271 °C
480 - 520 °F
Melt Temperature 254 - 282 °C
490 - 540 °F
Mold Temperature 71.1 - 93.3 °C
160 - 200 °F
Drying Temperature 79.4 °C
175 °F
Opened bags and gaylord boxes
Dry Time 2 - 4 hour
2 - 4 hour
Opened bags and gaylord boxes
Moisture Content 0.050 - 0.20 %
0.050 - 0.20 %
During molding to prevent hydrolytic degradation
<= 0.20 %
<= 0.20 %
In shipping bags, ready to mold
Injection Pressure 34.5 - 138 MPa
5000 - 20000 psi
Back Pressure 0.345 MPa
50.0 psi
Screw Speed 30 - 120 rpm
30 - 120 rpm