Idemitsu Kosan Xarec® WA 550 SPS, 30% Glass Filled
| Category | Polymer , Thermoplastic , Polystyrene (PS) , Syndiotactic Polystyrene (SPS) , Syndiotactic Polystyrene (SPS) with Glass or Carbon Fiber |
| Manufacturer | Idemitsu Kosan Co., Ltd. |
| Trade Name | Xarec® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Idemitsu Kosan Xarec® WA 550 SPS, 30% Glass Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Crystalline Polymer, Glass Filled. Used in Automotive and Industrial applications
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.27 g/cc | 0.0459 lb/in³ | |
| Filler Content | 30 % | 30 % | |
| Water Absorption | 0.010 % | 0.010 % | 24 hrs., 50% RH |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm | 0.0010 - 0.0030 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0030 - 0.0060 cm/cm | 0.0030 - 0.0060 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 135 MPa | 19600 psi | |
| Elongation at Break | 1.8 % | 1.8 % | |
| Tensile Modulus | 10.0 GPa | 1450 ksi | |
| Flexural Yield Strength | 200 MPa | 29000 psi | |
| Flexural Modulus | 9.80 GPa | 1420 ksi | |
| Izod Impact, Notched (ISO) | 12.0 kJ/m² | 5.71 ft-lb/in² | |
| Izod Impact, Unnotched (ISO) | 39.0 kJ/m² | 18.6 ft-lb/in² | |
| Charpy Impact Unnotched | 4.70 J/cm² | 22.4 ft-lb/in² | |
| Charpy Impact, Notched | 1.30 J/cm² | 6.19 ft-lb/in² |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 20.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
11.1 µin/in-°F @Temperature -22.0 - 86.0 °F |
|
| CTE, linear, Transverse to Flow | 44.0 µm/m-°C | 24.4 µin/in-°F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 270 °C | 518 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | |
| UL RTI, Electrical | 120 °C | 248 °F | UL746B |
| UL RTI, Mechanical with Impact | 105 °C | 221 °F | UL746B |
| UL RTI, Mechanical without Impact | 105 °C | 221 °F | UL746B |
| Flammability, UL94 | HB @Thickness 0.750 mm |
HB @Thickness 0.0295 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | |
| Dielectric Constant | 3.1 | 3.1 | |
| Dielectric Strength | 25.0 kV/mm | 635 kV/in | ASTM D145 |
| Dissipation Factor | 0.0010 | 0.0010 | IEC 60250 |
| Arc Resistance | 120 - 180 sec | 120 - 180 sec | ASTM D495 |
| Comparative Tracking Index | 400 - 600 V | 400 - 600 V | IEC 60112 |
| Hot Wire Ignition, HWI | 60 - 120 sec @Thickness 1.50 mm |
60 - 120 sec @Thickness 0.0591 in |
UL 746A |
| High Amp Arc Ignition, HAI | >= 120 arcs @Thickness 1.50 mm |
>= 120 arcs @Thickness 0.0591 in |
UL 746A |
| High Voltage Arc-Tracking Rate, HVTR | 0.000 - 10.0 mm/min | 0.000 - 0.394 in/min | UL746A |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 280 - 310 °C | 536 - 590 °F | |
| Mold Temperature | 50.0 - 80.0 °C | 122 - 176 °F | |
| 130 - 155 °C | 266 - 311 °F | For optimal surface finish |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Comments | Optimized for heat & chemical resistance |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Cycoloy® CY5005 PC+ABS
- Lehmann & Voss LUVOTECH® GS 58 Polyamide 66, with glass fiber, lubricant modified
- SABIC Innovative Plastics ULTEM 1010TC PEI (Asia Pacific)
- Styron XZ 97209.00 SB Latex
- Epoxy Technology EPO-TEK® 305 Spectrally Transparent Epoxy
- Chosun Refractories INCT-110S Light-Weight Castable
- AorTech Biomaterials ECSil™ 60D Biomedical Carbonate Silicone Pellets
- Multibase Multibatch® MP 63001 Anti-split
- LyondellBasell Higlass BJ62A Polypropylene Copolymer, 30% Glass Fiber
Copyright © lookpolymers.com All Rights Reserved