- Idemitsu Kosan Xarec® N WA 7030 SPS, 30% Glass Filled
Idemitsu Kosan Xarec® N WA 7030 SPS, 30% Glass Filled
| Category | Polymer , Thermoplastic , Polystyrene (PS) , Syndiotactic Polystyrene (SPS) , Syndiotactic Polystyrene (SPS) with Glass or Carbon Fiber |
| Manufacturer | Idemitsu Kosan Co., Ltd. |
| Trade Name | Xarec® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Idemitsu Kosan Xarec® N WA 7030 SPS, 30% Glass Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Crystalline Polymer Blend, Glass Filled, Impact Modified
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.32 g/cc | 0.0477 lb/in³ | |
| Filler Content | 30 % | 30 % | |
| Water Absorption | 0.20 % | 0.20 % | 24 hrs., 50% RH |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0050 cm/cm | 0.0020 - 0.0050 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 175 MPa | 25400 psi | |
| Elongation at Break | 2.6 % | 2.6 % | |
| Tensile Modulus | 10.0 GPa | 1450 ksi | |
| Flexural Yield Strength | 250 MPa | 36300 psi | |
| Flexural Modulus | 9.10 GPa | 1320 ksi | |
| Izod Impact, Notched (ISO) | 11.0 kJ/m² | 5.23 ft-lb/in² | |
| Izod Impact, Unnotched (ISO) | 57.0 kJ/m² | 27.1 ft-lb/in² | |
| Charpy Impact Unnotched | 6.80 J/cm² | 32.4 ft-lb/in² | |
| Charpy Impact, Notched | 1.10 J/cm² | 5.23 ft-lb/in² |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 24.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
13.3 µin/in-°F @Temperature -22.0 - 86.0 °F |
|
| CTE, linear, Transverse to Flow | 49.0 µm/m-°C | 27.2 µin/in-°F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 260 °C | 500 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 245 °C | 473 °F | |
| UL RTI, Electrical | 50.0 °C | 122 °F | UL746B |
| UL RTI, Mechanical with Impact | 50.0 °C | 122 °F | UL746B |
| UL RTI, Mechanical without Impact | 50.0 °C | 122 °F | UL746B |
| Flammability, UL94 | HB @Thickness 0.750 mm |
HB @Thickness 0.0295 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 6.70e+15 ohm-cm | 6.70e+15 ohm-cm | |
| Dielectric Constant | 3.2 | 3.2 | |
| Dielectric Strength | 18.0 kV/mm | 457 kV/in | ASTM D145 |
| Dissipation Factor | 0.069 | 0.069 | IEC 60250 |
| Arc Resistance | 120 - 180 sec | 120 - 180 sec | ASTM D495 |
| Comparative Tracking Index | 250 - 400 V | 250 - 400 V | IEC 60112 |
| Hot Wire Ignition, HWI | 7.0 - 15 sec @Thickness 1.50 mm |
7.0 - 15 sec @Thickness 0.0591 in |
UL 746A |
| High Amp Arc Ignition, HAI | >= 120 arcs @Thickness 1.50 mm |
>= 120 arcs @Thickness 0.0591 in |
UL 746A |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 280 - 310 °C | 536 - 590 °F | |
| Mold Temperature | 50.0 - 80.0 °C | 122 - 176 °F | |
| Drying Temperature | 80.0 °C | 176 °F | 1 - 3 hrs |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Comments | High Ductility | |
| Nylon/SPS blend |
Users viewing this material also viewed the following:
- LyondellBasell Petrothene® LP500200 High Density Polyethylene (Sheet & Profile Grade)
- LG Chemical HIPS MI750L PS, Impact Modified
- LG Chemical IF850 PMMA, General Purpose Grade for Injection Molding
- Stir SpA Giesse RJA/9 (PVC)
- Hexcel® HexPly® F263 Epoxy Resin, 7781 Glass Fabric
- Dow Corning A-4040 PRIME COAT
- ATI Allegheny Ludlum Stainless Steel Chromium-Nickel Type 305, 60% Cold Rolled (UNS S30500)
- Arlon 55279R031 0.031" (0.787 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate
Copyright © lookpolymers.com All Rights Reserved