A. Schulman ComAlloy® E-14756 Flame Retardant Easy Flow Polycarbonate Alloy
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | A. Schulman ComAlloy® E-14756 Flame Retardant Easy Flow Polycarbonate Alloy.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by A. Schulman.The ComAlloy product line has been integrated into the A Schulman product line.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.34 g/cc | 1.34 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0030 cm/cm @Thickness 3.175 mm |
0.0030 in/in @Thickness 0.1250 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 56.5 MPa | 8200 psi | ASTM D638 |
| Elongation at Break | 15 % | 15 % | ASTM D638 |
| Flexural Strength | 89.6 MPa | 13000 psi | ASTM D790 |
| Flexural Modulus | 2.74 GPa | 398 ksi | ASTM D790 |
| Izod Impact, Notched | 1.12 J/cm | 2.10 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 4.22 J/cm | 7.90 ft-lb/in | ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 97.8 °C | 208 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 83.9 °C | 183 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 250 - 270 °C | 482 - 518 °F | |
| Mold Temperature | 65.0 - 95.0 °C | 149 - 203 °F | |
| Drying Temperature | 110 °C | 230 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | Predrying |
Users viewing this material also viewed the following:
- Osprey Metals Co502 Cobalt Alloy Powder (Grade 95% - 16)
- SABIC Innovative Plastics Valox® 420SE0U PBT (Asia Pacific)
- Tipco Tipcolene® FPT 20 FR VO LTHA - UL94-V0 Flame Retardant, 20% Talc Polypropylene Homopolymer, Long Term Heat Stability
- Formosa Plastics Formolene® 3335E Random Copolymer Polypropylene
- Chi Mei Polyrex® PH-88S Polystyrene - Extrusion
- Eurotec® Tecotek® PC44 GR003 ZG70 PC, unfilled, flame retardant - halogen (RoHS compliant), light grey
- Ashley Polymers Ashlene® 925-20PF Nylon 12, PTFE Lubricated
- Lucite International Diakon® CLG357 Acrylic Polymer