Chase Plastics CP Pryme® N310L (Dry) Nylon 6, 10% Glass Fiber Reinforced, Lubricated, Recycled Content
| Category | Polymer , Renewable/Recycled Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 10% Glass Fiber Filled |
| Manufacturer | Chase Plastics |
| Trade Name | CP Pryme® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Chase Plastics CP Pryme® N310L (Dry) Nylon 6, 10% Glass Fiber Reinforced, Lubricated, Recycled Content.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Features: LubricatedRecycled contentForm: PelletsInformation provided by Chase Plastics.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.23 g/cc | 0.0444 lb/in³ | ASTM D792 |
| Filler Content | 10 % | 10 % | |
| Water Absorption | 1.7 % | 1.7 % | At 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0050 cm/cm | 0.0050 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 96.5 MPa | 14000 psi | ASTM D638 |
| Elongation at Break | 2.0 % | 2.0 % | ASTM D638 |
| Flexural Strength | 152 MPa | 22000 psi | ASTM D790 |
| Flexural Modulus | 4.69 GPa | 680 ksi | ASTM D790 |
| Izod Impact, Notched | 0.534 J/cm | 1.00 ft-lb/in | 0.125 in; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 202 °C | 395 °F | Unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Network Polymers Nylon 6609
- Radici Radilon® S HSX (cond.) Nylon 6
- Ineos ABS Triax® 1120 ABS + Polyamide Blend (Conditioned)
- Struktol TPW 609 Processing Additive
- Saint-Gobain Rulon® DC7035 Bearing/Seal PTFE
- Techmer ES Plastiblend® PC/ABS FR 6206
- TIMET TIMETAL® 6-2-4-6 Titanium Alloy (Ti-6Al-2Sn-4Zr-6Mo), 10% Equiaxed Alpha + STA
- ExxonMobil LLDPE LL 3404.48 Linear Low Density Polyethylene Resin
- Aaron Industries AAROPRENE® GFIPP 2020 High Impact Glass Filled Polypropylene
- Axiall 18660 Moldings & Extrusions Flexible PVC
Copyright © lookpolymers.com All Rights Reserved