- Fiberfil® J-69/40/E High performance polypropylene Homopolymer, 40% Glass Reinforced, Chemically coupled
Fiberfil® J-69/40/E High performance polypropylene Homopolymer, 40% Glass Reinforced, Chemically coupled
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | FiberFil |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Fiberfil® J-69/40/E High performance polypropylene Homopolymer, 40% Glass Reinforced, Chemically coupled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by FIBERFIL Engineered Plastics
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.22 g/cc | 1.22 g/cc | ASTM D792 |
| Water Absorption | 0.030 % | 0.030 % | 24 hr; ASTM D570 |
| Linear Mold Shrinkage | 0.0020 cm/cm @Thickness 3.17 mm |
0.0020 in/in @Thickness 0.125 in |
ASTM D955 |
| 0.0030 cm/cm @Thickness 6.35 mm |
0.0030 in/in @Thickness 0.250 in |
ASTM D955 | |
| Melt Flow | 6.0 g/10 min | 6.0 g/10 min | 230/2.16 (typical); ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 105 - 110 | 105 - 110 | ASTM D785 |
| Tensile Strength, Yield | 114 MPa | 16500 psi | ASTM D638 |
| Elongation at Yield | 2.0 % | 2.0 % | ASTM D638 |
| Tensile Modulus | 8.62 GPa | 1250 ksi | ASTM D638 |
| Flexural Strength | 148 MPa | 21400 psi | ASTM D790 |
| Flexural Modulus | 7.93 GPa | 1150 ksi | Tangent; ASTM D790 |
| Izod Impact, Notched | 0.961 J/cm @Thickness 3.17 mm |
1.80 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 160 °C | 320 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 154 °C | 310 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 204 - 221 °C | 400 - 430 °F | |
| Middle Barrel Temperature | 216 - 232 °C | 420 - 450 °F | |
| Front Barrel Temperature | 204 - 227 °C | 400 - 440 °F | |
| Nozzle Temperature | 204 - 221 °C | 400 - 430 °F | |
| Melt Temperature | 210 - 232 °C | 410 - 450 °F | |
| Mold Temperature | 37.8 - 65.6 °C | 100 - 150 °F | |
| Back Pressure | 0.172 - 0.345 MPa | 25.0 - 50.0 psi |
Users viewing this material also viewed the following:
- Process Technologies Inc Silicone-Clear Sanitary Gasket
- Rostone Rosite® 3950ES SMC Thermoset Polyester, 25% Glass Reinforced (discontinued **)
- Techmer ES HiFill® PA6 GF14 L 14% Glass Filled
- Styron SE PB-5800 Schkopau Low-cis Polybutadiene Rubber (PBR)
- Borealis Borcoat™ HE3450 Black High Density Polyethylene Top Coat for Steel Pipe Coating
- C.O.I.M. FILCO® 350 Non Ionic Unsaturated Polyester Polymer Emulsion for Glass Fiber Sizing
- 3M 4008 Double Coated Urethane Foam Tape
- Multibase Multi-ABS 3245 FR Flame Retardant ABS
- Covestro Makrolon® Rx1452 Polycarbonate
Copyright © lookpolymers.com All Rights Reserved