Eurostar Starflam PF0057E PA6, 25% Glass Filled, Injection Molded

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled
Manufacturer Eurostar Engineering Plastics
Trade Name Starflam
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Eurostar Starflam PF0057E PA6, 25% Glass Filled, Injection Molded.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Halogen Free and Red Phosphorous Free, Flame Retardant, Glass Fiber Reinforced, Polyamide 6 Injection Molding Resin (also known as PF-1005 Z270)Information provided by Polymer Technology & Services, the North American exclusive supplier.
Physical Properties Metric English Comments
Density 1.39 g/cc
0.0502 lb/in³
ISO 1183
Linear Mold Shrinkage, Flow 0.0010 - 0.0030 cm/cm

@Time 86400 sec
 0.0010 - 0.0030 in/in

@Time 24.0 hour
 ISO 294
Linear Mold Shrinkage, Transverse 0.0090 - 0.013 cm/cm

@Time 86400 sec
 0.0090 - 0.013 in/in

@Time 24.0 hour
 ISO 294
Mechanical Properties Metric English Comments
Tensile Strength at Break 145 MPa
21000 psi
ISO 527
Elongation at Break 3.0 %
3.0 %
ISO 527
Tensile Modulus 9.50 GPa
1380 ksi
1 mm/min; ISO 527
Flexural Strength 210 MPa
30500 psi
ISO 178
Flexural Modulus 8.00 GPa
1160 ksi
ISO 178
Izod Impact, Notched (ISO) 10.0 kJ/m²
4.76 ft-lb/in²
80x10x4; ISO 180/1A
Izod Impact, Unnotched (ISO) 54.0 kJ/m²
25.7 ft-lb/in²
80x10x4; ISO 180/1U
Thermal Properties Metric English Comments
Thermal Conductivity 0.300 W/m-K
2.08 BTU-in/hr-ft²-°F
ISO 8302
Hot Ball Pressure Test 200 °C

@Thickness 3.00 mm
 392 °F

@Thickness 0.118 in
 IEC 60695-10-2
Deflection Temperature at 1.8 MPa (264 psi) 205 °C
401 °F
Flatw 80x10x4, sp=64 mm; ISO 75/Af
UL RTI, Electrical 140 °C

@Thickness 0.800 mm
 284 °F

@Thickness 0.0315 in
140 °C

@Thickness 1.60 mm
 284 °F

@Thickness 0.0630 in
140 °C

@Thickness 1.60 mm
 284 °F

@Thickness 0.0630 in
140 °C

@Thickness 3.00 mm
 284 °F

@Thickness 0.118 in
UL RTI, Mechanical with Impact 105 °C

@Thickness 0.800 mm
 221 °F

@Thickness 0.0315 in
105 °C

@Thickness 1.60 mm
 221 °F

@Thickness 0.0630 in
105 °C

@Thickness 1.60 mm
 221 °F

@Thickness 0.0630 in
105 °C

@Thickness 3.00 mm
 221 °F

@Thickness 0.118 in
UL RTI, Mechanical without Impact 140 °C

@Thickness 0.800 mm
 284 °F

@Thickness 0.0315 in
140 °C

@Thickness 1.60 mm
 284 °F

@Thickness 0.0630 in
140 °C

@Thickness 1.60 mm
 284 °F

@Thickness 0.0630 in
140 °C

@Thickness 3.00 mm
 284 °F

@Thickness 0.118 in
Flammability, UL94 V-0

@Thickness 0.800 mm
 V-0

@Thickness 0.0315 in
 IEC 60695-11-10
V-0 - 5VB

@Thickness 1.60 mm
 V-0 - 5VB

@Thickness 0.0630 in
 IEC 60695-11-10
V-0 - 5VA

@Thickness 1.60 mm
 V-0 - 5VA

@Thickness 0.0630 in
 IEC 60695-11-10
V-0 - 5VA

@Thickness 3.00 mm
 V-0 - 5VA

@Thickness 0.118 in
 IEC 60695-11-10
Glow Wire Test 775 °C

@Thickness 0.800 mm
 1430 °F

@Thickness 0.0315 in
 Glow-Wire Ignition; IEC 60695-2-13
775 °C

@Thickness 1.60 mm
 1430 °F

@Thickness 0.0630 in
 Glow-Wire Ignition; IEC 60695-2-13
775 °C

@Thickness 1.60 mm
 1430 °F

@Thickness 0.0630 in
 Glow-Wire Ignition; IEC 60695-2-13
800 °C

@Thickness 3.00 mm
 1470 °F

@Thickness 0.118 in
 Glow-Wire Ignition; IEC 60695-2-13
960 °C

@Thickness 0.800 mm
 1760 °F

@Thickness 0.0315 in
 Glow-Wire Flammability; IEC 60695-2-12
960 °C

@Thickness 1.60 mm
 1760 °F

@Thickness 0.0630 in
 Glow-Wire Flammability; IEC 60695-2-12
960 °C

@Thickness 1.60 mm
 1760 °F

@Thickness 0.0630 in
 Glow-Wire Flammability; IEC 60695-2-12
960 °C

@Thickness 3.00 mm
 1760 °F

@Thickness 0.118 in
 Glow-Wire Flammability; IEC 60695-2-12
Electrical Properties Metric English Comments
Comparative Tracking Index 600 V
600 V
IEC 60112
Hot Wire Ignition, HWI >= 120 sec

@Thickness 0.800 mm
 >= 120 sec

@Thickness 0.0315 in
 PLC 0
>= 120 sec

@Thickness 1.50 mm
 >= 120 sec

@Thickness 0.0591 in
 PLC 0
>= 120 sec

@Thickness 1.60 mm
 >= 120 sec

@Thickness 0.0630 in
 PLC 0
>= 120 sec

@Thickness 3.00 mm
 >= 120 sec

@Thickness 0.118 in
 PLC 0
High Amp Arc Ignition, HAI >= 120 arcs

@Thickness 0.800 mm
 >= 120 arcs

@Thickness 0.0315 in
 PLC 0
>= 120 arcs

@Thickness 1.50 mm
 >= 120 arcs

@Thickness 0.0591 in
 PLC 0
>= 120 arcs

@Thickness 1.60 mm
 >= 120 arcs

@Thickness 0.0630 in
 PLC 0
>= 120 arcs

@Thickness 3.00 mm
 >= 120 arcs

@Thickness 0.118 in
 PLC 0
Processing Properties Metric English Comments
Rear Barrel Temperature 240 - 250 °C
464 - 482 °F
Zone 1
Middle Barrel Temperature 250 - 260 °C
482 - 500 °F
Zone 2
Front Barrel Temperature 250 - 270 °C
482 - 518 °F
Zone 3
Melt Temperature 250 - 270 °C
482 - 518 °F
Mold Temperature 50.0 - 90.0 °C
122 - 194 °F
Drying Temperature 80.0 °C
176 °F
Dry Time 4.00 hour
4.00 hour
Moisture Content 0.20 %
0.20 %
Descriptive Properties Value Comments
UL f1 f1