Eurostar Staramide B28H PA6, Heat Stabilized, Injection Molded
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Heat Stabilized |
| Manufacturer | Eurostar Engineering Plastics |
| Trade Name | Staramide |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eurostar Staramide B28H PA6, Heat Stabilized, Injection Molded.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Staramide B28H is a Heat Stabilized, Unreinforced Polyamide 6, Injection Molding ResinInformation provided by Eurostar.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | ISO 1183 |
| Moisture Absorption | 2.60 % @Temperature 23.0 °C |
2.60 % @Temperature 73.4 °F |
50% RH; ISO 62 |
| Water Absorption at Saturation | 10 % @Temperature 23.0 °C |
10 % @Temperature 73.4 °F |
ISO 62-1 |
| Linear Mold Shrinkage, Flow | 0.011 - 0.015 cm/cm | 0.011 - 0.015 in/in | on Tensile Bar; E2P method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | ISO 2039-2 |
| Tensile Strength, Yield | 70.0 MPa | 10200 psi | 50 mm/min; ISO 527 |
| Elongation at Break | >= 15 % | >= 15 % | 50 mm/min; ISO 527 |
| Elongation at Yield | 3.5 % | 3.5 % | 50 mm/min; ISO 527 |
| Tensile Modulus | 2.70 GPa | 392 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 85.0 MPa | 12300 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 2.40 GPa | 348 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 3.00 kJ/m² @Temperature -40.0 °C |
1.43 ft-lb/in² @Temperature -40.0 °F |
80x10x4; ISO 180/1A |
| 4.00 kJ/m² @Temperature -20.0 °C |
1.90 ft-lb/in² @Temperature -4.00 °F |
80x10x4; ISO 180/1A | |
| 5.00 kJ/m² @Temperature 23.0 °C |
2.38 ft-lb/in² @Temperature 73.4 °F |
80x10x4; ISO 180/1A | |
| Charpy Impact Unnotched | >= 10.0 J/cm² @Temperature -30.0 °C |
>= 47.6 ft-lb/in² @Temperature -22.0 °F |
Edgew 80x10x4 sp=62; ISO 179/1eU |
| >= 27.0 J/cm² @Temperature 23.0 °C |
>= 128 ft-lb/in² @Temperature 73.4 °F |
Edgew 80x10x4 sp=62; ISO 179/1eU | |
| Charpy Impact, Notched | 0.400 J/cm² @Temperature -30.0 °C |
1.90 ft-lb/in² @Temperature -22.0 °F |
Edgew 80x10x4 sp=62; ISO 179/1eA |
| 0.500 J/cm² @Temperature 23.0 °C |
2.38 ft-lb/in² @Temperature 73.4 °F |
Edgew 80x10x4 sp=62; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 80.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
44.4 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 80.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
44.4 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Thermal Conductivity | 0.290 W/m-K | 2.01 BTU-in/hr-ft²-°F | ISO 8302 |
| Hot Ball Pressure Test | 123 - 127 °C | 253 - 261 °F | IEC 60695-10-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 180 °C | 356 °F | Edgew 120x10x4, sp=100 mm; ISO 75/Be |
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C | 140 °F | Edgew 120x10x4, sp=100 mm; ISO 75/Ae |
| Vicat Softening Point | 200 °C | 392 °F | B/120; ISO 306 |
| 210 °C | 410 °F | B/50; ISO 306 | |
| UL RTI, Electrical | 65.0 °C | 149 °F | |
| UL RTI, Mechanical with Impact | 65.0 °C | 149 °F | |
| UL RTI, Mechanical without Impact | 65.0 °C | 149 °F | |
| Flammability, UL94 | HB @Thickness 0.750 mm |
HB @Thickness 0.0295 in |
|
| HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
||
| Oxygen Index | 24 % | 24 % | ISO 4589 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+16 ohm-cm | >= 1.00e+16 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+16 ohm | >= 1.00e+16 ohm | IEC 60093 |
| Dielectric Constant | 3.0 @Frequency 1.00e+6 Hz |
3.0 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 3.3 @Frequency 50.0 - 60.0 Hz |
3.3 @Frequency 50.0 - 60.0 Hz |
IEC 60250 | |
| Dielectric Strength | 16.0 kV/mm @Thickness 3.20 mm |
406 kV/in @Thickness 0.126 in |
in oil; IEC 60243-1 |
| Dissipation Factor | 0.0058 @Frequency 50.0 - 60.0 Hz |
0.0058 @Frequency 50.0 - 60.0 Hz |
IEC 60250 |
| 0.018 @Frequency 1.00e+6 Hz |
0.018 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 |
| 600 V | 600 V | M; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Zone 1 | 230 - 240 °C | 446 - 464 °F | |
| Zone 2 | 240 - 250 °C | 464 - 482 °F | |
| Zone 3 | 250 - 260 °C | 482 - 500 °F | |
| Melt Temperature | 250 - 260 °C | 482 - 500 °F | |
| Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F | |
| Drying Temperature | 75.0 - 85.0 °C @Time 14400 - 21600 sec |
167 - 185 °F @Time 4.00 - 6.00 hour |
|
| Moisture Content | 0.20 % | 0.20 % |
Users viewing this material also viewed the following:
- ExxonMobil Santoprene® 281-87MED Thermoplastic Elastomer (discontinued **)
- TSE Industries EcoSPRAY® SS100 Aliphatic Polyurethane Resin
- PolyOne Therma-Tech™ NJC-6500 Nylon 12 (discontinued **)
- Techmer ES HiFill® PA6 IM 0240 Impact Modified
- Techmer ES Plaslube® J-50/30/TF/10 Polycarbonate, 30% GFR, 10% PTFE
- Supreme Petrochem SP6432 9690 Medium Impact Polystyrene
- ExxonMobil Febis K Series 68
- 3M 3294 Vent Tape
- Arlon 56596R045 0.045" (1.14 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate
Copyright © lookpolymers.com All Rights Reserved