Eurostar Staramide AG5 PA66, 25% Glass Filled, Injection Molded
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled |
| Manufacturer | Eurostar Engineering Plastics |
| Trade Name | Staramide |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eurostar Staramide AG5 PA66, 25% Glass Filled, Injection Molded.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
AG5 is a 25% Glass Fiber Reinforced Polyamide 66 Injection Molding ResinInformation provided by Polymer Technology & Services, the North American exclusive supplier.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.31 g/cc | 0.0473 lb/in³ | ISO 1183 |
| Water Absorption at Saturation | 6.0 % @Temperature 23.0 °C |
6.0 % @Temperature 73.4 °F |
ISO 62-1 |
| Linear Mold Shrinkage, Flow | 0.0025 - 0.0035 cm/cm | 0.0025 - 0.0035 in/in | on Tensile Bar; ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell L | 114 | 114 | ISO 2039-2 |
| Tensile Strength at Break | 165 MPa | 23900 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 3.5 % | 3.5 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 7.10 GPa | 1030 ksi | 1 mm/min; ISO 527 |
| Flexural Strength | 190 MPa | 27600 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 7.20 GPa | 1040 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 9.00 kJ/m² @Temperature 23.0 °C |
4.28 ft-lb/in² @Temperature 73.4 °F |
80x10x4; ISO 180/1A |
| 9.00 kJ/m² @Temperature -30.0 °C |
4.28 ft-lb/in² @Temperature -22.0 °F |
80x10x4; ISO 180/1A | |
| 9.00 kJ/m² @Temperature -40.0 °C |
4.28 ft-lb/in² @Temperature -40.0 °F |
80x10x4; ISO 180/1A | |
| Charpy Impact Unnotched | 4.50 J/cm² | 21.4 ft-lb/in² | Edgew 80x10x4; ISO 179/1eU |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 28.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
15.6 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 80.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
44.4 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Thermal Conductivity | 0.330 W/m-K | 2.29 BTU-in/hr-ft²-°F | ISO 8302 |
| Deflection Temperature at 0.46 MPa (66 psi) | 260 °C | 500 °F | Edgew 120x10x4, sp=100 mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 255 °C | 491 °F | Edgew 120x10x4, sp=100 mm; ISO 75/Af |
| Vicat Softening Point | 255 °C | 491 °F | B/120; ISO 306 |
| UL RTI, Electrical | 65.0 °C @Thickness 0.750 mm |
149 °F @Thickness 0.0295 in |
|
| 65.0 °C @Thickness 3.00 mm |
149 °F @Thickness 0.118 in |
||
| UL RTI, Mechanical with Impact | 65.0 °C @Thickness 0.750 mm |
149 °F @Thickness 0.0295 in |
|
| 65.0 °C @Thickness 3.00 mm |
149 °F @Thickness 0.118 in |
||
| UL RTI, Mechanical without Impact | 65.0 °C @Thickness 0.750 mm |
149 °F @Thickness 0.0295 in |
|
| 65.0 °C @Thickness 3.00 mm |
149 °F @Thickness 0.118 in |
||
| Flammability, UL94 | HB @Thickness 0.750 mm |
HB @Thickness 0.0295 in |
IEC 60695-11-10 |
| HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
IEC 60695-11-10 | |
| Flame Spread | 2.00 mm/min @Thickness 3.00 mm |
0.0787 in/min @Thickness 0.118 in |
FMVSS Buring Speed |
| 6.00 mm/min @Thickness 2.00 mm |
0.236 in/min @Thickness 0.0787 in |
FMVSS Buring Speed | |
| Oxygen Index | 27 % | 27 % | ISO 4589 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+16 ohm-cm | >= 1.00e+16 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+16 ohm | >= 1.00e+16 ohm | ROA; IEC 60093 |
| Dielectric Constant | 3.2 @Frequency 1.00e+6 Hz |
3.2 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 3.4 @Frequency 50.0 - 60.0 Hz |
3.4 @Frequency 50.0 - 60.0 Hz |
IEC 60250 | |
| Dielectric Strength | 19.0 kV/mm @Thickness 3.20 mm |
483 kV/in @Thickness 0.126 in |
in oil; IEC 60243-1 |
| Dissipation Factor | 0.0068 @Frequency 50.0 - 60.0 Hz |
0.0068 @Frequency 50.0 - 60.0 Hz |
IEC 60250 |
| 0.015 @Frequency 1.00e+6 Hz |
0.015 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| Comparative Tracking Index | 400 V | 400 V | M; IEC 60112 |
| 500 V | 500 V | IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 260 - 280 °C | 500 - 536 °F | Zone 1 |
| Middle Barrel Temperature | 270 - 280 °C | 518 - 536 °F | Zone 2 |
| Front Barrel Temperature | 270 - 290 °C | 518 - 554 °F | Zone 3 |
| Melt Temperature | 270 - 290 °C | 518 - 554 °F | |
| Mold Temperature | 60.0 - 90.0 °C | 140 - 194 °F | |
| Drying Temperature | 75.0 - 85.0 °C | 167 - 185 °F | |
| Dry Time | 4.00 - 6.00 hour | 4.00 - 6.00 hour | |
| Moisture Content | 0.20 % | 0.20 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| UL f1 | f1 |
Users viewing this material also viewed the following:
- RheTech Products CC20P200-00 20% Calcium Carbonate Reinforced Polypropylene Copolymer, Natural
- SABIC Innovative Plastics LNP Faradex ZX93134 PPE+PS (Europe-Africa-Middle East)
- Fainplast Compounds RE 412 Rigid PVC, Extrusion
- LG Chemical Lupoy 1200-08 Polycarbonate Resin
- Guarniflon PTFE G800 Polytetrafluoroethylene
- Solvay IGEPAL® CO 887 Surfactant
- ChevronTexaco Heavy Duty Coolant
- Daikin NEOFLON EPW-1606BL ETFE Liquid Primer, Blue
- Arlon 41580R030 0.030" Uncured, Unsupported Silicone Rubber on Release Carrier
- 3M FM001 Indoor UL Recognized Clear Polyester Overlaminate Label Product
Copyright © lookpolymers.com All Rights Reserved