- Acrylonitrile Butadiene Styrene (ABS), 10% Glass Fiber Filled
- Polymer Resources ABS-G5-[color]-3 ABS, 5% Glass Reinforced, UV-stabilized
Polymer Resources ABS-G5-[color]-3 ABS, 5% Glass Reinforced, UV-stabilized
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), 10% Glass Fiber Filled |
| Manufacturer | Polymer Resources, LTD |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polymer Resources ABS-G5-[color]-3 ABS, 5% Glass Reinforced, UV-stabilized.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Acrylonitrile Butadiene Styrene, 5% Glass Reinforced, UV-stabilizedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provided by Polymer Resources Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.08 g/cc | 1.08 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0030 - 0.0050 cm/cm | 0.0030 - 0.0050 in/in | ASTM D955 |
| Melt Flow | 0.50 - 5.0 g/10 min @Load 3.80 kg, Temperature 230 °C |
0.50 - 5.0 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 42.7 MPa | 6200 psi | ASTM D638 |
| Tensile Strength, Yield | 45.5 MPa | 6600 psi | ASTM D638 |
| Flexural Strength | 65.5 MPa | 9500 psi | ASTM D790 |
| Flexural Modulus | 2.90 GPa | 420 ksi | ASTM D790 |
| Izod Impact, Notched | 0.801 J/cm @Temperature 22.8 °C |
1.50 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 93.3 °C | 200 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 87.8 °C | 190 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 191 - 199 °C | 375 - 390 °F | |
| Middle Barrel Temperature | 210 - 221 °C | 410 - 430 °F | |
| Front Barrel Temperature | 210 - 227 °C | 410 - 440 °F | |
| Melt Temperature | 227 - 238 °C | 440 - 460 °F | |
| Mold Temperature | 48.9 - 60.0 °C | 120 - 140 °F | |
| Drying Temperature | 79.4 - 85.0 °C | 175 - 185 °F | |
| Dry Time | 3.00 - 4.00 hour | 3.00 - 4.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Vent | 0.001 |
Users viewing this material also viewed the following:
- Plastcom PLASTALEN® PQ 82 N Polypropylene with improved impact strength
- Omya OMYACARB® 15 - LU Calcium Carbonate
- NOVA Chemicals Sclair® 58G (High Gloss) HDPE Blow Molding Resin (discontinued **)
- Shakespeare LMX-3 Easy Casting Nylon Copolymer Fishing Line, 20 lb
- Sumitomo Bakelite North America Epiall® 1904B-1 Short Glass Fiber Reinforced Epoxy
- Shakespeare WP-89 diameter 0.2 mm Warp Polyester Monofilament
- Teknor Apex Sinvicomp SIM 6029 Polyvinyl Chloride, Flexible
- DuPont Teijin Films Melinex® 694 Polyester Film
- ConocoPhillips HD Fleet™ 149 Engine Oil SAE 50
- Azdel SuperLite® SL550800-100 PP Resin Matrix / 55% Glass Fiber (3 mm Molded Thickness)
Copyright © lookpolymers.com All Rights Reserved