EMS-Grivory Grivory® TSGZ-15/4 PA666-GF15
| Category | Polymer , Thermoplastic , Nylon , Nylon 6/66 , Nylon 66/6, 20% Glass Fiber Reinforced |
| Manufacturer | EMS-Grivory (EMS-CHEMIE) |
| Trade Name | Grivory® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | EMS-Grivory Grivory® TSGZ-15/4 PA666-GF15.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by EMS Grivory
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in³ | ISO 1183 |
| Water Absorption | 7.0 % | 7.0 % | ISO 62 |
| Moisture Absorption | 2.00 % | 2.00 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0010 cm/cm | 0.0010 in/in | ISO 294-4, 2577 |
| Linear Mold Shrinkage, Transverse | 0.0070 cm/cm | 0.0070 in/in | ISO 294-4, 2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 65.0 MPa | 9430 psi | conditioned; ISO 527-1/-2 |
| 110 MPa | 16000 psi | dry; ISO 527-1/-2 | |
| Tensile Strength, Yield | 70.0 MPa | 10200 psi | conditioned; ISO 527-1/-2 |
| Elongation at Break | 4.0 % | 4.0 % | dry; ISO 527-1/-2 |
| 10 % | 10 % | conditioned; ISO 527-1/-2 | |
| Elongation at Yield | 5.0 % | 5.0 % | conditioned; ISO 527-1/-2 |
| Tensile Modulus | 3.10 GPa | 450 ksi | conditioned; ISO 527-1/-2 |
| 5.80 GPa | 841 ksi | dry; ISO 527-1/-2 | |
| Charpy Impact Unnotched | 7.00 J/cm² | 33.3 ft-lb/in² | dry; ISO 179/1eU |
| 8.50 J/cm² | 40.4 ft-lb/in² | conditioned; ISO 179/1eU | |
| 6.00 J/cm² @Temperature 30.0 °C |
28.6 ft-lb/in² @Temperature 86.0 °F |
dry; ISO 179/1eU | |
| 7.00 J/cm² @Temperature 30.0 °C |
33.3 ft-lb/in² @Temperature 86.0 °F |
conditioned; ISO 179/1eU | |
| Charpy Impact, Notched | 1.10 J/cm² | 5.23 ft-lb/in² | dry; ISO 179/1eA |
| 1.60 J/cm² | 7.61 ft-lb/in² | conditioned; ISO 179/1eA | |
| 0.500 J/cm² @Temperature 30.0 °C |
2.38 ft-lb/in² @Temperature 86.0 °F |
dry; ISO 179/1eU | |
| 0.500 J/cm² @Temperature 30.0 °C |
2.38 ft-lb/in² @Temperature 86.0 °F |
conditioned; ISO 179/1eU |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 20.0 µm/m-°C | 11.1 µin/in-°F | ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 110 µm/m-°C | 61.1 µin/in-°F | ISO 11359-1/-2 |
| Melting Point | 260 °C | 500 °F | 10°C/min; ISO 11357-1/-3 |
| Maximum Service Temperature, Air | 90.0 - 120 °C | 194 - 248 °F | long term; EMS |
| 160 °C | 320 °F | short term; EMS | |
| Deflection Temperature at 1.8 MPa (264 psi) | 225 °C | 437 °F | ISO 75-1/-2 |
| Deflection Temperature at 8.0 MPa | 65.0 °C | 149 °F | ISO 75-1/-2 |
| Flammability, UL94 | HB | HB | IEC 60695-11-10 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+11 ohm-cm | 1.00e+11 ohm-cm | conditioned; IEC 60093 |
| 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | dry; IEC 60093 | |
| Surface Resistance | 1.00e+10 ohm | 1.00e+10 ohm | IEC 60093 |
| Dielectric Strength | 27.0 kV/mm | 686 kV/in | conditioned; IEC 60243-1 |
| 30.0 kV/mm | 762 kV/in | dry; IEC 60243-1 | |
| Comparative Tracking Index | 600 V | 600 V | dry; IEC 60112 |
| 600 V | 600 V | conditioned; IEC 60112 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Automotive | Interior | |
| Powertrain and Chassis | ||
| Electricals & Electronics | Connectors | |
| Electrical appliances | ||
| Form | Granules | |
| Industry & Consumer goods | Housewares | |
| Mechanical Engineering | ||
| Power transmission | ||
| Sports & Leisure | ||
| Tools & Accessories | ||
| Processing | Injection Molding | |
| Special Characteristics | High impact or impact modified |
Users viewing this material also viewed the following:
- Omni Plastics OmniTuff™ CPP GRC30 Copolymer Polypropylene Glass Reinforced
- BASF Master Builders Solutions ChemRex® CX-25 Polyurethane Adhesive/Sealant (discontinued **)
- Iran Petrochemical (PCC) 6040UA High Density Polyethylene
- Henkel Turco 4215 NC-LT Cleaner
- Saint-Gobain CHR® M60 Polyester Film Backing Acrylic Adhesive Pressure Sensitive Tape
- Trelleborg Horda Cable E8900 Strippable Semiconductive Shielding
- Cheng Yu Plastic N6G30 Nylon 6, 30% Glass Filled
- 3M 1080 Vinyl Film
- Beijing Chemical Industry KAIFA® HN201-G10 PA6 Resin
Copyright © lookpolymers.com All Rights Reserved