3M Dyneon™ CCX1029 PTFE, 10% Carbon Fiber Filled (discontinued **)

Category	Polymer , Thermoplastic , Fluoropolymer , PTFE , Polytetrafluoroethylene (PTFE), Carbon Fiber Filled
Manufacturer
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	3M Dyneon™ CCX1029 PTFE, 10% Carbon Fiber Filled (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Type I, non-free-flowing.Typical Applications: Finished or semi-finished parts: sheets, rods, tubes, billets for skiving of films or machining into complex shapes.Information provided by the Dyneon division of 3M.

Physical Properties	Metric	English	Comments
Specific Gravity	2.08 g/cc	2.08 g/cc	ASTM D4894
Bulk Density	0.475 g/cc	0.0172 lb/in³	ASTM D4894
Particle Size	25 µm	25 µm	ASTM D4894
Deformation	3.0 % @Pressure 15.00 MPa	3.0 % @Pressure 2175 psi	permanent; ASTM D621
	5.0 % @Time 86400 sec, Pressure 15.00 MPa	5.0 % @Time 24.0 hour, Pressure 2175 psi	ASTM D621

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	66	66	Initial; ASTM D2240
	60 @Time 15.0 sec	60 @Time 0.00417 hour	ASTM D2240
Tensile Strength at Break	27.6 MPa	4000 psi	ASTM D4894
Elongation at Break	280 %	280 %	ASTM D4894
Tensile Modulus	0.121 GPa	17.5 ksi	ASTM D638

Thermal Properties	Metric	English	Comments
CTE, linear	124 µm/m-°C @Temperature 30.0 - 100 °C	69.0 µin/in-°F @Temperature 86.0 - 212 °F	ASTM E831
	176 µm/m-°C @Temperature 100 - 200 °C	98.0 µin/in-°F @Temperature 212 - 392 °F	ASTM E831
	223 µm/m-°C @Temperature 200 - 300 °C	124 µin/in-°F @Temperature 392 - 572 °F	ASTM E831
Thermal Conductivity	0.290 W/m-K @Temperature 100 °C	2.01 BTU-in/hr-ft²-°F @Temperature 212 °F	ASTM E1530
	0.310 W/m-K @Temperature 250 °C	2.15 BTU-in/hr-ft²-°F @Temperature 482 °F	ASTM E1530
Shrinkage	1.4 %	1.4 %	ASTM D4894