EMS-Grivory Grivory® TSG-50/4 FA PA666-GF50
| Category | Polymer , Thermoplastic , Nylon , Nylon 6/66 , Nylon 66/6, 40% Glass Fiber Reinforced |
| Manufacturer | EMS-Grivory (EMS-CHEMIE) |
| Trade Name | Grivory® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | EMS-Grivory Grivory® TSG-50/4 FA PA666-GF50.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by EMS Grivory
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.55 g/cc | 0.0560 lb/in³ | ISO 1183 |
| Water Absorption | 5.0 % | 5.0 % | ISO 62 |
| Moisture Absorption | 1.50 % | 1.50 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0010 cm/cm | 0.0010 in/in | ISO 294-4, 2577 |
| Linear Mold Shrinkage, Transverse | 0.0030 cm/cm | 0.0030 in/in | ISO 294-4, 2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 160 MPa | 23200 psi | conditioned; ISO 2039-1 |
| 280 MPa | 40600 psi | dry; ISO 2039-1 | |
| Tensile Strength at Break | 170 MPa | 24700 psi | conditioned; ISO 527-1/-2 |
| 250 MPa | 36300 psi | dry; ISO 527-1/-2 | |
| Elongation at Break | 2.4 % | 2.4 % | dry; ISO 527-1/-2 |
| 4.5 % | 4.5 % | conditioned; ISO 527-1/-2 | |
| Tensile Modulus | 12.5 GPa | 1810 ksi | conditioned; ISO 527-1/-2 |
| 17.5 GPa | 2540 ksi | dry; ISO 527-1/-2 | |
| Charpy Impact Unnotched | 8.00 J/cm² | 38.1 ft-lb/in² | dry; ISO 179/1eU |
| 8.50 J/cm² | 40.4 ft-lb/in² | conditioned; ISO 179/1eU | |
| 7.00 J/cm² @Temperature 30.0 °C |
33.3 ft-lb/in² @Temperature 86.0 °F |
dry; ISO 179/1eU | |
| 8.00 J/cm² @Temperature 30.0 °C |
38.1 ft-lb/in² @Temperature 86.0 °F |
conditioned; ISO 179/1eU | |
| Charpy Impact, Notched | 1.40 J/cm² | 6.66 ft-lb/in² | dry; ISO 179/1eA |
| 2.00 J/cm² | 9.52 ft-lb/in² | conditioned; ISO 179/1eA | |
| 1.20 J/cm² @Temperature 30.0 °C |
5.71 ft-lb/in² @Temperature 86.0 °F |
dry; ISO 179/1eU | |
| 1.20 J/cm² @Temperature 30.0 °C |
5.71 ft-lb/in² @Temperature 86.0 °F |
conditioned; ISO 179/1eU |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 15.0 µm/m-°C | 8.33 µin/in-°F | ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 90.0 µm/m-°C | 50.0 µin/in-°F | ISO 11359-1/-2 |
| Melting Point | 260 °C | 500 °F | 10°C/min; ISO 11357-1/-3 |
| Maximum Service Temperature, Air | 100 - 120 °C | 212 - 248 °F | long term; EMS |
| 220 °C | 428 °F | short term; EMS | |
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | ISO 75-1/-2 |
| Deflection Temperature at 8.0 MPa | 200 °C | 392 °F | ISO 75-1/-2 |
| Flammability, UL94 | HB | HB | IEC 60695-11-10 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | conditioned; IEC 60093 |
| 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | dry; IEC 60093 | |
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | IEC 60093 |
| Dielectric Strength | 22.0 kV/mm | 559 kV/in | conditioned; IEC 60243-1 |
| 27.0 kV/mm | 686 kV/in | dry; IEC 60243-1 | |
| Comparative Tracking Index | 550 V | 550 V | conditioned; IEC 60112 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Food contact | EU Requirements | |
| FDA | ||
| Form | Granules | |
| Industry & Consumer goods | Housewares | |
| Sports & Leisure | ||
| Packaging | Medical packaging | |
| Processing | Injection Molding |
Users viewing this material also viewed the following:
- Polykemi AB POLYblend 65FS GF10 PC/ABS-blend, Glass Fiber reinforced
- SABIC Innovative Plastics LNP Lubricomp UX06442 PPA
- Saint-Gobain Chemfab® 250F PTFE Coated Beta Fiberglass Conveyor Belting
- Techmer ES HiFill FR® PA6/6 GF25 FR NAT003 25% Glass Filled (Dry)
- Teknor Apex Sinvicomp SMG 7500 Polyvinyl Chloride, Flexible
- Total MDPE 3802 Medium Density Polyethylene, Cable
- DuPont Performance Polymers Hytrel® 4556 Polyester Elastomer TPC-ET (Unverified Data**)
- Diamond Polymers ABS 3501 GF-30
- Fainplast Compounds CL 8315 Flexible PVC, Sheathing
- DuPont Performance Polymers Hypalon® 48 Chlorosulfonated Polyethylene Rubber, General Description (discontinu
Copyright © lookpolymers.com All Rights Reserved