Chesterton ARC BX2 Contractor Grade Fine Sliding Wear Compound

Category Ceramic , Polymer , Thermoset , Epoxy
Manufacturer Chesterton
Trade Name ARC
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Chesterton ARC BX2 Contractor Grade Fine Sliding Wear Compound.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: ARC BX2 is an advanced contractor grade ceramic reinforced composite for the repair and protection of all metal surfaces subjected to severe erosion, corrosion, and chemical attack. It is applied at a thickness of 3 mm (1/8”) or more. Non-shrinking. 100% Solids. ARC BX2 is formulated with a high concentration of small ceramic beads and particles for extremely abrasive environments where metal loss is often repaired by more conventional and costly weld overlay. ARC BX2 can be used either to rebuild eroded metal surfaces or to provide a wear resistant, sacrificial surface which frequently outperforms the original metal, rubber liners, ceramic tiles or weld overlay. ARC BX2 is a long lasting wearing surface and is chosen over ARC BX1 where a thinner, more easily applied composite is required.Benefits:Excellent wear characteristics of ARC BX2 extends equipment operating cyclesTough resin structures resists thermal-mechanical shockOutstanding adhesion results in reliable performance with no undercuttingEase of application reduces labor and downtime costsIt can be easily shaped and formed to any metal surfaceConvenient packaging suitable for large volume applications. Suggested Uses:Pneumatic ConveyorsChipper and Chip BinsHydro PulpersTurbo SeparatorsNi-Hard Slurry PumpsFly Ash SeparatorsWood Chip Transport FansScrew ConveyorsExhaust FansCyclones, HoppersWear PlatesPipe ElbowsPulverized Fuel LinesPulverizersInformation provided by Chesterton
Physical Properties Metric English Comments
Density 2.20 g/cc
0.0795 lb/in³
Cured
Mechanical Properties Metric English Comments
Hardness, Rockwell R 105
105
ASTM D785
Hardness, Shore D 90
90
ASTM D2240
Tensile Strength at Break 31.4 MPa
4550 psi
ASTM D638
Flexural Strength 63.8 MPa
9250 psi
ASTM D790
Compressive Strength 88.3 MPa
12800 psi
ASTM D695
Impact Test 5.76 J
4.25 ft-lb
Reverse; ASTM D2794
Thermal Properties Metric English Comments
CTE, linear 39.6 µm/m-°C
22.0 µin/in-°F
ASTM C531
Maximum Service Temperature, Air 95.0 °C
203 °F
Wet Service
205 °C
401 °F
Dry Service
Processing Properties Metric English Comments
Cure Time 19.8 min

@Temperature 43.0 °C
0.330 hour

@Temperature 109 °F
Tack Free
90.0 min

@Temperature 43.0 °C
1.50 hour

@Temperature 109 °F
Light Load
120 min

@Temperature 32.0 °C
2.00 hour

@Temperature 89.6 °F
Tack Free
240 min

@Temperature 25.0 °C
4.00 hour

@Temperature 77.0 °F
Tack Free
360 min

@Temperature 32.0 °C
6.00 hour

@Temperature 89.6 °F
Light Load
420 min

@Temperature 16.0 °C
7.00 hour

@Temperature 60.8 °F
Tack Free
480 min

@Temperature 25.0 °C
8.00 hour

@Temperature 77.0 °F
Light Load
720 min

@Temperature 43.0 °C
12.0 hour

@Temperature 109 °F
Full Load
960 min

@Temperature 10.0 °C
16.0 hour

@Temperature 50.0 °F
Tack Free
1200 min

@Temperature 32.0 °C
20.0 hour

@Temperature 89.6 °F
Full Load
1440 min

@Temperature 16.0 °C
24.0 hour

@Temperature 60.8 °F
Light Load
1440 min

@Temperature 43.0 °C
24.0 hour

@Temperature 109 °F
Full Chemical
1800 min

@Temperature 32.0 °C
30.0 hour

@Temperature 89.6 °F
Full Chemical
2160 min

@Temperature 10.0 °C
36.0 hour

@Temperature 50.0 °F
Light Load
2160 min

@Temperature 25.0 °C
36.0 hour

@Temperature 77.0 °F
Full Load
2880 min

@Temperature 16.0 °C
48.0 hour

@Temperature 60.8 °F
Full Load
2880 min

@Temperature 25.0 °C
48.0 hour

@Temperature 77.0 °F
Full Chemical
4320 min

@Temperature 10.0 °C
72.0 hour

@Temperature 50.0 °F
Full Load
4320 min

@Temperature 16.0 °C
72.0 hour

@Temperature 60.8 °F
Full Chemical
5760 min

@Temperature 10.0 °C
96.0 hour

@Temperature 50.0 °F
Full Chemical
Descriptive Properties Value Comments
Color Gray