SABIC Innovative Plastics NORYL GTX GTX9400W PPE+PS+PA

Category Polymer , Thermoplastic , Nylon , Polyphenylene Ether/PPO , Polystyrene (PS)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name NORYL GTX
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics NORYL GTX GTX9400W PPE+PS+PA.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
High flow PPO+PA. Power distribution box applications.
Physical Properties Metric English Comments
Specific Gravity 1.10 g/cc
1.10 g/cc
ASTM D792
Linear Mold Shrinkage, Flow 0.012 - 0.014 cm/cm

@Thickness 3.20 mm
0.012 - 0.014 in/in

@Thickness 0.126 in
SABIC Method
Linear Mold Shrinkage, Transverse 0.011 - 0.014 cm/cm

@Thickness 3.20 mm
0.011 - 0.014 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 97 g/10 min

@Load 5.00 kg,
Temperature 280 °C
97 g/10 min

@Load 11.0 lb,
Temperature 536 °F
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 62.0 MPa
8990 psi
Type I, 50 mm/min; ASTM D638
Tensile Strength, Yield 64.0 MPa
9280 psi
Type I, 50 mm/min; ASTM D638
69.0 MPa
10000 psi
50 mm/min; ISO 527
Elongation at Break 39 %
39 %
5 mm/min; ISO 527
40 %
40 %
Type I, 50 mm/min; ASTM D638
Elongation at Yield 11 %
11 %
Type I, 50 mm/min; ASTM D638
Tensile Modulus 1.95 GPa
283 ksi
50 mm/min; ASTM D638
Flexural Yield Strength 100 MPa
14500 psi
2.6 mm/min, 100 mm span; ASTM D790
Flexural Modulus 2.35 GPa
341 ksi
2.6 mm/min, 100 mm span; ASTM D790
2.70 GPa
392 ksi
2 mm/min; ISO 178
Izod Impact, Notched 2.56 J/cm
4.80 ft-lb/in
ASTM D256
1.12 J/cm

@Temperature -30.0 °C
2.10 ft-lb/in

@Temperature -22.0 °F
ASTM D256
Izod Impact, Unnotched 8.49 J/cm
15.9 ft-lb/in
ASTM D4812
7.68 J/cm

@Temperature -30.0 °C
14.4 ft-lb/in

@Temperature -22.0 °F
ASTM D4812
Izod Impact, Notched (ISO) 21.0 kJ/m²
9.99 ft-lb/in²
80*10*4; ISO 180/1A
13.0 kJ/m²

@Temperature -40.0 °C
6.19 ft-lb/in²

@Temperature -40.0 °F
80*10*4; ISO 180/1A
15.0 kJ/m²

@Temperature -20.0 °C
7.14 ft-lb/in²

@Temperature -4.00 °F
80*10*4; ISO 180/1A
Dart Drop, Total Energy 15.0 J

@Temperature -30.0 °C
11.1 ft-lb

@Temperature -22.0 °F
ASTM D3763
43.0 J

@Temperature 23.0 °C
31.7 ft-lb

@Temperature 73.4 °F
ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 122 µm/m-°C

@Temperature -40.0 - 40.0 °C
67.8 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
CTE, linear, Transverse to Flow 142 µm/m-°C

@Temperature -40.0 - 40.0 °C
78.9 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
Deflection Temperature at 0.46 MPa (66 psi) 187 °C
369 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
190 °C

@Thickness 3.20 mm
374 °F

@Thickness 0.126 in
unannealed; ASTM D648
202 °C

@Thickness 6.40 mm
396 °F

@Thickness 0.252 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 78.0 °C
172 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
83.0 °C

@Thickness 3.20 mm
181 °F

@Thickness 0.126 in
unannealed; ASTM D648
170 °C

@Thickness 6.40 mm
338 °F

@Thickness 0.252 in
unannealed; ASTM D648
Vicat Softening Point 203 °C
397 °F
Rate B/50; ISO 306
212 °C
414 °F
Rate B/50; ASTM D1525