- Toyobo GLAMIDE® NB-5620S Nylon/Olefin
Toyobo GLAMIDE® NB-5620S Nylon/Olefin
| Category | Polymer , Thermoplastic , Nylon |
| Manufacturer | Toyobo |
| Trade Name | GLAMIDE® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Toyobo GLAMIDE® NB-5620S Nylon/Olefin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
GLAMIDE® is very tough and exhibits high abrasion resistance. It has a high melting point and heat resistance, has well-balanced proportions of mechanical properties, performs self-distinguishing and a specific grade approved as UL94V-0 class is provided, and it exhibits excellent chemical resistance and oil resistance. Grade NB-5620S is a light weight, mineral-reinforced alloy of nylon and olefin.15
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.17 g/cc | 1.17 g/cc | Absolute Drying; ASTM-D792 |
| Filler Content | 15 % | 15 % | |
| Water Absorption | 0.50 % | 0.50 % | Absolute Drying; ASTM-D570 |
| Moisture Absorption at Equilibrium | 2.1 % | 2.1 % | Absolute Drying; ASTM-D570 |
| Linear Mold Shrinkage | 0.0060 - 0.0080 cm/cm @Thickness 1.00 mm |
0.0060 - 0.0080 in/in @Thickness 0.0394 in |
Absolute Drying |
| 0.014 - 0.018 cm/cm @Thickness 3.00 mm |
0.014 - 0.018 in/in @Thickness 0.118 in |
Absolute Drying | |
| Melt Flow | 8.0 g/10 min | 8.0 g/10 min |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 116 | 116 | Absolute Drying; ASTM-D785 |
| Tensile Strength, Ultimate | 22.0 MPa @Temperature 80.0 °C |
3190 psi @Temperature 176 °F |
Practical Use (Water Absorption 2.1%); ASTM-D638 |
| 25.0 MPa @Temperature 80.0 °C |
3630 psi @Temperature 176 °F |
Absolute Drying; ASTM-D638 | |
| 52.0 MPa @Temperature 23.0 °C |
7540 psi @Temperature 73.4 °F |
Practical Use (Water Absorption 2.1%); ASTM-D638 | |
| 60.0 MPa @Temperature 23.0 °C |
8700 psi @Temperature 73.4 °F |
Absolute Drying; ASTM-D638 | |
| 90.0 MPa @Temperature -40.0 °C |
13100 psi @Temperature -40.0 °F |
Practical Use (Water Absorption 2.1%); ASTM-D638 | |
| 100 MPa @Temperature -40.0 °C |
14500 psi @Temperature -40.0 °F |
Absolute Drying; ASTM-D638 | |
| Elongation at Break | 8.0 % | 8.0 % | Absolute Drying; ASTM-D638 |
| Flexural Strength | 30.0 MPa @Temperature 80.0 °C |
4350 psi @Temperature 176 °F |
Practical Use (Water Absorption 2.1%); ASTM-D790 |
| 40.0 MPa @Temperature 80.0 °C |
5800 psi @Temperature 176 °F |
Absolute Drying; ASTM-D790 | |
| 79.0 MPa @Temperature 23.0 °C |
11500 psi @Temperature 73.4 °F |
Practical Use (Water Absorption 2.1%); ASTM-D790 | |
| 95.0 MPa @Temperature 23.0 °C |
13800 psi @Temperature 73.4 °F |
Absolute Drying; ASTM-D790 | |
| 152 MPa @Temperature -40.0 °C |
22000 psi @Temperature -40.0 °F |
Practical Use (Water Absorption 2.1%); ASTM-D790 | |
| 160 MPa @Temperature -40.0 °C |
23200 psi @Temperature -40.0 °F |
Absolute Drying; ASTM-D790 | |
| Flexural Modulus | 1.40 GPa @Temperature 80.0 °C |
203 ksi @Temperature 176 °F |
Practical Use (Water Absorption 2.1%); ASTM-D790 |
| 2.30 GPa @Temperature 23.0 °C |
334 ksi @Temperature 73.4 °F |
Practical Use (Water Absorption 2.1%); ASTM-D790 | |
| 2.80 GPa @Temperature 80.0 °C |
406 ksi @Temperature 176 °F |
Absolute Drying; ASTM-D790 | |
| 3.70 GPa @Temperature 23.0 °C |
537 ksi @Temperature 73.4 °F |
Absolute Drying; ASTM-D790 | |
| 5.40 GPa @Temperature -40.0 °C |
783 ksi @Temperature -40.0 °F |
Practical Use (Water Absorption 2.1%); ASTM-D790 | |
| 6.20 GPa @Temperature -40.0 °C |
899 ksi @Temperature -40.0 °F |
Absolute Drying; ASTM-D790 | |
| Izod Impact, Notched | 0.400 J/cm @Temperature -40.0 °C |
0.749 ft-lb/in @Temperature -40.0 °F |
Absolute Drying; ASTM-D256 |
| 0.540 J/cm @Temperature 23.0 °C |
1.01 ft-lb/in @Temperature 73.4 °F |
Absolute Drying; ASTM-D256 | |
| 0.600 J/cm @Temperature -40.0 °C |
1.12 ft-lb/in @Temperature -40.0 °F |
Practical Use (Water Absorption 2.1%); ASTM-D256 | |
| 2.20 J/cm @Temperature 23.0 °C |
4.12 ft-lb/in @Temperature 73.4 °F |
Practical Use (Water Absorption 2.1%); ASTM-D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 180 °C | 356 °F | Absolute Drying; ASTM-D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 102 °C | 216 °F | Absolute Drying; ASTM-D648 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+9 ohm-cm | 1.00e+9 ohm-cm | Practical Use (Water Absorption 2.1%); ASTM-D257 |
| 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | Absolute Drying; ASTM-D257 | |
| Dielectric Strength | 21.0 kV/mm @Thickness 2.00 mm |
533 kV/in @Thickness 0.0787 in |
Practical Use (Water Absorption 2.1%); ASTM-D149 |
| 25.0 kV/mm @Thickness 2.00 mm |
635 kV/in @Thickness 0.0787 in |
Absolute Drying; ASTM-D149 | |
| Arc Resistance | 120 sec | 120 sec | Practical Use (Water Absorption 2.1%); ASTM-D495 |
| 130 sec | 130 sec | Absolute Drying; ASTM-D495 | |
| Comparative Tracking Index | >= 600 V | >= 600 V | IEC Method |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 240 - 290 °C | 464 - 554 °F | |
| Mold Temperature | 50.0 - 120 °C | 122 - 248 °F | |
| Injection Pressure | 50.0 MPa | 7250 psi |