EMS-Grivory Grivory® EBGM-20 HX PA666-GF15

Category	Polymer , Thermoplastic , Nylon , Nylon 6/66 , Nylon 66/6, 20% Glass Fiber Reinforced
Manufacturer	EMS-Grivory (EMS-CHEMIE)
Trade Name	Grivory®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	EMS-Grivory Grivory® EBGM-20 HX PA666-GF15.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Product description: Grilon EBGM-20 HX black 9992 is a high viscosity, high heat stabilized PA66 + PA6 extrusion blow molding grade with 15% glass fibers. The special features of Grilon EBGM-20 HX black 9992 are: High melt strengthHigh heat ageing resistanceEasy to processProcessable in Blow MoldingProcessable in Injection Molding Grilon EBGM-20 HX black 9992 is typically used in the automotive industry for applications such as charged air ducts and associated parts.Information provided by EMS Grivory

Physical Properties	Metric	English	Comments
Density	1.24 g/cc	0.0448 lb/in³	ISO 1183
Water Absorption	8.0 %	8.0 %	ISO 62
Moisture Absorption	3.00 %	3.00 %	ISO 62
Linear Mold Shrinkage, Flow	0.0040 cm/cm	0.0040 in/in	ISO 294-4, 2577
Linear Mold Shrinkage, Transverse	0.0070 cm/cm	0.0070 in/in	ISO 294-4, 2577

Mechanical Properties	Metric	English	Comments
Ball Indentation Hardness	75.0 MPa	10900 psi	conditioned; ISO 2039-1
	150 MPa	21800 psi	dry; ISO 2039-1
Tensile Strength at Break	55.0 MPa	7980 psi	conditioned; ISO 527-1/-2
	105 MPa	15200 psi	dry; ISO 527-1/-2
Elongation at Break	3.0 %	3.0 %	dry; ISO 527-1/-2
	7.0 %	7.0 %	conditioned; ISO 527-1/-2
Tensile Modulus	3.30 GPa	479 ksi	conditioned; ISO 527-1/-2
	6.30 GPa	914 ksi	dry; ISO 527-1/-2
Charpy Impact Unnotched	5.00 J/cm²	23.8 ft-lb/in²	dry; ISO 179/1eU
	6.50 J/cm²	30.9 ft-lb/in²	conditioned; ISO 179/1eU
	5.00 J/cm² @Temperature 30.0 °C	23.8 ft-lb/in² @Temperature 86.0 °F	dry; ISO 179/1eU
	5.00 J/cm² @Temperature 30.0 °C	23.8 ft-lb/in² @Temperature 86.0 °F	conditioned; ISO 179/1eU
Charpy Impact, Notched	0.800 J/cm²	3.81 ft-lb/in²	dry; ISO 179/1eA
	1.00 J/cm²	4.76 ft-lb/in²	conditioned; ISO 179/1eA
	0.500 J/cm² @Temperature 30.0 °C	2.38 ft-lb/in² @Temperature 86.0 °F	dry; ISO 179/1eU
	0.500 J/cm² @Temperature 30.0 °C	2.38 ft-lb/in² @Temperature 86.0 °F	conditioned; ISO 179/1eU

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	30.0 µm/m-°C	16.7 µin/in-°F	ISO 11359-1/-2
CTE, linear, Transverse to Flow	100 µm/m-°C	55.6 µin/in-°F	ISO 11359-1/-2
Melting Point	260 °C	500 °F	10°C/min; ISO 11357-1/-3
Deflection Temperature at 1.8 MPa (264 psi)	195 °C	383 °F	ISO 75-1/-2
Deflection Temperature at 8.0 MPa	65.0 °C	149 °F	ISO 75-1/-2
Flammability, UL94	HB	HB	IEC 60695-11-10

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+11 ohm-cm	1.00e+11 ohm-cm	conditioned; IEC 60093
	1.00e+12 ohm-cm	1.00e+12 ohm-cm	dry; IEC 60093
Surface Resistance	1.00e+10 ohm	1.00e+10 ohm	IEC 60093
Dielectric Strength	30.0 kV/mm	762 kV/in	conditioned; IEC 60243-1
	40.0 kV/mm	1020 kV/in	dry; IEC 60243-1
Comparative Tracking Index	550 V	550 V	conditioned; IEC 60112

Descriptive Properties	Value	Comments
Automotive	Air intake sytems
Form	Granules
Processing	Extrusion - blow molding
	Other Extrusion
Product Attributes	Nanocomposite
Special Characteristics	Improved heat resistance