Polymer Property : Tensile Modulus = 914 ksi Product List

Mechanical Properties

Tips: 30 items are displayed at most.

Mechanical Properties	Metric	English	Comments
Tensile Modulus	6.30 GPa <br>@Thickness 0.0500 mm	914 ksi <br>@Thickness 0.00197 in	ASTM D882-02
NeXolve LaRC™-CP1 Conductive Black Polyimide Lower RF loss than other black and conductive black polyimides. NeXolve’s Conductive Black LaRC™-CP1 Polyimide is filled with carbon nanoparticles to produce a conductive black polyimide material ..
Tensile Modulus	6.30 GPa <br>@Thickness 4.00 mm,<br> Temperature 23.0 °C	914 ksi <br>@Thickness 0.157 in,<br> Temperature 73.4 °F	Injection Molded; ISO 527-2/1
PolyOne Bergamid™ B70 G30 BK Polyamide 6 (Nylon 6) Information provided by PolyOne
Tensile Modulus	6.30 GPa	914 ksi	same value from ASTM and ISO test.
BASF Capron® HPN 9333G Impact Modified, 33% Glass-Filled Nylon 6 (Conditioned)  (discontinued **) Capron HPN 9333G is a 33% glass reinforced, impact modified polyamide 6 injection molding compound combining exceptional strength, stiffness and high temperature performance with excellent surface a..
Tensile Modulus	6.30 GPa	914 ksi	ISO 527-1/-2
Lanxess DurethanÂ® BG 30 X H2.0 901510 Nylon 6, 30% Glass Fiber PA 6, injection molding grade, 30% glass fibers/glass spheres, good surface, good heat-ageing resistance
Tensile Modulus	6.30 GPa	914 ksi	Conditioned; ISO 527-1/-2
Lanxess DurethanÂ® BKV 35 HTS 901510 Nylon 6, 35% Glass Fiber PA 6, injection molding grade, 35% glass fibers, very good heat-ageing resistance
Tensile Modulus	6.30 GPa	914 ksi	d.a.m.; ISO 527-1, -2; 1 mm/min
Lanxess DurethanÂ® DP 2-2240/15 H2.0 901510 Nylon 66, 15% Glass Fiber PA 66, 15% glass fibers, blow molding, heat-aging stabilized, hydrolysis stabilizedInformation provided by LANXESS.
Tensile Modulus	6.30 GPa	914 ksi	cond.; ISO 527-1, -2; 1 mm/min
Lanxess DurethanÂ® DP BKV 35 XF 901510 Nylon 6, 35% Glass Fiber PA 6, 35% glass fibers, injection molding, improved flowability, improved surface finishInformation provided by LANXESS.
Tensile Modulus	6.30 GPa	914 ksi	ISO 527 Type 1A
Solvay TECHNYLÂ® A 218 V25 Black 21 N PA66, 25% glass fiber, Conditioned Description: TECHNYLÂ® A 218 V25 is a polyamide 66, reinforced with 25% of glass fiber, heat stabilized, for injection molding. This product is available in natural and black colors.Benefits: The ..
Tensile Modulus	6.30 GPa	914 ksi	1 mm/min; ISO 527
SABIC Innovative Plastics LNP LUBRICOMP RX94033 PA6.6 (Europe-Africa-Middle East) LNP* LUBRICOMP* RX94033 is a compound based on PA 66 resin containing Aramide Fiber, Glass Fiber, PTFE. Added features include: Internally Lubricated.
Tensile Modulus	6.30 GPa	914 ksi	1 mm/min; ISO 527
SABIC Innovative Plastics ValoxÂ® DR48 - CS1049 PBT (Europe-Africa-Middle East) VALOX DR48 is a 15 % glass reinforced, flame retardant injection moulding PBT resin. Applications: lamp sockets, connectors, switches, electrical housings and bases, bobbins, trimmers and electromot..
Tensile Modulus	6.30 GPa	914 ksi	1 mm/min; ISO 527
SABIC Innovative Plastics LNP THERMOCOMP DF004 PC (Europe-Africa-Middle East) LNP* THERMOCOMP* DF004 is a compound based on Polycarbonate resin containing Glass Fiber.
Tensile Modulus	6.30 GPa	914 ksi	50 mm/min; ASTM D 638
SABIC Innovative Plastics LNP Thermocomp DFZ42P PC LNP* Thermocomp* DFZ42P is a compound based on Polycarbonate resin containing Glass Fiber. Added features of this material include: Exceptional Processing.This data was supplied by SABIC-IP for the..
Tensile Modulus	6.30 GPa	914 ksi	1 mm/min; ISO 527
SABIC Innovative Plastics LNP THERMOCOMP RF0039S PA 66 LNP THERMOCOMP* RF0039S is a compound based on Nylon 66 resin containing 15% Glass Fiber, Flame Retardant. Added features of this material include: Flame Retardant, Heat Stabilized.
Tensile Modulus	6.30 GPa	914 ksi	1 mm/min; ISO 527
SABIC Innovative Plastics LNP LUBRICOMP RKN14 PA 66 (Europe-Africa-Middle East) LNP* Lubricomp* RKN14 is a compound based on Nylon 66 resin containing Mineral, MOS2.
Tensile Modulus	6.30 GPa	914 ksi	50 mm/min; ASTM D638
SABIC Innovative Plastics LNP STAT-KON DFD03 PC LNP* STAT-KON* DFD03 is a compound based on Polycarbonate containing 15% Glass Fiber. Added feature of this grade is: Impact Modified.
Tensile Modulus	6.30 GPa	914 ksi	5 mm/min; ASTM D638
SABIC Innovative Plastics ValoxÂ® SHF4930 PBT (Europe-Africa-Middle East) Super high flow FR PBT grade with 15% Glass reinforced
Tensile Modulus	6.30 GPa	914 ksi	ISO 527-1
Sax Polymers SAXLAC 108 GF17 Acrylonitrile Butadiene Styrene, 17% Glass Fiber Saxalac 108 GF17 is a 17% glass fiber reinforced ABS injection molding grade, characterized by high impact strength, high stiffness and good resistance to heat distortion.Mechanical property data te..
Tensile Modulus	6.30 GPa	914 ksi	ISO 527
Polyram Polytron P60B08-S Polypropylene, 60% Long Glass Fiber Polytron P60B08-S (Single strand) is a chemically coupled polypropylene 60% long glass fiber with extra load of additives for dilution.Information provided by Polyram.
Tensile Modulus	6.30 GPa	914 ksi	cond; ISO 527-1/-2
DSM Novamid® 1015GH35 BK37 PA6-GF35 35% Glass Reinforced, Heat Stabilized, Injection Molding
Tensile Modulus	6.30 GPa	914 ksi	cond; ISO 527-1/-2
DSM Novamid® 3021GH30 NAT PA66-GF30 30% Glass Reinforced, Heat Stabilized
Tensile Modulus	6.30 GPa	914 ksi	dry; ISO 527-1/-2
EMS-Grivory Grivory® EBGM-20 HX PA666-GF15 Product description: Grilon EBGM-20 HX black 9992 is a high viscosity, high heat stabilized PA66 + PA6 extrusion blow molding grade with 15% glass fibers. The special features of Grilon EBGM-20 HX b..
Tensile Modulus	6.30 GPa	914 ksi	ISO 527
CP-Polymer-Technik Wellamid® 6600 GV 25 DCHP 25% Glass Fiber Nylon 66, Special Heat Ageing Stabilization, Conditioned Information provided by CP-Polymer-Technik GmbH & Co. KG
Tensile Modulus	6.30 GPa	914 ksi	ISO 527
CP-Polymer-Technik Wellamid® 6600 GV 25 HWCP 25% Glass Fiber Nylon 66, Heat Stabilized, Conditioned Information provided by CP-Polymer-Technik GmbH & Co. KG
Tensile Modulus	6.30 GPa <br>@Temperature 120 °C	914 ksi <br>@Temperature 248 °F	ISO 527-1/-2
DSM Stanyl® TW271B3 (PA46+PTFE)-CF15 15% Carbon Reinforced, Heat Stabilized, Wear and Friction Modified
Tensile Modulus	6.30 GPa <br>@Temperature 23.0 °C	914 ksi <br>@Temperature 73.4 °F	EN ISO 527
Ensinger TECASINT™ 2031 Polyimide, 40% Graphite Filled (PI) TECASINT™ 2000 series of polyimide stock shapes provide a superior combination of high temperature and bearing and wear, properties that make it an ideal choice for the most demanding applications...
Tensile Modulus	6.30 GPa	914 ksi	same value from ASTM and ISO test.
BASF Capron® HPN 9333G HS Impact Modified, 33% Glass-Filled Nylon 6 (Conditioned)  (discontinued **) Capron HPN 9333G HS is a heat stabilized, 33% glass reinforced, impact modified polyamide 6 injection molding compound combining exceptional strength, stiffness and high temperature performance with..
Tensile Modulus	6.30 GPa	914 ksi	STN EN ISO 527-2
Plastcom SLOVASTER® B GB 40 PBT reinforced with glass beads PBT for injection molding, reinforced with 40% glass beads. Characterized by very good properties also at low temperature. Melt is characterized by very good rheology, which enables manufacturing of..