Arlon Thermabond® 99A90N008 Primerless Electronic Adhesive (discontinued **)
| Category | Polymer , Adhesive , Thermoset , Rubber or Thermoset Elastomer (TSE) , Silicone , Silicone Rubber |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Arlon Thermabond® 99A90N008 Primerless Electronic Adhesive
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Electrically insulating, thermally conductive, electronic adhesive. Bonds without primer.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.85 g/cc | 1.85 g/cc | Silicone Property; Arlon SQA-TMS-024 |
| Thickness | 203 microns | 8.00 mil | Arlon SQA-TMS-003 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 87 | 87 | Silicone Property; ASTM D2240 |
| Tensile Strength, Ultimate | 2.52 MPa | 365 psi | Silicone Property; ASTM D412 |
| Elongation at Break | 28 % | 28 % | Silicone Property; ASTM D412 |
| Modulus of Elasticity | 0.0621 GPa | 9.00 ksi | 1% strain, Silicone Property; Arlon SQA-TMS-008 |
| Poissons Ratio | 0.50 | 0.50 | |
| Shear Modulus | 0.00183 GPa | 0.265 ksi | up to 100% strain; ASTM D1002 |
| Shear Strength | 0.965 MPa | 140 psi | Lap; ASTM D1002 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 52.0 µm/m-°C @Temperature 20.0 °C |
28.9 µin/in-°F @Temperature 68.0 °F |
Silicone Property; ASTM E 831 |
| Specific Heat Capacity | 0.850 J/g-°C @Temperature 100 °C |
0.203 BTU/lb-°F @Temperature 212 °F |
Silicone Property; ASTM E 1952 |
| Thermal Conductivity | 3.00 W/m-K | 20.8 BTU-in/hr-ft²-°F | Silicone Property; ASTM E 1530 |
| 3.38667 W/m-K @Temperature 100 °C |
23.5035 BTU-in/hr-ft²-°F @Temperature 212 °F |
Arlon SQA-TMS-054 | |
| Maximum Service Temperature, Air | 95.6 °C | 204 °F | |
| Minimum Service Temperature, Air | -73.3 °C | -100 °F | |
| Glass Transition Temp, Tg | -119 °C | -182 °F | Silicone Property; ASTM D3418 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 4.602 @Frequency 1.00e+6 Hz |
4.602 @Frequency 1.00e+6 Hz |
Silicone Property; IPC TM 650 - 2.5.5.3 |
| Dielectric Strength | 35.4 kV/mm | 900 kV/in | ASTM D149 |
| Dissipation Factor | 0.0041 @Frequency 1.00e+6 Hz |
0.0041 @Frequency 1.00e+6 Hz |
Silicone Property; IPC TM 650 - 2.5.5.3 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Cure Time | 15.0 min @Pressure 0.345 MPa, Temperature 121 °C |
0.250 hour @Pressure 50.0 psi, Temperature 250 °F |
|
| Shelf Life | 6.00 Month @Temperature 7.00 °C |
6.00 Month @Temperature 44.6 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Gray | |
| Plasticity (mm) Arlon SQA-TMS-005 | Silicone Property |
Users viewing this material also viewed the following:
- Quadrant EPP TIVAR® 88 UHMW-PE, Premium Glass Filled, Crosslinked Lining Material (ASTM Product Data Sheet)
- Ravago Manufacturing Americas Hylon® N1240MHL BK Nylon 6/6
- Mitsui Fybrel® E 795 Polyolefin Synthetic Pulp, Dry Processes (discontinued **)
- Chevron Phillips Marlex® CL-200YB (Black) Rotational molding crosslinkable high density polyethylene (discont
- Lehmann & Voss LUVOCOM® 50-8479/BL-1 Polycarbonate, unreinforced
- Gromax BFG30-FU00B3 Nylon 6 30% Glass Filled (Dry)
- Samsung Cheil Industries Infino® NH-1017D PC/ABS, Unreinforced FR
- API Megol AM DP2395/85 SEBS Adhesion Modified Overmolding for Polar Polymers
- 3M 4492G Double Coated Polyethylene Foam Tape
- Loctite® 3887 High Adhesion Isotropic Epoxy Adhesive
Copyright © lookpolymers.com All Rights Reserved