EMS-Grivory Grivory® BM-30 FR PA6-MD30 FR
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Mineral Filled |
| Manufacturer | EMS-Grivory (EMS-CHEMIE) |
| Trade Name | Grivory® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | EMS-Grivory Grivory® BM-30 FR PA6-MD30 FR.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by EMS Grivory
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.37 g/cc | 0.0495 lb/in³ | ISO 1183 |
| Water Absorption | 8.0 % | 8.0 % | ISO 62 |
| Moisture Absorption | 3.00 % | 3.00 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0080 cm/cm | 0.0080 in/in | ISO 294-4, 2577 |
| Linear Mold Shrinkage, Transverse | 0.0090 cm/cm | 0.0090 in/in | ISO 294-4, 2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 34.0 MPa | 4930 psi | conditioned; ISO 527-1/-2 |
| 85.0 MPa | 12300 psi | dry; ISO 527-1/-2 | |
| Tensile Strength, Yield | 40.0 MPa | 5800 psi | dry; ISO 527-1/-2 |
| 85.0 MPa | 12300 psi | dry; ISO 527-1/-2 | |
| Elongation at Break | 2.5 % | 2.5 % | dry; ISO 527-1/-2 |
| 45 % | 45 % | conditioned; ISO 527-1/-2 | |
| Elongation at Yield | 3.0 % | 3.0 % | dry; ISO 527-1/-2 |
| 6.0 % | 6.0 % | conditioned; ISO 527-1/-2 | |
| Tensile Modulus | 2.80 GPa | 406 ksi | conditioned; ISO 527-1/-2 |
| 6.40 GPa | 928 ksi | dry; ISO 527-1/-2 | |
| Charpy Impact Unnotched | 4.00 J/cm² | 19.0 ft-lb/in² | dry; ISO 179/1eU |
| 8.50 J/cm² | 40.4 ft-lb/in² | conditioned; ISO 179/1eU | |
| 3.50 J/cm² @Temperature 30.0 °C |
16.7 ft-lb/in² @Temperature 86.0 °F |
dry; ISO 179/1eU | |
| 3.50 J/cm² @Temperature 30.0 °C |
16.7 ft-lb/in² @Temperature 86.0 °F |
conditioned; ISO 179/1eU | |
| Charpy Impact, Notched | 0.300 J/cm² | 1.43 ft-lb/in² | dry; ISO 179/1eA |
| 0.400 J/cm² | 1.90 ft-lb/in² | conditioned; ISO 179/1eA | |
| 0.200 J/cm² @Temperature 30.0 °C |
0.952 ft-lb/in² @Temperature 86.0 °F |
dry; ISO 179/1eU | |
| 0.200 J/cm² @Temperature 30.0 °C |
0.952 ft-lb/in² @Temperature 86.0 °F |
conditioned; ISO 179/1eU |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 70.0 µm/m-°C | 38.9 µin/in-°F | ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 80.0 µm/m-°C | 44.4 µin/in-°F | ISO 11359-1/-2 |
| Melting Point | 222 °C | 432 °F | 10°C/min; ISO 11357-1/-3 |
| Maximum Service Temperature, Air | 80.0 - 110 °C | 176 - 230 °F | long term; EMS |
| 160 °C | 320 °F | short term; EMS | |
| Deflection Temperature at 1.8 MPa (264 psi) | 100 °C | 212 °F | ISO 75-1/-2 |
| Deflection Temperature at 8.0 MPa | 50.0 °C | 122 °F | ISO 75-1/-2 |
| Flammability, UL94 | V-2 | V-2 | IEC 60695-11-10 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Electricals & Electronics | Connectors | |
| Electrical equipment | ||
| Energy distribution | ||
| Form | Granules | |
| Processing | Injection Molding | |
| Special Characteristics | Flame retardant | |
| Improved UV resistance (outdoor use) |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Cycoloy® CY5210 PC+ABS (Europe-Africa-Middle East)
- Parker Chomerics CHO-SHIELD® MZ-45 Paint Additive
- Styron EMERGEâ„¢ 4330-15 Polycarbonate
- Chase Plastics CP Pryme® NN300L (COND, 50% RH) Nylon 66 (Utility Grade), Internally Lubricated
- A. Schulman PP 3449-01 Polypropylene Copolymer Polypropylene
- Eastman Tenite Acetate 105E1R26033 Clear, Trsp Cellulose Acetate
- Cossa Polimeri ESTADIENE 1030 V0/F Flame Retardant ABS
- China Tungsten YG15 Tungsten Carbide Powder
- Azoty Tarnow™ Tarnamid® T-27 CF30 Polyamide 6 30% Carbon Fiber - Antistatic and Electroconductive
- Adell EQ-18 Homopolymer Polypropylene, 40% Mica Filled
Copyright © lookpolymers.com All Rights Reserved