Techmer ES HiFill® HDPE TM5 5% Talc Filled
| Category | Polymer , Thermoplastic , Polyethylene (PE) , HDPE |
| Manufacturer | Techmer ES |
| Trade Name | HiFill® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Techmer ES HiFill® HDPE TM5 5% Talc Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Availability: North AmericaForms: PelletsFiller/Reinforcement: Talc Filler, 5% Filler by WeightInformation provided by TP Composites, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.990 g/cc | 0.0358 lb/in³ | ASTM D792 |
| Water Absorption | 0.020 % @Time 86400 sec |
0.020 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.022 cm/cm @Thickness 3.17 mm |
0.022 in/in @Thickness 0.125 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 30 | 30 | ASTM D785 |
| Tensile Strength, Yield | 24.1 MPa | 3500 psi | ASTM D638 |
| Elongation at Break | 25 % | 25 % | ASTM D638 |
| Flexural Strength | 25.5 MPa | 3700 psi | ASTM D790 |
| Flexural Modulus | 0.758 GPa | 110 ksi | ASTM D790 |
| Izod Impact, Notched | 0.267 J/cm @Thickness 3.17 mm |
0.500 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Izod Impact, Unnotched | 3.20 J/cm @Thickness 3.17 mm |
6.00 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 93.6 µm/m-°C | 52.0 µin/in-°F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 60.0 °C | 140 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 43.3 °C | 110 °F | Unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Dielectric Strength | 23.6 kV/mm | 600 kV/in | Method A (Short-Time); ASTM D149 |
Users viewing this material also viewed the following:
- ExxonMobil LL 8401.67 Rotational Molding Resin (discontinued **)
- SABIC Innovative Plastics Lexan® SLX1231D PC Copolymer
- Huntsman Araldite GT 6703 Bisphenol A Epoxy Solid Resin
- Lanxess Durethan® BG 30 X W1 000000 Nylon 6, Glass Fiber Reinforced
- Solvay ALKAMULS® A 9 Surfactant
- Hexcel® HexPly® 171/174/176 120°C Curing Epoxy Matrix
- ATI Allegheny Ludlum 420 Martensitic Stainless Steel
- Bhansali Engineering Abstron KU650N ABS Heat Resistant
- Materion Beryllium Copper Alloy 3 Strip; HT (TH04) Temper (UNS C17510)
Copyright © lookpolymers.com All Rights Reserved