SABIC Innovative Plastics LNP STAT-KON REF42 PA 66

Category Polymer , Thermoplastic , Nylon , Nylon 66
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP STAT-KON
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP STAT-KON REF42 PA 66.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* STAT-KON* REF42 is a compound based on Nylon 66 resin containing 20% Glass Fiber, 10% Carbon Fiber. Added features of this material include: Electrically Conductive.
Physical Properties Metric English Comments
Density 1.35 g/cc
0.0488 lb/in³
ASTM D792
1.35 g/cc
0.0488 lb/in³
ISO 1183
Moisture Absorption 0.500 %
0.500 %
50% RH, 24 hrs; ASTM D570
Linear Mold Shrinkage, Flow 0.0025 cm/cm

@Time 86400 sec
 0.0025 in/in

@Time 24.0 hour
 ISO 294
0.0030 cm/cm

@Time 86400 sec
 0.0030 in/in

@Time 24.0 hour
 ASTM D955
Linear Mold Shrinkage, Transverse 0.011 cm/cm

@Time 86400 sec
 0.011 in/in

@Time 24.0 hour
 ASTM D955
0.011 cm/cm

@Time 86400 sec
 0.011 in/in

@Time 24.0 hour
 ISO 294
Mechanical Properties Metric English Comments
Tensile Strength at Break 173 MPa
25100 psi
ASTM D638
207 MPa
30000 psi
ISO 527
Tensile Strength, Yield 173 MPa
25100 psi
ASTM D638
207 MPa
30000 psi
ISO 527
Elongation at Break 1.8 %
1.8 %
ASTM D638
2.6 %
2.6 %
ISO 527
Elongation at Yield 1.8 %
1.8 %
ASTM D638
2.6 %
2.6 %
ISO 527
Tensile Modulus 14.36 GPa
2083 ksi
1 mm/min; ISO 527
15.16 GPa
2199 ksi
50 mm/min; ASTM D638
Flexural Strength 282 MPa
40900 psi
ASTM D790
361 MPa
52400 psi
ISO 178
Flexural Modulus 11.03 GPa
1600 ksi
ASTM D790
17.0 GPa
2470 ksi
ISO 178
Izod Impact, Notched 0.800 J/cm
1.50 ft-lb/in
ASTM D256
Izod Impact, Unnotched 8.54 J/cm
16.0 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 8.00 kJ/m²
3.81 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 62.0 kJ/m²
29.5 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 5.00 J
3.69 ft-lb
Instrumented Impact Energy @ peak; ASTM D3763
Impact Test 2.00 J
1.48 ft-lb
Multiaxial Impact; ISO 6603
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 66.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 36.7 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
66.6 µm/m-°C

@Temperature -40.0 - 40.0 °C
 37.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
CTE, linear, Transverse to Flow 21.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 11.7 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
21.6 µm/m-°C

@Temperature -40.0 - 40.0 °C
 12.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
Deflection Temperature at 0.46 MPa (66 psi) 201 °C
394 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
262 °C

@Thickness 3.20 mm
 504 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 249 °C
480 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
253 °C

@Thickness 3.20 mm
 487 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Electrical Properties Metric English Comments
Surface Resistance 1e+05 - 1.00e+10 ohm
1e+05 - 1.00e+10 ohm
ASTM D257