DuPont Performance Polymers Zytel® 70G13HS1L NC010 Nylon 66  (Unverified Data**)

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 10% Glass Fiber Filled
Manufacturer DuPont Performance Polymers
Trade Name Zytel®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Zytel® 70G13HS1L NC010 Nylon 66  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
13% Glass Reinforced Heat Stabilized Polyamide 66 Zytel 70G13HS1L NC010 is a 13% glass fiber reinforced heat stabilized polyamide 66 resin for injection molding.Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.23 g/cc
0.0444 lb/in³
DAM; ISO 1183
Water Absorption 7.6 %

@Thickness 2.00 mm
 7.6 %

@Thickness 0.0787 in
 DAM; Sim. to ISO 62
Moisture Absorption 2.20 %

@Thickness 2.00 mm
 2.20 %

@Thickness 0.0787 in
 DAM; Sim. to ISO 62
Water Absorption at Saturation 1.7 %
1.7 %
DAM; Immersion 24h; ASTM D570
Viscosity Test 150 cm³/g
150 cm³/g
DAM; ISO 307 1157 1628
Linear Mold Shrinkage, Flow 0.0070 cm/cm
0.0070 in/in
DAM; ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.012 cm/cm
0.012 in/in
DAM; ISO 294-4 2577
Mechanical Properties Metric English Comments
Tensile Strength at Break 75.0 MPa
10900 psi
50%RH; ISO 527-1/-2
120 MPa
17400 psi
DAM; ISO 527-1/-2
Tensile Stress 15.93 MPa

@Strain 0.270 %,
Temperature 23.0 °C
 2310 psi

@Strain 0.270 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
16.9 MPa

@Strain 0.250 %,
Temperature -40.0 °C
 2450 psi

@Strain 0.250 %,
Temperature -40.0 °F
 DAM; ISO 11403-1 -2
58.34 MPa

@Strain 1.08 %,
Temperature 23.0 °C
 8462 psi

@Strain 1.08 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
58.9 MPa

@Strain 1.00 %,
Temperature -40.0 °C
 8540 psi

@Strain 1.00 %,
Temperature -40.0 °F
 DAM; ISO 11403-1 -2
93.71 MPa

@Strain 1.89 %,
Temperature 23.0 °C
 13590 psi

@Strain 1.89 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
96.35 MPa

@Strain 1.75 %,
Temperature -40.0 °C
 13970 psi

@Strain 1.75 %,
Temperature -40.0 °F
 DAM; ISO 11403-1 -2
120 MPa

@Strain 2.70 %,
Temperature 23.0 °C
 17400 psi

@Strain 2.70 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
128.5 MPa

@Strain 2.50 %,
Temperature -40.0 °C
 18640 psi

@Strain 2.50 %,
Temperature -40.0 °F
 DAM; ISO 11403-1 -2
Elongation at Break 3.0 %
3.0 %
DAM; ISO 527-1/-2
13 %
13 %
50%RH; ISO 527-1/-2
Tensile Modulus 3.50 GPa
508 ksi
50%RH; ISO 527-1/-2
5.50 GPa
798 ksi
DAM; ISO 527-1/-2
Flexural Strength 100 MPa
14500 psi
50%RH; ISO 178
190 MPa
27600 psi
DAM; ISO 178
Flexural Modulus 2.90 GPa
421 ksi
50%RH; ISO 178
4.90 GPa
711 ksi
DAM; ISO 178
Secant Modulus 0.846 GPa

@Strain 6.80 %,
Temperature 100 °C
 123 ksi

@Strain 6.80 %,
Temperature 212 °F
 DAM; ISO 11403-1 -2
1.04 GPa

@Strain 6.40 %,
Temperature 80.0 °C
 151 ksi

@Strain 6.40 %,
Temperature 176 °F
 DAM; ISO 11403-1 -2
1.37 GPa

@Strain 3.40 %,
Temperature 100 °C
 199 ksi

@Strain 3.40 %,
Temperature 212 °F
 DAM; ISO 11403-1 -2
1.63 GPa

@Strain 3.20 %,
Temperature 80.0 °C
 237 ksi

@Strain 3.20 %,
Temperature 176 °F
 DAM; ISO 11403-1 -2
1.74 GPa

@Strain 0.850 %,
Temperature 100 °C
 253 ksi

@Strain 0.850 %,
Temperature 212 °F
 DAM; ISO 11403-1 -2
2.2125 GPa

@Strain 0.800 %,
Temperature 80.0 °C
 320.90 ksi

@Strain 0.800 %,
Temperature 176 °F
 DAM; ISO 11403-1 -2
4.8037 GPa

@Strain 2.16 %,
Temperature 23.0 °C
 696.73 ksi

@Strain 2.16 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
5.39 GPa

@Strain 2.00 %,
Temperature -40.0 °C
 782 ksi

@Strain 2.00 %,
Temperature -40.0 °F
 DAM; ISO 11403-1 -2
5.40 GPa

@Strain 1.08 %,
Temperature 23.0 °C
 783 ksi

@Strain 1.08 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
5.89 GPa

@Strain 1.00 %,
Temperature -40.0 °C
 854 ksi

@Strain 1.00 %,
Temperature -40.0 °F
 DAM; ISO 11403-1 -2
5.90 GPa

@Strain 0.270 %,
Temperature 23.0 °C
 856 ksi

@Strain 0.270 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
6.76 GPa

@Strain 0.250 %,
Temperature -40.0 °C
 980 ksi

@Strain 0.250 %,
Temperature -40.0 °F
 DAM; ISO 11403-1 -2
Izod Impact, Notched (ISO) 4.00 kJ/m²
1.90 ft-lb/in²
50%RH; ISO 180/1A
4.50 kJ/m²
2.14 ft-lb/in²
DAM; ISO 180/1A
3.00 kJ/m²

@Temperature -40.0 °C
 1.43 ft-lb/in²

@Temperature -40.0 °F
 50%RH; ISO 180/1A
3.00 kJ/m²

@Temperature -30.0 °C
 1.43 ft-lb/in²

@Temperature -22.0 °F
 50%RH; ISO 180/1A
4.50 kJ/m²

@Temperature -40.0 °C
 2.14 ft-lb/in²

@Temperature -40.0 °F
 DAM; ISO 180/1A
4.50 kJ/m²

@Temperature -30.0 °C
 2.14 ft-lb/in²

@Temperature -22.0 °F
 DAM; ISO 180/1A
Izod Impact, Unnotched (ISO) 40.0 kJ/m²
19.0 ft-lb/in²
DAM; ISO 180/1U
55.0 kJ/m²
26.2 ft-lb/in²
50%RH; ISO 180/1U
28.0 kJ/m²

@Temperature -30.0 °C
 13.3 ft-lb/in²

@Temperature -22.0 °F
 50%RH; ISO 180/1U
35.0 kJ/m²

@Temperature -30.0 °C
 16.7 ft-lb/in²

@Temperature -22.0 °F
 DAM; ISO 180/1U
Charpy Impact Unnotched 3.20 J/cm²
15.2 ft-lb/in²
DAM; ISO 179/1eU
7.00 J/cm²
33.3 ft-lb/in²
50%RH; ISO 179/1eU
3.00 J/cm²

@Temperature -30.0 °C
 14.3 ft-lb/in²

@Temperature -22.0 °F
 DAM; ISO 179/1eU
3.00 J/cm²

@Temperature -30.0 °C
 14.3 ft-lb/in²

@Temperature -22.0 °F
 50%RH; ISO 179/1eU
Charpy Impact, Notched 0.500 J/cm²
2.38 ft-lb/in²
DAM; ISO 179/1eA
0.600 J/cm²
2.86 ft-lb/in²
50%RH; ISO 179/1eA
0.400 J/cm²

@Temperature -30.0 °C
 1.90 ft-lb/in²

@Temperature -22.0 °F
 50%RH; ISO 179/1eA
0.450 J/cm²

@Temperature -40.0 °C
 2.14 ft-lb/in²

@Temperature -40.0 °F
 DAM; ISO 179/1eA
Tensile Creep Modulus, 1 hour 3300 MPa

@Time 3600 sec
 479000 psi

@Time 1.00 hour
 50%RH; ISO 899-1
Tensile Creep Modulus, 1000 hours 2200 MPa

@Time 3.60e+6 sec
 319000 psi

@Time 1000 hour
 50%RH; ISO 899-1
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 40.0 µm/m-°C
22.2 µin/in-°F
DAM; ISO 11359-1/-2
CTE, linear, Transverse to Flow 96.0 µm/m-°C
53.3 µin/in-°F
DAM; ISO 11359-1/-2
Specific Heat Capacity 2.37 J/g-°C
0.566 BTU/lb-°F
Thermal Conductivity 0.160 W/m-K
1.11 BTU-in/hr-ft²-°F
of melt
Melting Point 262 °C
504 °F
DAM; 10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi) 258 °C
496 °F
DAM; ISO 75-1/-2
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+15 ohm-cm
>= 1.00e+15 ohm-cm
DAM; IEC 60093
Dissipation Factor 0.0070

@Frequency 100 Hz
 0.0070

@Frequency 100 Hz
 DAM; IEC 60250
0.0070

@Frequency 1.00e+6 Hz
 0.0070

@Frequency 1.00e+6 Hz
 DAM; IEC 60250
0.24

@Frequency 1.00e+6 Hz
 0.24

@Frequency 1.00e+6 Hz
 50%RH; IEC 60250
0.24

@Frequency 100 Hz
 0.24

@Frequency 100 Hz
 50%RH; IEC 60250