A. Schulman SCHULAMID® 66 MK40HI 40% Mineral Reinforced, Impact Modified 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 40% Mineral Filled |
| Manufacturer | A. Schulman, Inc. |
| Trade Name | SCHULAMID® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | A. Schulman SCHULAMID® 66 MK40HI 40% Mineral Reinforced, Impact Modified 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by A. Schulman.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.45 g/cc | 1.45 g/cc | ISO 1183/1 |
| Linear Mold Shrinkage | 0.0040 - 0.012 cm/cm @Thickness 3.175 mm |
0.0040 - 0.012 in/in @Thickness 0.1250 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 84.8 MPa | 12300 psi | ISO 527 |
| Tensile Modulus | 5.00 GPa | 725 ksi | ISO 527 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 120 °C | 248 °F | ISO 75 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 295 - 305 °C | 563 - 581 °F | |
| Mold Temperature | 65.6 - 93.3 °C | 150 - 200 °F | |
| Drying Temperature | 79.4 °C | 175 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | Predrying |
Users viewing this material also viewed the following:
- Nye Lubricants 5201 (SVLG) Synthetic Oil
- Plastcom SLOVAMID® 6/66 GF 15 GB 15 PA6/66 reinforced with glass fiber, glass beads
- NanoAmor 90%, OD/ID: 10-30/3-10 nm Aligned Multi-Walled Carbon Nanotubes
- Nitriflex SB-1006 AG Styrene Butadiene Copolymer
- Iran Petrochemical (PCC) PET BG-821 Polyethylene Terephthalate
- Solvay Specialty Polymers Algoflon® D 2711 F Polytetrafluoroethylene (PTFE)
- Ashley Polymers Ashlene® 266 PPO, 30% Glass Reinforced
- BCC Products Kwik Kast BC 8001 Urethane Casting
Copyright © lookpolymers.com All Rights Reserved