DuPont Performance Polymers Rynite® 530 BK503 PET (Unverified Data**)

Category	Polymer , Thermoplastic , Polyester, TP , Polyethylene Terephthalate (PET) , Polyethylene Terephthalate (PET), 30% Glass Reinforced
Manufacturer
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	DuPont Performance Polymers Rynite® 530 BK503 PET (Unverified Data**).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Rynite® 530 BK503 is a 30% glass reinforced modified polyethylene terephthalate with outstanding balance of strength, stiffness, and toughness, excellent electrical properties, surface appearance, and chemical resistance.Information provided by DuPont Performance Polymers

Physical Properties	Metric	English	Comments
Density	1.56 g/cc	0.0564 lb/in³	ISO 1183
Filler Content	30 %	30 %
Linear Mold Shrinkage, Flow	0.0030 cm/cm @Thickness 2.00 mm	0.0030 in/in @Thickness 0.0787 in	ISO 294-4, Similar
Linear Mold Shrinkage, Transverse	0.0090 cm/cm @Thickness 2.00 mm	0.0090 in/in @Thickness 0.0787 in	ISO 294-4, Similar

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	150 MPa @Temperature 23.0 °C	21800 psi @Temperature 73.4 °F	ISO 527
Elongation at Break	2.1 % @Temperature 23.0 °C	2.1 % @Temperature 73.4 °F	ISO 527
Tensile Modulus	10.2 GPa @Temperature 23.0 °C	1480 ksi @Temperature 73.4 °F	ISO 527
Flexural Strength	210 MPa @Temperature 23.0 °C	30500 psi @Temperature 73.4 °F	ISO 178
Flexural Modulus	3.00 GPa @Temperature 150 °C	435 ksi @Temperature 302 °F	ISO 178
	5.165 GPa @Temperature 90.0 °C	749.1 ksi @Temperature 194 °F	ISO 178
	8.94 GPa @Temperature 23.0 °C	1300 ksi @Temperature 73.4 °F	ISO 178
	10.367 GPa @Temperature -40.0 °C	1503.6 ksi @Temperature -40.0 °F	ISO 178
Izod Impact, Notched (ISO)	8.50 kJ/m² @Temperature -40.0 °C	4.04 ft-lb/in² @Temperature -40.0 °F	ISO 180/1A
	9.50 kJ/m² @Temperature 23.0 °C	4.52 ft-lb/in² @Temperature 73.4 °F	ISO 180/1A
Izod Impact, Unnotched (ISO)	35.0 kJ/m² @Temperature -40.0 °C	16.7 ft-lb/in² @Temperature -40.0 °F	ISO 180/1U
	45.0 kJ/m² @Temperature 23.0 °C	21.4 ft-lb/in² @Temperature 73.4 °F	ISO 180/1U
Charpy Impact Unnotched	4.50 J/cm² @Temperature -40.0 °C	21.4 ft-lb/in² @Temperature -40.0 °F	ISO 179/1eU
	5.20 J/cm² @Temperature 23.0 °C	24.7 ft-lb/in² @Temperature 73.4 °F	ISO 179/1eU
Charpy Impact, Notched	0.800 J/cm² @Temperature -40.0 °C	3.81 ft-lb/in² @Temperature -40.0 °F	ISO 179/1eA
	0.850 J/cm² @Temperature -30.0 °C	4.04 ft-lb/in² @Temperature -22.0 °F	ISO 179/1eA
	0.950 J/cm² @Temperature 23.0 °C	4.52 ft-lb/in² @Temperature 73.4 °F	ISO 179/1eA

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	244 °C	471 °F	ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi)	221 °C	430 °F	ISO 75-1/-2
UL RTI, Electrical	140 °C	284 °F	UL 746B
	140 °C @Thickness 0.810 mm	284 °F @Thickness 0.0319 in	UL 746B
	140 °C @Thickness 6.00 mm	284 °F @Thickness 0.236 in	UL 746B
	140 °C @Thickness 1.50 mm	284 °F @Thickness 0.0591 in	UL 746B
	140 °C @Thickness 2.00 mm	284 °F @Thickness 0.0787 in	UL 746B
UL RTI, Mechanical with Impact	140 °C	284 °F	UL 746B
	140 °C @Thickness 0.810 mm	284 °F @Thickness 0.0319 in	UL 746B
	140 °C @Thickness 1.50 mm	284 °F @Thickness 0.0591 in	UL 746B
	140 °C @Thickness 2.00 mm	284 °F @Thickness 0.0787 in	UL 746B
	140 °C @Thickness 6.00 mm	284 °F @Thickness 0.236 in	UL 746B
UL RTI, Mechanical without Impact	140 °C	284 °F	UL 746B
	140 °C @Thickness 2.00 mm	284 °F @Thickness 0.0787 in	UL 746B
	140 °C @Thickness 1.50 mm	284 °F @Thickness 0.0591 in	UL 746B
	140 °C @Thickness 0.810 mm	284 °F @Thickness 0.0319 in	UL 746B
	140 °C @Thickness 6.00 mm	284 °F @Thickness 0.236 in	UL 746B
Flammability, UL94	HB @Thickness 2.00 mm	HB @Thickness 0.0787 in	UL94
	HB @Thickness 0.810 mm	HB @Thickness 0.0319 in	UL94
	HB @Thickness 1.50 mm	HB @Thickness 0.0591 in	UL94
	HB @Thickness 3.00 mm	HB @Thickness 0.118 in	UL94
	HB @Thickness 6.00 mm	HB @Thickness 0.236 in	UL94
	HB @Thickness 6.00 mm	HB @Thickness 0.236 in	IEC 60695-11-10
	HB @Thickness 3.00 mm	HB @Thickness 0.118 in	IEC 60695-11-10
	HB @Thickness 2.00 mm	HB @Thickness 0.0787 in	IEC 60695-11-10
	HB @Thickness 1.50 mm	HB @Thickness 0.0591 in	IEC 60695-11-10
	HB @Thickness 0.810 mm	HB @Thickness 0.0319 in	IEC 60695-11-10
Glow Wire Test	800 °C @Thickness 2.00 mm	1470 °F @Thickness 0.0787 in	IEC 60695-2-12
	825 °C @Thickness 2.00 mm	1520 °F @Thickness 0.0787 in	Ignition; IEC 60695-2-13

Electrical Properties	Metric	English	Comments
Dielectric Strength	22.0 kV/mm @Thickness 2.00 mm, Temperature 23.0 °C	559 kV/in @Thickness 0.0787 in, Temperature 73.4 °F	2000 V/s, in oil; IEC 60243-1

Processing Properties	Metric	English	Comments
Melt Temperature	285 °C	545 °F	Optimum
	280 - 300 °C	536 - 572 °F
Mold Temperature	>= 95.0 °C	>= 203 °F
	110 °C	230 °F	optimum
Drying Temperature	120 °C	248 °F
Dry Time	4.00 hour	4.00 hour
Moisture Content	<= 0.020 %	<= 0.020 %

Descriptive Properties	Value	Comments
Appearance	Black Color
Drying Recommended	Yes
Features	Electrical Properties, Good
	Fatigue Resistance
	Stiffness, Good
	Strength, Good
	Thermal Aging Resistance, Good
Filler	Glass fiber reinforcement
Forms	Pellets
	Pellets
Generic	PET
Material Status	Current
Part Marking Code	>PET-GF30<	ISO 11469
Polymer Family	Polyester
Polymer Type	PET
Processing Method	Injection Molding
Product Category	Glass Reinforced Resins
Region Available - Global	Yes
Resin Identification	PET-GF30	ISO 1043
RoHS Compliance	Contact Manufacturer
Uses	Automotive Applications
	Electrical/Electronic Applications
	Housings
	Phenolic Replacement
	Structural Parts