- Acrylonitrile Butadiene Styrene (ABS), Heat Resistant, Molded
- Diamond Polymers ABS 4011 HH
Diamond Polymers ABS 4011 HH
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Heat Resistant, Molded |
| Manufacturer | Diamond and Network Polymers |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Diamond Polymers ABS 4011 HH.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Ultra High Heat ABSInformation provided by Diamond Polymers, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.09 g/cc | 1.09 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in | ASTM D955 |
| Melt Flow | 0.20 g/10 min @Load 10.0 kg, Temperature 220 °C |
0.20 g/10 min @Load 22.0 lb, Temperature 428 °F |
Procedure A; ASTM D1238 |
| 1.2 g/10 min @Load 5.00 kg, Temperature 265 °C |
1.2 g/10 min @Load 11.0 lb, Temperature 509 °F |
Procedure A; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 112 | 112 | ASTM D785 |
| Tensile Strength, Yield | 46.2 MPa | 6700 psi | chs 2 in/min; ASTM D638 |
| Flexural Modulus | 2.21 GPa | 320 ksi | Procedure B, Test Method I(chs 0.05 in/min); ASTM D790 |
| Izod Impact, Notched | 0.534 J/cm | 1.00 ft-lb/in | Test Method A (0.125 in bar); ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 122 °C | 252 °F | 0.125 in bar Unannealed/Conditioned 48 hours at 23°C; ASTM D648 |
| 130 °C | 266 °F | 0.25 in bar Unannealed/Conditioned 48 hours at 23°C; ASTM D648 | |
| Vicat Softening Point | 165 °C | 329 °F | 0.125 inch, 1 Kg; ASTM D1525 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Middle Barrel Temperature | 200 - 250 °C | 392 - 482 °F | |
| Mold Temperature | 40.0 - 80.0 °C | 104 - 176 °F | Higher mold temperature provides a product with excellent surface finishing and less residual stress. |
| Drying Temperature | 80.0 - 90.0 °C | 176 - 194 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | |
| Injection Pressure | 4.83 - 7.58 MPa | 700 - 1100 psi |
Users viewing this material also viewed the following:
- Polykemi AB SCANAMID 66 A43^E F14 Nylon 66, Glass Fiber Reinforced, Modified
- PolyOne Edgetek® PF-20GF/000 Polysulfone (PSU)
- Plaskolite West Optix® CA-927 G HF Clear Impact Modified Acrylic Resin
- Entec Hypel® PELLD60/.925 LLDPE (discontinued **)
- DSM Akulon® K223-KM6 Nylon 6-30% Mineral Reinforced (European Grade) (Dry) (discontinued **)
- Gromax BTE25-DN00N1 Nylon 6 (Dry)
- H.C. Starck Molybdenum Hafnium Carbide Powder, Metallurgy Alloy Bar MHC
- Techmer ES HiFill® PA4/6 HS LBK
- Techmer ES Luriblend® PA4/6 HS TL15
- Colorite Polymers Weatherflex™ CS1522WX (NTL01P) Wire and Cable Vinyl Compound
Copyright © lookpolymers.com All Rights Reserved