Haynes R-41 alloy, 0.635 mm thick sheet, solution heat treated at 1079°C, water quenched, 30 minutes at 1066°C, aged 16 hours at 760°C (1400°F), air cooled

Category Metal , Nonferrous Metal , Nickel Alloy , Superalloy
Manufacturer Haynes International, Inc.
Trade Name
Port Ningbo port,China
Trade Terms EXW, FOB, CFR, CIF
Payment Terms L/C, T/T, PayPal
Download PDF Haynes R-41 alloy, 0.635 mm thick sheet, solution heat treated at 1079°C, water quenched, 30 minutes at 1066°C, aged 16 hours at 760°C (1400°F), air cooled.pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
Vacuum melted, exceptionally high strength at temperature between 649-982°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications include afterburner parts and nozzle diaphragm partitions in current gas turbine engines. Formed with success on drop-hammers, expanding mandrels and stretch formers.Data provided by the manufacturer, Haynes International, Inc.
Physical Properties Metric English Comments
Density 8.25 g/cc
0.298 lb/in³
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 664 MPa
<br>@Temperature 871 °C
 96300 psi
<br>@Temperature 1600 °F
924 MPa
<br>@Temperature 760 °C
 134000 psi
<br>@Temperature 1400 °F
1047 MPa
<br>@Temperature 649 °C
 151900 psi
<br>@Temperature 1200 °F
Tensile Strength, Yield 506 MPa
<br>@Strain 0.200 %,<br> Temperature 871 °C
 73400 psi
<br>@Strain 0.200 %,<br> Temperature 1600 °F
785 MPa
<br>@Strain 0.200 %,<br> Temperature 760 °C
 114000 psi
<br>@Strain 0.200 %,<br> Temperature 1400 °F
847 MPa
<br>@Strain 0.200 %,<br> Temperature 649 °C
 123000 psi
<br>@Strain 0.200 %,<br> Temperature 1200 °F
Elongation at Break 2.0 %
<br>@Temperature 871 °C
 2.0 %
<br>@Temperature 1600 °F
 in 50.8 mm
4.0 %
<br>@Temperature 760 °C
 4.0 %
<br>@Temperature 1400 °F
 in 50.8 mm
7.0 %
<br>@Temperature 649 °C
 7.0 %
<br>@Temperature 1200 °F
 in 50.8 mm
Modulus of Elasticity 185 GPa
26800 ksi
RT
110 GPa
<br>@Temperature 871 °C
 16000 ksi
<br>@Temperature 1600 °F
163 GPa
<br>@Temperature 760 °C
 23600 ksi
<br>@Temperature 1400 °F
185 GPa
<br>@Temperature 649 °C
 26800 ksi
<br>@Temperature 1200 °F
Poissons Ratio 0.31
0.31
27°C (80°F)
0.31
<br>@Temperature 149 °C
 0.31
<br>@Temperature 300 °F
0.32
<br>@Temperature 482 °C
 0.32
<br>@Temperature 900 °F
0.32
<br>@Temperature 371 °C
 0.32
<br>@Temperature 700 °F
0.32
<br>@Temperature 260 °C
 0.32
<br>@Temperature 500 °F
0.33
<br>@Temperature 760 °C
 0.33
<br>@Temperature 1400 °F
0.33
<br>@Temperature 677 °C
 0.33
<br>@Temperature 1250 °F
0.33
<br>@Temperature 649 °C
 0.33
<br>@Temperature 1200 °F
0.34
<br>@Temperature 843 °C
 0.34
<br>@Temperature 1550 °F
0.35
<br>@Temperature 927 °C
 0.35
<br>@Temperature 1700 °F
Shear Modulus 83.0 GPa
12000 ksi
27°C
55.0 GPa
<br>@Temperature 927 °C
 7980 ksi
<br>@Temperature 1700 °F
61.0 GPa
<br>@Temperature 843 °C
 8850 ksi
<br>@Temperature 1550 °F
64.0 GPa
<br>@Temperature 760 °C
 9280 ksi
<br>@Temperature 1400 °F
67.0 GPa
<br>@Temperature 677 °C
 9720 ksi
<br>@Temperature 1250 °F
69.0 GPa
<br>@Temperature 593 °C
 10000 ksi
<br>@Temperature 1100 °F
72.0 GPa
<br>@Temperature 482 °C
 10400 ksi
<br>@Temperature 900 °F
75.0 GPa
<br>@Temperature 371 °C
 10900 ksi
<br>@Temperature 700 °F
77.0 GPa
<br>@Temperature 260 °C
 11200 ksi
<br>@Temperature 500 °F
81.0 GPa
<br>@Temperature 149 °C
 11700 ksi
<br>@Temperature 300 °F
Thermal Properties Metric English Comments
CTE, linear 13.5 µm/m-°C
<br>@Temperature 21.0 - 538 °C
 7.50 µin/in-°F
<br>@Temperature 69.8 - 1000 °F
14.0 µm/m-°C
<br>@Temperature 21.0 - 649 °C
 7.78 µin/in-°F
<br>@Temperature 69.8 - 1200 °F
14.8 µm/m-°C
<br>@Temperature 21.0 - 760 °C
 8.22 µin/in-°F
<br>@Temperature 69.8 - 1400 °F
15.2 µm/m-°C
<br>@Temperature 21.0 - 871 °C
 8.44 µin/in-°F
<br>@Temperature 69.8 - 1600 °F
16.3 µm/m-°C
<br>@Temperature 21.0 - 927 °C
 9.06 µin/in-°F
<br>@Temperature 69.8 - 1700 °F
16.8 µm/m-°C
<br>@Temperature 21.0 - 982 °C
 9.33 µin/in-°F
<br>@Temperature 69.8 - 1800 °F
Specific Heat Capacity 0.452 J/g-°C
<br>@Temperature 21.0 °C
 0.108 BTU/lb-°F
<br>@Temperature 69.8 °F
Thermal Conductivity 11.5 W/m-K
<br>@Temperature 149 °C
 79.8 BTU-in/hr-ft²-°F
<br>@Temperature 300 °F
12.5 W/m-K
<br>@Temperature 204 °C
 86.8 BTU-in/hr-ft²-°F
<br>@Temperature 399 °F
13.6 W/m-K
<br>@Temperature 260 °C
 94.4 BTU-in/hr-ft²-°F
<br>@Temperature 500 °F
14.7 W/m-K
<br>@Temperature 316 °C
 102 BTU-in/hr-ft²-°F
<br>@Temperature 601 °F
16.8 W/m-K
<br>@Temperature 427 °C
 117 BTU-in/hr-ft²-°F
<br>@Temperature 801 °F
18.8 W/m-K
<br>@Temperature 538 °C
 130 BTU-in/hr-ft²-°F
<br>@Temperature 1000 °F
20.0 W/m-K
<br>@Temperature 593 °C
 139 BTU-in/hr-ft²-°F
<br>@Temperature 1100 °F
21.0 W/m-K
<br>@Temperature 644 °C
 146 BTU-in/hr-ft²-°F
<br>@Temperature 1190 °F
22.0 W/m-K
<br>@Temperature 704 °C
 153 BTU-in/hr-ft²-°F
<br>@Temperature 1300 °F
23.1 W/m-K
<br>@Temperature 760 °C
 160 BTU-in/hr-ft²-°F
<br>@Temperature 1400 °F
24.1 W/m-K
<br>@Temperature 816 °C
 167 BTU-in/hr-ft²-°F
<br>@Temperature 1500 °F
25.1 W/m-K
<br>@Temperature 871 °C
 174 BTU-in/hr-ft²-°F
<br>@Temperature 1600 °F
Melting Point 1310 - 1345 °C
2390 - 2453 °F
Solidus 1310 °C
2390 °F
Liquidus 1335 °C
2435 °F
Component Elements Properties Metric English Comments
Aluminum, Al 1.4 - 1.6 %
1.4 - 1.6 %
Boron, B 0.0030 - 0.010 %
0.0030 - 0.010 %
Carbon, C 0.050 - 0.12 %
0.050 - 0.12 %
Chromium, Cr 18 - 20 %
18 - 20 %
Cobalt, Co 10 - 12 %
10 - 12 %
Iron, Fe <= 5.0 %
<= 5.0 %
Manganese, Mn <= 0.10 %
<= 0.10 %
Molybdenum, Mo 9.0 - 10.5 %
9.0 - 10.5 %
Nickel, Ni 53 %
53 %
As Remainder
Silicon, Si <= 0.50 %
<= 0.50 %
Sulfur, S <= 0.015 %
<= 0.015 %
Titanium, Ti 3.0 - 3.3 %
3.0 - 3.3 %
Electrical Properties Metric English Comments
Magnetic Permeability <= 1.002
<br>@Temperature 21.0 °C
 <= 1.002
<br>@Temperature 69.8 °F
 200 Oersted