TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, 10.0 PHR TCP Plasticizer

Category	Polymer , Thermoset , Polyester, TS , Polyurethane, TS , Thermoset Polyurethane, Elastomer, Unreinforced , Rubber or Thermoset Elastomer (TSE)
Manufacturer
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, 10.0 PHR TCP Plasticizer.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Millathane® 76 is a very suitable choice for use in products such as bushings, small copier rolls; automotive applications — bumpers, o-rings, hydraulic seals, belts, gaskets, solid tires — and many other high performance polyurethane applications. Millathane 76 can be vulcanized by sulfur or peroxide cured systems.Plasticizers should be used in all Millathane®76 compounds to better incorporate fillers and improve processing. Some plasticizers are not compatible with Millathane76, e.g. naphthenic and all paraffinic oils, however, a number of ester plasticizers perform very well.FormulationMillathane 76 100.0Zinc Stearate0.5N-550 Black40.0MBTS4.0MBT2.0Thanecure® ZM1.0Sulfur1.5Plasticizer10.0All information provided by TSE Industries

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	65	65
	73	73	heat aged 70 hours @ 100ºC
Tensile Strength, Yield	23.82 MPa	3455 psi
Elongation at Yield	541 %	541 %
100% Modulus	0.00314 GPa	0.456 ksi
200% Modulus	0.007274 GPa	1.055 ksi
300% Modulus	0.01216 GPa	1.764 ksi
Tear Strength	66.2 kN/m	378 pli	Die C
Compression Set	36.4 % @Temperature 70.0 °C, Time 79200 sec	36.4 % @Temperature 158 °F, Time 22.0 hour

Thermal Properties	Metric	English	Comments
Brittleness Temperature	-35.0 °C	-31.0 °F

Processing Properties	Metric	English	Comments
Cure Time	10.0 min @Temperature 155 °C	0.167 hour @Temperature 311 °F

Descriptive Properties	Value	Comments
Weight Loss (%)	1.9	heat aged 70 hours @ 100ºC