- Acrylonitrile Butadiene Styrene (ABS), Heat Resistant, Molded
- Diamond Polymers ABS 4003HH
Diamond Polymers ABS 4003HH
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Heat Resistant, Molded |
| Manufacturer | Diamond and Network Polymers |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Diamond Polymers ABS 4003HH.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Heat Resistant Grade, Very High HeatInformation provided by Diamond Polymers, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.07 g/cc | 1.07 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0040 - 0.0060 cm/cm | 0.0040 - 0.0060 in/in | ASTM D955 |
| Melt Flow | 0.80 g/10 min @Load 5.00 kg, Temperature 200 °C |
0.80 g/10 min @Load 11.0 lb, Temperature 392 °F |
Procedure A Condition G; ASTM D1238 |
| 3.0 g/10 min @Load 3.80 kg, Temperature 230 °C |
3.0 g/10 min @Load 8.38 lb, Temperature 446 °F |
Procedure A Condition I; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 112 | 112 | ASTM D785 |
| Tensile Strength, Yield | 49.0 MPa | 7100 psi | chs 2 in/min; ASTM D638 |
| Flexural Modulus | 2.45 GPa | 356 ksi | Tangent, chs 0.05 in/min; ASTM D790 |
| Izod Impact, Notched | 1.60 J/cm @Thickness 3.17 mm, Temperature 23.0 °C |
3.00 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
bar; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 91.1 °C | 196 °F | 0.125 in bar Unannealed/Conditioned 48 hours at 23°C; ASTM D648 |
| 106 °C | 223 °F | 0.125 in bar Annealed 4 hours at 80°C; ASTM D648 | |
| Vicat Softening Point | 118 °C | 244 °F | 0.125 inch, 1 Kg; ASTM D1525 |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Middle Barrel Temperature | 200 - 250 °C | 392 - 482 °F | |
| Mold Temperature | 40.0 - 80.0 °C | 104 - 176 °F | Higher mold temperature provides a product with excellent surface finishing and less residual stress. |
| Drying Temperature | 80.0 - 90.0 °C | 176 - 194 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | |
| Injection Pressure | 4.83 - 7.58 MPa | 700 - 1100 psi |
Users viewing this material also viewed the following:
- Polymax® Maxelast® A9930 TPE, ABS/PC Overmold
- Ineos ABS Lustran® 266 Specialty, Transparent (discontinued **)
- Materion Brush 1915â„¢ Heat Treated Temper Wire, 0.375" - 0.500"
- Multibase Multi-Flex® A 7455 ER TPE Thermoplastic Elastomer
- SABIC Innovative Plastics LNP LUBRILOY RF206H PA 66 (Asia Pacific)
- ExxonMobil Mobil Avrex S Turbo 256
- Zeon Chemicals Sivic® Z760 Polyblend Nitrile Elastomer
- ExxonMobil Escorene™ FL 00209 Ethylene Vinyl Acetate Copolymer (European Grade)
- DuPont Performance Polymers Hytrel® HTR8441 BK316 Polyester Elastomer TPC-ET (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved