Lucobit Lucofin® 1400MN Powder Ethylene Butyl Acrylate
| Category | Polymer , Thermoplastic , Ethylene Butyl Acrylate |
| Manufacturer | Lucobit AG |
| Trade Name | Lucofin® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lucobit Lucofin® 1400MN Powder Ethylene Butyl Acrylate.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Lucofin 1400MN Powder is a polar copolymer consisting of ethylene and butyl acrylate with low crystallinity. Due to its chemical structure Lucofin 1400MN Powder is softer and more flexible ethane ethylene homopolymers with comparable density.Applications:• Supporting material for compounds• Polymer modification of bitumen and asphalt• Powder coating• RotomoldingInformation provided by Lucobit AG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.924 g/cc | 0.0334 lb/in³ | ISO 1183 |
| Particle Size | 500 µm | 500 µm | ASTM D 1921 |
| Melt Flow | 7.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
7.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 88 | 88 | ISO 868 |
| Hardness, Shore D | 32 | 32 | ISO 868 |
| Tensile Strength, Yield | 3.50 MPa | 508 psi | ISO 527 |
| Elongation at Yield | 13 % | 13 % | ISO 527 |
| Modulus of Elasticity | 0.0450 GPa | 6.53 ksi | ISO 527 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 95.0 °C | 203 °F | ISO 3146 |
| Vicat Softening Point | 60.0 °C | 140 °F | ISO 306 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 160 - 220 °C | 320 - 428 °F | Rotomolding |
| 160 - 240 °C | 320 - 464 °F | Bitumen modification | |
| 160 - 270 °C | 320 - 518 °F | Coatings | |
| 160 - 290 °C | 320 - 554 °F | Compounding |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Comonomer BA | 0.17 | DIN 51451 |
Users viewing this material also viewed the following:
- Omya OMYAFLOW® 3 - SY Calcium Carbonate
- Precision Polymer Engineering S40H Silicone Rubber
- Ipiranga Petrochem PRB 0131 Polypropylene
- Zhejiang Juner PA66-301-G20 Flame-Retardant & Glass Reinforced, Environmental PA66
- ExxonMobil Exceed™ 4518PA Premium Cast Film Resin
- ExxonMobil LDPE LD 506.07 Low Density Polyethylene Resin
- Arkema Group Orevac® 9309 Film EVA-MAH Terpolymer
- AK Steel ASTM A 1011, Class 1 Formable, Grade 60K Hot Rolled Carbon Steel, Medium/High Strength Low Alloy Steel (HSLA)
- Arkema Group EVATANE® 28-420 Copolymer Ethylene - Vinyl Acetate
- Addiplast Addilene PMD 50203 Flame Retardant Polypropylene
Copyright © lookpolymers.com All Rights Reserved