POLYMER SEARCH

DSM Stanyl® TS200F6 PA46-GF30

Category	Polymer , Thermoplastic , Nylon , Nylon 46 , Nylon 46, Glass Fiber Reinforced
Manufacturer	DSM Engineering Plastics
Trade Name	Stanyl®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	DSM Stanyl® TS200F6 PA46-GF30.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

30% Glass Reinforced

Physical Properties	Metric	English	Comments
Density	1.41 g/cc	0.0509 lb/in³	dry; ISO 1183
Moisture Absorption	2.60 %	2.60 %	Sim. To ISO 62
Linear Mold Shrinkage, Flow	0.0050 cm/cm	0.0050 in/in	Sim. To ISO 294-4
Linear Mold Shrinkage, Transverse	0.013 cm/cm	0.013 in/in	Sim. To ISO 294-4

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	115 MPa	16700 psi	cond; ISO 527-1/-2
	210 MPa	30500 psi	dry; ISO 527-1/-2
	90.0 MPa @Temperature 200 °C	13100 psi @Temperature 392 °F	ISO 527-1/-2
	95.0 MPa @Temperature 180 °C	13800 psi @Temperature 356 °F	ISO 527-1/-2
	100 MPa @Temperature 160 °C	14500 psi @Temperature 320 °F	ISO 527-1/-2
	110 MPa @Temperature 120 °C	16000 psi @Temperature 248 °F	ISO 527-1/-2
Elongation at Break	4.0 %	4.0 %	dry; ISO 527-1/-2
	7.0 %	7.0 %	cond; ISO 527-1/-2
	7.5 % @Temperature 120 °C	7.5 % @Temperature 248 °F	ISO 527-1/-2
	7.5 % @Temperature 160 °C	7.5 % @Temperature 320 °F	ISO 527-1/-2
	7.5 % @Temperature 180 °C	7.5 % @Temperature 356 °F	ISO 527-1/-2
	7.5 % @Temperature 200 °C	7.5 % @Temperature 392 °F	ISO 527-1/-2
Tensile Modulus	6.00 GPa	870 ksi	cond; ISO 527-1/-2
	10.0 GPa	1450 ksi	dry; ISO 527-1/-2
	4.00 GPa @Temperature 200 °C	580 ksi @Temperature 392 °F	ISO 527-1/-2
	4.40 GPa @Temperature 180 °C	638 ksi @Temperature 356 °F	ISO 527-1/-2
	5.00 GPa @Temperature 160 °C	725 ksi @Temperature 320 °F	ISO 527-1/-2
	5.50 GPa @Temperature 120 °C	798 ksi @Temperature 248 °F	ISO 527-1/-2
Flexural Modulus	5.50 GPa	798 ksi	cond; ISO 178
	9.00 GPa	1310 ksi	dry; ISO 178
	3.90 GPa @Temperature 160 °C	566 ksi @Temperature 320 °F	ISO 178
	4.70 GPa @Temperature 120 °C	682 ksi @Temperature 248 °F	ISO 178
Izod Impact Resistance	1.10 J/cm² @Temperature -40.0 °C	5.24 ft-lb/in² @Temperature -40.0 °F	cond; ISO 180/1A
	1.10 J/cm² @Temperature -40.0 °C	5.24 ft-lb/in² @Temperature -40.0 °F	dry; ISO 180/1A
	1.20 J/cm² @Temperature 23.0 °C	5.71 ft-lb/in² @Temperature 73.4 °F	dry; ISO 180/1A
	2.10 J/cm² @Temperature 23.0 °C	9.99 ft-lb/in² @Temperature 73.4 °F	cond; ISO 180/1A
Charpy Impact Unnotched	6.50 J/cm² @Temperature -30.0 °C	30.9 ft-lb/in² @Temperature -22.0 °F	dry; ISO 179/1eU
	7.50 J/cm² @Temperature -30.0 °C	35.7 ft-lb/in² @Temperature -22.0 °F	cond; ISO 179/1eU
	8.00 J/cm² @Temperature 23.0 °C	38.1 ft-lb/in² @Temperature 73.4 °F	dry; ISO 179/1eU
	10.0 J/cm² @Temperature 23.0 °C	47.6 ft-lb/in² @Temperature 73.4 °F	cond; ISO 179/1eU
Charpy Impact, Notched	1.10 J/cm² @Temperature -30.0 °C	5.23 ft-lb/in² @Temperature -22.0 °F	cond; ISO 179/1eA
	1.10 J/cm² @Temperature -30.0 °C	5.23 ft-lb/in² @Temperature -22.0 °F	dry; ISO 179/1eA
	1.20 J/cm² @Temperature 23.0 °C	5.71 ft-lb/in² @Temperature 73.4 °F	dry; ISO 179/1eA
	2.10 J/cm² @Temperature 23.0 °C	9.99 ft-lb/in² @Temperature 73.4 °F	cond; ISO 179/1eA

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	25.0 µm/m-°C	13.9 µin/in-°F	dry; ISO 11359-1/-2
CTE, linear, Transverse to Flow	60.0 µm/m-°C	33.3 µin/in-°F	dry; ISO 11359-1/-2
Melting Point	295 °C	563 °F	10°C/min; ISO 11357-1/-3
Maximum Service Temperature, Air	152 °C	306 °F	5000 hours Thermal Index; IEC 60216/ISO 527-1/-2
Deflection Temperature at 1.8 MPa (264 psi)	290 °C	554 °F	dry; ISO 75-1/-2
Flammability, UL94	HB @Thickness 1.50 mm	HB @Thickness 0.0591 in	dry; IEC 60695-11-10
	HB @Thickness 0.830 mm	HB @Thickness 0.0327 in	dry; IEC 60695-11-10

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+11 ohm-cm	1.00e+11 ohm-cm	cond; IEC 60093
	1.00e+15 ohm-cm	1.00e+15 ohm-cm	dry; IEC 60093
Dielectric Strength	25.0 kV/mm	635 kV/in	cond; IEC 60243-1
	35.0 kV/mm	889 kV/in	dry; IEC 60243-1
Comparative Tracking Index	500 V	500 V	dry; IEC 60112