- A. Schulman SCHULAMID® 66 MF40 Mineral Filled Nylon 66
A. Schulman SCHULAMID® 66 MF40 Mineral Filled Nylon 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Mineral Filled, Impact Grade |
| Manufacturer | A. Schulman, Inc. |
| Trade Name | SCHULAMID® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | A. Schulman SCHULAMID® 66 MF40 Mineral Filled Nylon 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by A. Schulman.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.48 g/cc | 1.48 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0080 cm/cm @Thickness 3.175 mm |
0.0080 in/in @Thickness 0.1250 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 82.7 MPa | 12000 psi | ASTM D638 |
| Elongation at Break | 4.0 % | 4.0 % | ASTM D638 |
| Flexural Strength | 137 MPa | 19900 psi | ASTM D790 |
| Flexural Modulus | 6.89 GPa | 1000 ksi | ASTM D790 |
| Izod Impact, Notched | 0.374 J/cm | 0.700 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 3.74 J/cm | 7.00 ft-lb/in | ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 223 °C | 433 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 149 °C | 300 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 295 - 305 °C | 563 - 581 °F | |
| Mold Temperature | 65.6 - 93.3 °C | 150 - 200 °F | |
| Drying Temperature | 79.4 °C | 175 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | Predrying |
Users viewing this material also viewed the following:
- Karina E 39/81-IE MBU Pink Color Concentrate
- Sylvin Technologies 8950-75 Natural PVC Extrusion Compound
- SABIC Innovative Plastics Xenoy® 1105 PBT+PC (Asia Pacific)
- SABIC Innovative Plastics LNP LUBRICOMP IP004Z PA6.12 (Europe-Africa-Middle East)
- A. Schulman POLYFLAM™ FLP 3714 20% Glass Filled HDPE
- Master Bond EP36 High Temperature Resistant, Toughened Epoxy System
- CP-Polymer-Technik Wellamid® 6600 MR 209 HWCP 20% Mineral Nylon 66, Heat Stabilized, Dry
- Eagle Brass 101 OFE COPPER (Certified), Annealed
- Alcoa KAMA 1500 Freezer Modified OPS (discontinued **)
- PolyOne Elastamax XL 1092-35 TPU-Based Thermoplastic Elastomer (discontinued **)
Copyright © lookpolymers.com All Rights Reserved