DSM Stanyl® 46HF5041LW Nylon 46-40% Glass Reinforced (European and Asian Grade) (Dry)

Category	Polymer , Thermoplastic , Nylon , Nylon 46 , Nylon 46, Glass Fiber Reinforced
Manufacturer	DSM Engineering Plastics
Trade Name	Stanyl®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	DSM Stanyl® 46HF5041LW Nylon 46-40% Glass Reinforced (European and Asian Grade) (Dry).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Stanyl is a high performance polyamide providing good performance and value across a broad range of automotive and electronic applications. Stanyl offers:Highest mechanical properties at high temperatures Excellent resistance to wear and low friction Outstanding flow for easy processing and exceptional design freedomStanyl High Flowgrades that match the best flowing LCPs while maintaining a high level of mechanical propertiesKey Applications: Automotive: Powertrain components, Charge-air coolers, EPS and ETC gears, Motor Sensors, Auto connectors, Chain tensionersE&E: Connectors, Microswitches, Bobbins, Memory modules, Motor components, Industrial, Specialty films and fibers, Consumer appliancesInformation provided by DSM.

Physical Properties	Metric	English	Comments
Density	1.87 g/cc	0.0676 lb/in³	ISO 1183
Moisture Absorption at Equilibrium	1.1 %	1.1 %	Humidity Absorption; Sim. to ISO 62
Viscosity Test	70 cm³/g	70 cm³/g	Viscosity Number
Linear Mold Shrinkage, Flow	0.0030 cm/cm	0.0030 in/in	ISO 294-4
Linear Mold Shrinkage, Transverse	0.0070 cm/cm	0.0070 in/in	ISO 294-4

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	150 MPa	21800 psi	ISO 527-1/-2
Elongation at Break	1.3 %	1.3 %	ISO 527-1/-2
Tensile Modulus	16.0 GPa	2320 ksi	ISO 527-1/-2
Charpy Impact Unnotched	2.50 J/cm² @Temperature 23.0 °C	11.9 ft-lb/in² @Temperature 73.4 °F	ISO 179/1eU
Charpy Impact, Notched	0.800 J/cm² @Temperature 23.0 °C	3.81 ft-lb/in² @Temperature 73.4 °F	ISO 179/1eA

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	20.0 µm/m-°C @Temperature 20.0 °C	11.1 µin/in-°F @Temperature 68.0 °F	ISO 11359-1/-2
CTE, linear, Transverse to Flow	80.0 µm/m-°C @Temperature 20.0 °C	44.4 µin/in-°F @Temperature 68.0 °F	ISO 11359-1/-2
Melting Point	295 °C	563 °F	10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi)	290 °C	554 °F	ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi)	270 °C	518 °F	ISO 75-1/-2
Vicat Softening Point	290 °C	554 °F	50°C/h 50N; ISO 306
Glass Transition Temp, Tg	75.0 °C	167 °F	Glass Transition Temperature (10°C/min); ISO 11357-1/-2
UL RTI, Electrical	140 °C @Thickness 1.50 mm	284 °F @Thickness 0.0591 in	UL746B
	140 °C @Thickness 0.750 mm	284 °F @Thickness 0.0295 in	UL746B
UL RTI, Mechanical with Impact	110 °C @Thickness 0.750 mm	230 °F @Thickness 0.0295 in	UL746B
	125 °C @Thickness 1.50 mm	257 °F @Thickness 0.0591 in	UL746B
UL RTI, Mechanical without Impact	120 °C @Thickness 0.750 mm	248 °F @Thickness 0.0295 in	UL746B
	125 °C @Thickness 1.50 mm	257 °F @Thickness 0.0591 in	UL746B
Flammability, UL94	V-0 @Thickness 0.400 mm	V-0 @Thickness 0.0157 in	IEC 60695-11-10
	V-0 @Thickness 1.60 mm	V-0 @Thickness 0.0630 in	IEC 60695-11-10
Glow Wire Test	825 °C @Thickness 0.750 mm	1520 °F @Thickness 0.0295 in	Glow Wire Ignition Temperature; IEC 60695-2-13
	925 °C @Thickness 3.00 mm	1700 °F @Thickness 0.118 in	Glow Wire Ignition Temperature; IEC 60695-2-13
	960 °C @Thickness 0.750 mm	1760 °F @Thickness 0.0295 in	Glow Wire Flammability Index; IEC 60695-2-12
	960 °C @Thickness 3.00 mm	1760 °F @Thickness 0.118 in	Glow Wire Flammability Index; IEC 60695-2-12

Electrical Properties	Metric	English	Comments
Comparative Tracking Index	250 - 399 V	250 - 399 V	PLC 2; UL 746A

Descriptive Properties	Value	Comments
Flame Retardant	Yes
Flame Retarding Agent	Yes
Heat stabilized or stable to heat	Yes
Injection molding	Yes
Lubricants	Yes
Platable	Yes
Release Agent	Yes
With Fillers	Yes