Aleris Hokotol Aluminum Alloy, 100 mm Thickness

Category Metal , Nonferrous Metal , Aluminum Alloy , 7000 Series Aluminum Alloy
Manufacturer Aleris
Trade Name Hokotol
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Aleris Hokotol Aluminum Alloy, 100 mm Thickness.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Sample treatment not specified for property data.Applications include molds for blow forming and injection molding for plastics; bolsters and force plates; high strength/low weight machine parts; and mechanical components with elevated mechanical properties. Poor weldability and corrosion resistance. Very good machinability.
Physical Properties Metric English Comments
Density 2.83 g/cc
0.102 lb/in³
Mechanical Properties Metric English Comments
Hardness, Brinell 180
180
Hardness, Knoop 232
232
Estimated from Brinell
Hardness, Rockwell A 59
59
Estimated from Brinell
Hardness, Rockwell B 96
96
Estimated from Brinell
Hardness, Vickers 217
217
Estimated from Brinell
Tensile Strength, Ultimate >= 550 MPa
>= 79800 psi
Minimum
575 MPa
83400 psi
Typical
120 MPa

@Temperature 200 °C
17400 psi

@Temperature 392 °F
Typical, after 10,000 hours
225 MPa

@Temperature 150 °C
32600 psi

@Temperature 302 °F
Typical, after 10,000 hours
450 MPa

@Temperature 100 °C
65300 psi

@Temperature 212 °F
Typical, after 10,000 hours
Tensile Strength, Yield >= 495 MPa

@Strain 0.200 %
>= 71800 psi

@Strain 0.200 %
Minimum
535 MPa

@Strain 0.200 %
77600 psi

@Strain 0.200 %
Typical
Elongation at Break >= 4.0 %
>= 4.0 %
Minimum
7.5 %
7.5 %
Typical
Modulus of Elasticity 70.3 GPa
10200 ksi
Machinability 90 %
90 %
Shear Strength 340 MPa
49300 psi
Calculated
Thermal Properties Metric English Comments
CTE, linear 23.5 µm/m-°C

@Temperature 20.0 - 100 °C
13.1 µin/in-°F

@Temperature 68.0 - 212 °F
Thermal Conductivity 154 W/m-K
1070 BTU-in/hr-ft²-°F
Component Elements Properties Metric English Comments
Aluminum, Al 86 - 90.9 %
86 - 90.9 %
as balance
Chromium, Cr <= 0.10 %
<= 0.10 %
Copper, Cu 1.5 - 2.6 %
1.5 - 2.6 %
Iron, Fe <= 0.30 %
<= 0.30 %
Magnesium, Mg 1.8 - 2.6 %
1.8 - 2.6 %
Manganese, Mn <= 0.15 %
<= 0.15 %
Other, total <= 0.15 %
<= 0.15 %
Silicon, Si <= 0.20 %
<= 0.20 %
Titanium, Ti <= 0.060 %
<= 0.060 %
Zinc, Zn 5.7 - 7.6 %
5.7 - 7.6 %
Zirconium, Zr 0.080 - 0.25 %
0.080 - 0.25 %
Electrical Properties Metric English Comments
Electrical Resistivity 0.00000430 ohm-cm
0.00000430 ohm-cm