DSM Novamid® 3010GN30 NAT PA66-GF30 FR(17)
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled |
| Manufacturer | DSM Engineering Plastics |
| Trade Name | Novamid® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DSM Novamid® 3010GN30 NAT PA66-GF30 FR(17).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
30% Glass Reinforced, Flame Retardant
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.40 g/cc | 0.0506 lb/in³ | dry; ISO 1183 |
| Moisture Absorption | 1.60 % | 1.60 % | Sim. To ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm | 0.0030 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.012 cm/cm | 0.012 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 120 MPa | 17400 psi | cond; ISO 527-1/-2 |
| 170 MPa | 24700 psi | dry; ISO 527-1/-2 | |
| Elongation at Break | 2.0 % | 2.0 % | dry; ISO 527-1/-2 |
| 2.9 % | 2.9 % | cond; ISO 527-1/-2 | |
| Tensile Modulus | 8.00 GPa | 1160 ksi | cond; ISO 527-1/-2 |
| 11.5 GPa | 1670 ksi | dry; ISO 527-1/-2 | |
| Flexural Strength | 210 MPa | 30500 psi | cond; ISO 178 |
| 260 MPa | 37700 psi | dry; ISO 178 | |
| Flexural Modulus | 8.10 GPa | 1170 ksi | cond; ISO 178 |
| 10.4 GPa | 1510 ksi | dry; ISO 178 | |
| Charpy Impact Unnotched | 6.80 J/cm² @Temperature 23.0 °C |
32.4 ft-lb/in² @Temperature 73.4 °F |
dry; ISO 179/1eU |
| 7.00 J/cm² @Temperature 23.0 °C |
33.3 ft-lb/in² @Temperature 73.4 °F |
cond; ISO 179/1eU | |
| Charpy Impact, Notched | 1.10 J/cm² @Temperature 23.0 °C |
5.23 ft-lb/in² @Temperature 73.4 °F |
dry; ISO 179/1eA |
| 1.40 J/cm² @Temperature 23.0 °C |
6.66 ft-lb/in² @Temperature 73.4 °F |
cond; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 20.0 µm/m-°C | 11.1 µin/in-°F | dry; ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 60.0 µm/m-°C | 33.3 µin/in-°F | dry; ISO 11359-1/-2 |
| Melting Point | 260 °C | 500 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 243 °C | 469 °F | dry; ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 258 °C | 496 °F | dry; ISO 75-1/-2 |
| Flammability, UL94 | V-0 @Thickness 0.800 mm |
V-0 @Thickness 0.0315 in |
dry; IEC 60695-11-10 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 3.00e+14 ohm-cm | >= 3.00e+14 ohm-cm | dry; IEC 60093 |
| Surface Resistance | 4.00e+14 ohm | 4.00e+14 ohm | cond; IEC 60093 |
| Dielectric Constant | 4.0 @Frequency 100 Hz |
4.0 @Frequency 100 Hz |
dry; IEC 60250 |
| 4.0 @Frequency 1.00e+6 Hz |
4.0 @Frequency 1.00e+6 Hz |
dry; IEC 60250 | |
| Dielectric Strength | 23.0 kV/mm | 584 kV/in | dry; IEC 60243-1 |
| Dissipation Factor | 0.0090 @Frequency 100 Hz |
0.0090 @Frequency 100 Hz |
dry; IEC 60250 |
| 0.019 @Frequency 1.00e+6 Hz |
0.019 @Frequency 1.00e+6 Hz |
dry; IEC 60250 | |
| Comparative Tracking Index | 175 V | 175 V | dry; IEC 60112 |
Users viewing this material also viewed the following:
- PolyOne LubriOne™ AT-000/10T 2S Acetal (POM) Copolymer
- Phillips 66 COPYLENE® CH200LN Polypropylene, Homopolymer, CR, Antistat, Nucleated, Injection Molding
- Huntsman IROGRAN® A 98 P 4535 TPU-Polyether
- Momentive Performance Materials Addisilâ„¢ 440 E Healthcare Extrusion Grade Heat Cured Rubber
- Momentive Performance Materials IS808 Translucent Adhesive Sealant, General Purpose Paste
- Polyram RamSter PF320G6 PBT, 30% Glass Fiber, Flame Retardant
- Trelleborg E646 EPDM Rubber
- Silberline Sparkle Silvet® 960-20-J
- RheTech Products HP508-01UV 15% Talc Reinforced High Performance Polypropylene Copolymer, UV Stabilized, Black
Copyright © lookpolymers.com All Rights Reserved