Daikin DAI-EL G-952 Fluoroelastomer Terpolymer, Peroxide Curable Grade, 69% Fluorine Content

Category	Polymer , Thermoset , Fluoropolymer, TS , Thermoset Fluoroelastomer , Rubber or Thermoset Elastomer (TSE)
Manufacturer	Daikin Industries
Trade Name	DAI-EL
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Daikin DAI-EL G-952 Fluoroelastomer Terpolymer, Peroxide Curable Grade, 69% Fluorine Content.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Offers excellent chemical and steam resistance. Offers good mechanical characteristics.Features: Good solvent resistance and low-temperature characteristics.Information provided by Daikin Industries.

Physical Properties	Metric	English	Comments
Specific Gravity	3.00 g/cc	3.00 g/cc	at 25°C
Mooney Viscosity	40 @Temperature 121 °C	40 @Temperature 250 °F	ML 1+10

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	67	67	Peak value, at 25°C
Tensile Strength at Break	24.0 MPa	3480 psi
Tensile Strength, Yield	2.30 MPa @Strain 100 %	334 psi @Strain 100 %
Elongation at Break	320 %	320 %
Tear Strength	19.6 kN/m	112 pli	at 25°C
Compression Set	13 %	13 %	70 hours at 25°C
	11 % @Temperature 100 °C	11 % @Temperature 212 °F	70 hours
	15 % @Temperature 175 °C	15 % @Temperature 347 °F	70 hours
	28 % @Temperature 200 °C	28 % @Temperature 392 °F	70 hours

Thermal Properties	Metric	English	Comments
Minimum Service Temperature, Air	-14.0 °C	6.80 °F	TR test, TR10
	-12.5 °C	9.50 °F	Gehman torsion test, T10
	-8.00 °C	17.6 °F	TR test, TR70
	-7.50 °C	18.5 °F	Gehman torsion test, T2
Brittleness Temperature	-26.0 °C	-14.8 °F

Processing Properties	Metric	English	Comments
Processing Temperature	160 °C	320 °F	Cure Measuring Temperature
Cure Time	2.00 min	0.0333 hour	Curelastmeter