DSM Novamid® 1015G35 NAT PA6-GF35
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 40% Glass Fiber Filled |
| Manufacturer | DSM Engineering Plastics |
| Trade Name | Novamid® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DSM Novamid® 1015G35 NAT PA6-GF35.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
35% Glass Reinforced, Injection Molding
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.41 g/cc | 0.0509 lb/in³ | dry; ISO 1183 |
| Moisture Absorption | 2.30 % | 2.30 % | Sim. To ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm | 0.0030 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.010 cm/cm | 0.010 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 120 MPa | 17400 psi | cond; ISO 527-1/-2 |
| 190 MPa | 27600 psi | dry; ISO 527-1/-2 | |
| Elongation at Break | 2.6 % | 2.6 % | dry; ISO 527-1/-2 |
| 6.0 % | 6.0 % | cond; ISO 527-1/-2 | |
| Tensile Modulus | 6.30 GPa | 914 ksi | cond; ISO 527-1/-2 |
| 11.4 GPa | 1650 ksi | dry; ISO 527-1/-2 | |
| Flexural Strength | 195 MPa | 28300 psi | cond; ISO 178 |
| 295 MPa | 42800 psi | dry; ISO 178 | |
| Flexural Modulus | 6.60 GPa | 957 ksi | cond; ISO 178 |
| 9.80 GPa | 1420 ksi | dry; ISO 178 | |
| Charpy Impact Unnotched | 9.60 J/cm² @Temperature 23.0 °C |
45.7 ft-lb/in² @Temperature 73.4 °F |
dry; ISO 179/1eU |
| 10.8 J/cm² @Temperature 23.0 °C |
51.4 ft-lb/in² @Temperature 73.4 °F |
cond; ISO 179/1eU | |
| Charpy Impact, Notched | 1.40 J/cm² @Temperature 23.0 °C |
6.66 ft-lb/in² @Temperature 73.4 °F |
dry; ISO 179/1eA |
| 2.40 J/cm² @Temperature 23.0 °C |
11.4 ft-lb/in² @Temperature 73.4 °F |
cond; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 220 °C | 428 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | dry; ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 206 °C | 403 °F | dry; ISO 75-1/-2 |
| Flammability, UL94 | HB @Thickness 0.800 mm |
HB @Thickness 0.0315 in |
dry; IEC 60695-11-10 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 7.00e+14 ohm-cm | 7.00e+14 ohm-cm | dry; IEC 60093 |
| Surface Resistance | 3.00e+13 ohm | 3.00e+13 ohm | cond; IEC 60093 |
| Dielectric Constant | 4.0 @Frequency 100 Hz |
4.0 @Frequency 100 Hz |
dry; IEC 60250 |
| 4.0 @Frequency 1.00e+6 Hz |
4.0 @Frequency 1.00e+6 Hz |
dry; IEC 60250 | |
| Dielectric Strength | 23.0 kV/mm | 584 kV/in | dry; IEC 60243-1 |
| Dissipation Factor | 0.011 @Frequency 100 Hz |
0.011 @Frequency 100 Hz |
dry; IEC 60250 |
| 0.019 @Frequency 1.00e+6 Hz |
0.019 @Frequency 1.00e+6 Hz |
dry; IEC 60250 | |
| Comparative Tracking Index | 400 V | 400 V | dry; IEC 60112 |
Users viewing this material also viewed the following:
- Nitriflex NP-1121 Powdered Nitrile
- LG Chemical RS657L ABS, Chemical Resistance to Cyclopentane, Low Specific Gravity
- Minelco 47 Sarca Chamottes
- SABIC Innovative Plastics LNP Stat-kon EE008E PEI
- Techmer ES HiFill® PA6/6 LGF60 HS L BK 12 mm
- A. Schulman CP80-01 Linear Low-Density Polyethylene
- Plastics Group Polifil® GFPPCC-20 20% Glass Reinforced Polypropylene
- Diamond Polymers ABS 9950 Injection Molding Grade
- Epoxy Technology EPO-TEK® B9021 Epoxy Paste
- Atom Adhesives AA-BOND 2104 Epoxy Adhesive
Copyright © lookpolymers.com All Rights Reserved