Schmolz + Bickenbach UGIMA® 316/316L Stainless Steel Bar

Category Metal , Ferrous Metal , Stainless Steel , T 300 Series Stainless Steel
Manufacturer Schmolz + Bickenbach (Swiss Steel International)
Trade Name UGIMA®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Schmolz + Bickenbach UGIMA® 316/316L Stainless Steel Bar.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: 316/316L UGIMA® is Ugitech’s improved machining grade produced only by Ugitech. It is identical in every way to regular 316L, except with respect to machinability. 316/316L UGIMA® represents the latest generation of Ugitech's popular UGIMA® family of high machinability grades. Through the use of new and beneficial modifications to the steel-making process, 316/316L UGIMA® builds upon the proprietary UGIMA® manufacturing process to allow for excellent machinability across a wider range of operations and cutting conditions. When compared with older Ugima® versions, 316/316L UGIMA® is a technologically advanced product that will allow for superior machinability at both low and high speeds, in cam-driven and CNC machines, and with high-speed steel or carbide tooling. Machine shops using 316/316L UGIMA® have experienced consistent success regardless of machine, operation, tooling, or cutting conditions. From lot to lot, 316/316L3 UGIMA® is engineered to give the same high performance every time without surpriseInformation provided by Schmolz + Bickenbach
Physical Properties Metric English Comments
Density 8.03 g/cc
0.290 lb/in³
Mechanical Properties Metric English Comments
Hardness, Brinell 160 - 190

@Thickness >=25.4 mm
 160 - 190

@Thickness >=1.00 in
 Turned Bars
190 - 220

@Thickness <=25.4 mm
 190 - 220

@Thickness <=1.00 in
 Cold Drawn Bars
Tensile Strength 517 - 655 MPa

@Thickness >=25.4 mm
 75000 - 95000 psi

@Thickness >=1.00 in
 Turned Bars
621 - 793 MPa

@Thickness <=25.4 mm
 90000 - 115000 psi

@Thickness <=1.00 in
 Cold Drawn Bars
Tensile Strength, Yield >= 207 MPa

@Strain 0.200 %,
Thickness >=25.4 mm
 >= 30000 psi

@Strain 0.200 %,
Thickness >=1.00 in
 Turned Bars
345 - 655 MPa

@Strain 0.200 %,
Thickness <=25.4 mm
 50000 - 95000 psi

@Strain 0.200 %,
Thickness <=1.00 in
 Cold Drawn Bars
Elongation at Yield >= 30 %

@Thickness <=25.4 mm
 >= 30 %

@Thickness <=1.00 in
 Cold Drawn Bars
>= 30 %

@Thickness >=25.4 mm
 >= 30 %

@Thickness >=1.00 in
 Turned Bars
Reduction of Area >= 50 %

@Thickness <=25.4 mm
 >= 50 %

@Thickness <=1.00 in
 Cold Drawn Bars
>= 50 %

@Thickness >=25.4 mm
 >= 50 %

@Thickness >=1.00 in
 Turned Bars
Modulus of Elasticity 164 GPa

@Temperature 100 °C
 23800 ksi

@Temperature 212 °F
 Tension
179 GPa

@Temperature 300 °C
 26000 ksi

@Temperature 572 °F
 Tension
200 GPa

@Temperature 20.0 °C
 29000 ksi

@Temperature 68.0 °F
 Tension
Thermal Properties Metric English Comments
CTE, linear 17.1 µm/m-°C

@Temperature 20.0 - 200 °C
 9.50 µin/in-°F

@Temperature 68.0 - 392 °F
Thermal Conductivity 15.3 W/m-K

@Temperature 20.0 °C
 106 BTU-in/hr-ft²-°F

@Temperature 68.0 °F
Component Elements Properties Metric English Comments
Carbon, C <= 0.030 %
<= 0.030 %
Chromium, Cr 16.5 - 18 %
16.5 - 18 %
Iron, Fe >= 63.545 %
>= 63.545 %
Manganese, Mn <= 2.0 %
<= 2.0 %
Molybdenum, Mo 2.0 - 2.5 %
2.0 - 2.5 %
Nickel, Ni 10.5 - 13 %
10.5 - 13 %
Nitrogen, N <= 0.10 %
<= 0.10 %
Phosphorous, P <= 0.045 %
<= 0.045 %
Silicon, Si <= 0.75 %
<= 0.75 %
Sulfur, S <= 0.030 %
<= 0.030 %
Electrical Properties Metric English Comments
Electrical Resistivity 0.0000730 ohm-cm
0.0000730 ohm-cm
Magnetic Permeability <= 1.03
<= 1.03
at 23% cold work
Processing Properties Metric English Comments
Annealing Temperature 1010 - 1090 °C
1850 - 2000 °F
followed by rapid cooling with forced air or water quenching
Hot-Working Temperature >= 949 °C
>= 1740 °F
Forge
999 - 1200 °C
1830 - 2190 °F
Forging range
1150 - 1220 °C
2100 - 2230 °F
Heat in range
<= 1224 °C
<= 2235 °F
Heat of core during fast forging
Descriptive Properties Value Comments
Corrosion Resistance 5% Sulphuric Acid at 106°F
0.19 mm/year
Acetic Acid
3/4
Boiling 50% Acetic 50% Formic Acids
0.25 mm/year
Boiling Acetic Acid
0.1 mm/year
Boiling Formic Acid
1.4 mm/year
Boiling Nitric Acid
0.25 mm/year
Boiling Phosphoric Acid
0.1 mm/year
H2SO42M
25 µA/cm<sup>2</sup>
Humidity
4/4
NaCl (Saline Mist)
3/4
NaCl 0.86M, 131°F, pH=6.6
175 mV/ECS
NaCl 0.86M, 131°F, pH=6.6
150 mV/ECS
Nitric Acid
3/4
Petroleum
2/4
Petroleum
2/4
Phosphoric Acid
2/4
Seawater
2/4
Sulfuric Acid
2/4