- Acrylonitrile Butadiene Styrene (ABS), Heat Resistant, Molded
- Samsung Cheil Industries Starex® SR-0320 High Heat Resistant Grade ABS
Samsung Cheil Industries Starex® SR-0320 High Heat Resistant Grade ABS
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Heat Resistant, Molded |
| Manufacturer | Samsung, Cheil Industries |
| Trade Name | Starex® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samsung Cheil Industries Starex® SR-0320 High Heat Resistant Grade ABS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Polymer Technology and Services, LLC (PTS).
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.05 g/cc | 0.0379 lb/in³ | ASTM D792 |
| Melt Flow | 6.0 g/10 min @Load 10.0 kg, Temperature 220 °C |
6.0 g/10 min @Load 22.0 lb, Temperature 428 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 110 | 110 | ASTM D785 |
| Tensile Strength, Yield | 51.0 MPa @Thickness 3.17 mm |
7400 psi @Thickness 0.125 in |
ASTM D638 |
| Elongation at Break | 10 % @Thickness 3.17 mm |
10 % @Thickness 0.125 in |
ASTM D638 |
| Flexural Strength | 74.5 MPa @Thickness 3.17 mm |
10800 psi @Thickness 0.125 in |
ASTM D790 |
| Flexural Modulus | 2.34 GPa @Thickness 3.17 mm |
340 ksi @Thickness 0.125 in |
ASTM D790 |
| Izod Impact, Notched | 1.66 J/cm @Thickness 3.17 mm |
3.10 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 98.9 °C @Thickness 6.35 mm |
210 °F @Thickness 0.250 in |
Unannealed; ASTM D648 |
| Vicat Softening Point | 110 °C | 230 °F | Unannealed; ISO R-306 |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
|
| HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
||
| HB @Thickness 6.00 mm |
HB @Thickness 0.236 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 190 - 210 °C | 374 - 410 °F | |
| Middle Barrel Temperature | 220 - 240 °C | 428 - 464 °F | |
| Front Barrel Temperature | 230 - 250 °C | 446 - 482 °F | |
| Melt Temperature | 240 - 260 °C | 464 - 500 °F | |
| Mold Temperature | 40.0 - 80.0 °C | 104 - 176 °F | |
| Drying Temperature | 176 - 194 °C | 349 - 381 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | |
| Injection Pressure | 68.6 - 108 MPa | 9950 - 15600 psi | |
| Back Pressure | 0.689 - 1.38 MPa | 100 - 200 psi | |
| Screw Speed | 60 - 80 rpm | 60 - 80 rpm |
Users viewing this material also viewed the following:
- Proto3000 Objet Digital Materials™ DM_7210 Transparent Prototyping Polymer
- Nilit FRIANYL A63 M2 Nylon 6.6 for injection molding, 2% molybdenum disulphide lubricated
- Lehmann & Voss LUVOCOM® 1-7984 Polyamide 66, with aramid reinforcement and PTFE, heat stabilized
- Samsung Cheil Industries Infino® WP-1069 PC/ABS, Unreinforced
- Styron Magnumâ„¢ 357HP ABS, High Heat
- Fainplast Compounds GA 0179 Flexible PVC, Flame Retardant Sheathing
- CMT Materials REN Shape® 440 Tooling Board, Modeling Board, Adhesive Products
- DSM Arnite® AV2 370 HF PET-GF35
- ExxonMobil Santoprene® 8291-60B500 Thermoplastic Vulcanizate (discontinued **)
- Haynes Hastelloy® C-2000® Bar, Annealed at 2100°F (1149°C)
Copyright © lookpolymers.com All Rights Reserved