DSM EcoPaXX® Q-X07207 PA410-I
| Category | Polymer , Renewable/Recycled Polymer , Thermoplastic , Nylon |
| Manufacturer | DSM Engineering Plastics |
| Trade Name | EcoPaXX® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DSM EcoPaXX® Q-X07207 PA410-I.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Impact Modified
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.05 g/cc | 0.0379 lb/in³ | dry; ISO 1183 |
| Moisture Absorption | 1.70 % | 1.70 % | Sim. To ISO 62 |
| Linear Mold Shrinkage, Flow | 0.028 cm/cm | 0.028 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.018 cm/cm | 0.018 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 35.0 MPa | 5080 psi | cond; ISO 527-1/-2 |
| 50.0 MPa | 7250 psi | dry; ISO 527-1/-2 | |
| Elongation at Break | 30 % | 30 % | dry; ISO 527-1/-2 |
| >= 50 % | >= 50 % | cond; ISO 527-1/-2 | |
| Elongation at Yield | 6.0 % | 6.0 % | dry; ISO 527-1/-2 |
| 20 % | 20 % | cond; ISO 527-1/-2 | |
| Tensile Modulus | 0.940 GPa | 136 ksi | cond; ISO 527-1/-2 |
| 2.00 GPa | 290 ksi | dry; ISO 527-1/-2 | |
| Flexural Strength | 40.0 MPa | 5800 psi | cond; ISO 178 |
| 70.0 MPa | 10200 psi | dry; ISO 178 | |
| Flexural Modulus | 0.950 GPa | 138 ksi | cond; ISO 178 |
| 1.75 GPa | 254 ksi | dry; ISO 178 | |
| Charpy Impact Unnotched | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
cond; ISO 179/1eU |
| NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
dry; ISO 179/1eU | |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
dry; ISO 179/1eU | |
| Charpy Impact, Notched | 2.00 J/cm² @Temperature -30.0 °C |
9.52 ft-lb/in² @Temperature -22.0 °F |
dry; ISO 179/1eA |
| 6.50 J/cm² @Temperature 23.0 °C |
30.9 ft-lb/in² @Temperature 73.4 °F |
dry; ISO 179/1eA | |
| 7.50 J/cm² @Temperature 23.0 °C |
35.7 ft-lb/in² @Temperature 73.4 °F |
cond; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 140 µm/m-°C | 77.8 µin/in-°F | dry; ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 120 µm/m-°C | 66.7 µin/in-°F | dry; ISO 11359-1/-2 |
| Melting Point | 250 °C | 482 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 140 °C | 284 °F | dry; ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C | 167 °F | dry; ISO 75-1/-2 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 5.00e+14 ohm-cm | 5.00e+14 ohm-cm | cond; IEC 60093 |
| >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | dry; IEC 60093 | |
| Dielectric Strength | 33.0 kV/mm | 838 kV/in | cond; IEC 60243-1 |
| 35.0 kV/mm | 889 kV/in | dry; IEC 60243-1 | |
| Comparative Tracking Index | 600 V | 600 V | cond; IEC 60112 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Calculated Bio Based Carbon Content (%) | 56 | ASTM 6866 |
Users viewing this material also viewed the following:
- Polimeri Europa Riblene® GM 20 Low Density Polyethylene - Coating Grade
- Resin Technology Group TIGA 908 Gold Bonder - Low Stress Silver Conductive
- LATI LATILUB 82-01M Nylon 12 Base, 1% Molybdenum Disulfide Self Lubricating Plastic (discontinued **)
- LyondellBasell Astryn 65F5-2 Polypropylene Homopolymer, 20% Calcium Carbonate
- SABIC Innovative Plastics Xenoy® CL200 PBT+PC (Europe-Africa-Middle East)
- A. Schulman PAPERMATCH® T-4228-50 Specialty Masterbatch
- A. Schulman POLYFLAM™ FCB 1236-8555 General Purpose Homopolymer Polypropylene
- A. Schulman POLYFORT™ FPP 3715 Glass Filled Homopolymer Polypropylene
- Asahi Kasei Thermylene® P6-20FG-0753 20% Glass Fiber Reinforced, Heat Stabilized
- Akro-Plastic Akromid® A3 GM 10/20 S1 PA, 10% Glass Filled, 20% Mineral Filled, Cold-Impact Resistant (discont
Copyright © lookpolymers.com All Rights Reserved