ExxonMobil Exact™ 4160 Series Ethylene-based Plastomer Resin
| Category | Polymer , Thermoplastic , Elastomer, TPE |
| Manufacturer | Exxon Chemical |
| Trade Name | EXACT™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | ExxonMobil Exact™ 4160 Series Ethylene-based Plastomer Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Product Description: Exact 4160 is an ethylene-based hexane plastomer produced using ExxonMobil Chemical’s EXXPOL® Catalyst Technology. These resins are designed for blown film applications requiring high impact and puncture resistance. They also exhibit excellent heat sealing performance. Availability: Latin America, North America and South America Applications:Blown Film Information provided by ExxonMobil
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.895 g/cc | 0.0323 lb/in³ | ExxonMobil method |
| Melt Flow | 1.1 g/10 min | 1.1 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Yield, MD | 4.55 MPa | 660 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 4.07 MPa | 590 psi | ASTM D882 |
| Film Elongation at Break, MD | 430 % | 430 % | ASTM D882 |
| Film Elongation at Break, TD | 620 % | 620 % | ASTM D882 |
| Film Elongation at Yield, MD | 10 % | 10 % | ASTM D882 |
| Film Elongation at Yield, TD | 9.0 % | 9.0 % | ASTM D882 |
| Puncture Energy | 7.91 J | 5.83 ft-lb | ExxonMobil Method |
| Elmendorf Tear Strength MD | 150 g | 150 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 280 g | 280 g | ASTM D1922 |
| Dart Drop Test | 1200 g | 2.65 lb | ASTM D1709A |
| Film Tensile Strength at Break, MD | 65.5 MPa | 9500 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 68.9 MPa | 10000 psi | ASTM D882 |
| 1% Secant Modulus, MD | 57.2 MPa | 8300 psi | ASTM D882 |
| 1% Secant Modulus, TD | 64.1 MPa | 9300 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | <= 194 °C | <= 381 °F | Peak Melting Point; ExxonMobil method |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 1.1 % | 1.1 % | ASTM D1003 |
| Gloss | 89 % | 89 % | 45°; ASTM D2457 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Puncture Force | 18 lbf | ExxonMobil Method |
Users viewing this material also viewed the following:
- MV Labs BI800 Bi2O3 Bismuth oxide
- Omnia Plastica PTFE Polytetrafluoroethylene
- Haynes HR-160® alloy, plate, aged 8000 hours at 871°C (1600°F)
- Solvay Specialty Polymers Amodel® AS-1933 HS Polyphthalamide (PPA), 33% Glass Fiber
- Silberline "A" Series A-226
- Teknor Apex APEX® 3315-NT Polyvinyl Chloride, Flexible
- Teknor Apex Monprene® MP-2357-A Thermoplastic Elastomer
- Covestro Bayblend® T 88-2N Polycarbonate/ABS Blend, 10% Glass Fiber
- Arlon LW301Rxx-P0 0.030" (0.762 mm) Self-Fusing Silicone Tape (Triangular, Unsupported) with Poly Interleave
- ExxonMobil Escorene™ AD 0633EH2 Ethylene Vinyl Acetate Copolymer (European Grade)
Copyright © lookpolymers.com All Rights Reserved