Polyram RamOfin PPH301G6NT Polypropylene, 30% Glass Fiber
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 30% Glass Fiber Filler |
| Manufacturer | Polyram |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polyram RamOfin PPH301G6NT Polypropylene, 30% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
30% Glass fiber reinforced polypropylene for injection molding applications. Approved and listed by WRAS Potable Water.Information provided by Polyram.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.0010 - 0.0040 cm/cm | 0.0010 - 0.0040 in/in | ISO 2577 |
| Melt Flow | 4.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
4.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 90.0 MPa | 13100 psi | ISO 527 |
| Elongation at Break | 3.0 % | 3.0 % | ISO 527 |
| Tensile Modulus | 6.00 GPa | 870 ksi | ISO 527 |
| Flexural Strength | 105 MPa | 15200 psi | ISO 178 |
| Flexural Modulus | 5.70 GPa | 827 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 12.5 kJ/m² | 5.95 ft-lb/in² | ISO 180 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 165 °C | 329 °F | ISO 11357 |
| Maximum Service Temperature, Air | 110 °C | 230 °F | Continuous use |
| 140 °C | 284 °F | Short peaks operation | |
| Deflection Temperature at 0.46 MPa (66 psi) | 153 °C | 307 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 145 °C | 293 °F | ISO 75 |
| Flammability, UL94 | HB | HB | |
| Flame Spread | 9.0 mm/min | 0.35 in/min | FMVSS302 |
Users viewing this material also viewed the following:
- MV Labs RH450 (NH4)3RhCl6 Ammonium hexachlororhodate(III)
- SABIC Innovative Plastics Lexan® XHT4143T PC Copolymer (Asia Pacific)
- Polymer Resources AH-GP3 Acetal Homopolymer, High Flow Resin (Unverified Data**)
- H.C. Starck Molybdenum Alloy AFB-3OW, Arc-Cast Forging Billet
- SABIC Innovative Plastics LNP LUBRICOMP WFL34H PBT (Asia Pacific)
- Polyram Polytron P30N01 Homopolymer Polypropylene, Chemically Coupled 30% Long Fiber
- Fainplast Compounds GS 6612 Flexible PVC, Injection Molding for Footwear
- Amco PRIMATOP PP HOMO 350NA Injection Molding Polypropylene
- ATG s.r.l. ACM Polyacrylic Rubber
- BASF Thiodiglycol Ultra
Copyright © lookpolymers.com All Rights Reserved