Covestro Bayblend® T65 XF Polycarbonate + ABS
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) |
| Manufacturer | Covestro |
| Trade Name | Bayblend® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Covestro Bayblend® T65 XF Polycarbonate + ABS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
General purpose injection molding gradeVicat/B 120 temperature = 120 °Cimproved flowability compared to T65PreprocessingMax. Water content
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in³ | ISO 1183 |
| 0.945 g/cc @Temperature 260 °C |
0.0341 lb/in³ @Temperature 500 °F |
Melt | |
| Water Absorption | 0.70 % | 0.70 % | Similar to ISO 62 |
| Moisture Absorption at Equilibrium | 0.20 % | 0.20 % | Similar to ISO 62 |
| Melt Flow | 17 g/10 min @Load 5.00 kg, Temperature 260 °C |
17 g/10 min @Load 11.0 lb, Temperature 500 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 54.0 MPa | 7830 psi | ISO 527-1/-2 |
| Elongation at Yield | 4.4 % | 4.4 % | ISO 527-1/-2 |
| Tensile Modulus | 2.40 GPa | 348 ksi | ISO 527-1/-2 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 80.0 µm/m-°C | 44.4 µin/in-°F | ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 85.0 µm/m-°C | 47.2 µin/in-°F | ISO 11359-1/-2 |
| Specific Heat Capacity | 1.76 J/g-°C | 0.421 BTU/lb-°F | Melt |
| Thermal Conductivity | 0.141 W/m-K | 0.979 BTU-in/hr-ft²-°F | Melt |
| Deflection Temperature at 0.46 MPa (66 psi) | 122 °C | 252 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 102 °C | 216 °F | ISO 75-1/-2 |
| Vicat Softening Point | 118 °C | 244 °F | 50°C/h 50N; ISO 306 |
| Flammability, UL94 | HB @Thickness 0.900 mm |
HB @Thickness 0.0354 in |
IEC 60695-11-10 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+13 ohm-cm | >= 1.00e+13 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | IEC 60093 |
| Dielectric Constant | 3.0 @Frequency 1.00e+6 Hz |
3.0 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 3.1 @Frequency 100 Hz |
3.1 @Frequency 100 Hz |
IEC 60250 | |
| Dielectric Strength | 35.0 kV/mm | 889 kV/in | IEC 60243-1 |
| Dissipation Factor | 0.0030 @Frequency 100 Hz |
0.0030 @Frequency 100 Hz |
IEC 60250 |
| 0.0085 @Frequency 1.00e+6 Hz |
0.0085 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| Comparative Tracking Index | 250 V | 250 V | IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 240 - 280 °C | 464 - 536 °F | |
| 260 °C | 500 °F | Injection Molding; ISO 294 | |
| Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F | |
| 80.0 °C | 176 °F | Injection Molding; ISO 10724 | |
| Ejection Temperature | 120 °C | 248 °F | |
| Injection Velocity | 240 mm/sec | 9.45 in/sec | ISO 294 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Availability | Asia Pacific | |
| Europe | ||
| Near East/Africa | ||
| South and Central America | ||
| Eff. thermal diffusivity (m²/s) | 8.48E-08 | |
| Feature | Release agent | |
| Form | Pellets | |
| Process | Injection Molding |
Users viewing this material also viewed the following:
- Plastcom SLOVALEN PH 69 GF 40 Polypropylene Homopolymer, 40% Glass Fiber
- MV Labs TL100 TlC2H3O2 Thallium(I) acetate
- Ovation Polymers UTTAP QU BM513 GF BM Nylon, 13% Glass Reinforced
- Solvay Specialty Polymers Torlon® 4301 Polyamide-imide (PAI) (Unverified Data**)
- Lucas-Milhaupt Silvaloy® A20 Brazing Alloy
- Solvay Technyl® C 206 Nylon 6, EH0
- A. Schulman POLYBATCH™ White LL8855 GP Concentrate Based In LLDPE
- Borealis Daplen™ EE065AI Polypropylene Elastomer Modified
- Eastman Cadence™ GS2 Copolyester for film calendering
- Carpenter BioDur™ 316LS Stainless Medical Implant Alloy, 48% Cold Worked
Copyright © lookpolymers.com All Rights Reserved