Samsung Cheil Industries Infino® UF-1013 PC, Unreinforced FR
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Molded |
| Manufacturer | Samsung, Cheil Industries |
| Trade Name | Infino® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samsung Cheil Industries Infino® UF-1013 PC, Unreinforced FR.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Samsung Cheil Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.25 g/cc | 1.25 g/cc | ASTM D792 |
| Melt Flow | 18 g/10 min @Load 10.0 kg, Temperature 220 °C |
18 g/10 min @Load 22.0 lb, Temperature 428 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 119 | 119 | ASTM D785 |
| Tensile Strength at Break | 56.9 MPa | 8250 psi | 50 mm/min; ASTM D638 |
| Tensile Strength, Yield | 63.7 MPa | 9250 psi | 50 mm/min; ASTM D638 |
| Elongation at Break | 83 % | 83 % | 50 mm/min; ASTM D638 |
| Tensile Modulus | 2.16 GPa | 313 ksi | 50 mm/min; ASTM D638 |
| Flexural Strength | 89.2 MPa | 12900 psi | 2.8 mm/min; ASTM D638 |
| Flexural Modulus | 2.26 GPa | 327 ksi | 2.8 mm/min; ASTM D638 |
| Izod Impact, Notched | 6.18 J/cm @Thickness 6.35 mm |
11.6 ft-lb/in @Thickness 0.250 in |
ASTM D256 |
| 7.85 J/cm @Thickness 3.17 mm |
14.7 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 103 °C @Thickness 6.40 mm |
217 °F @Thickness 0.252 in |
ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 95.0 °C @Thickness 6.40 mm |
203 °F @Thickness 0.252 in |
ASTM D648 |
| Vicat Softening Point | 108 °C | 226 °F | B/50; ISO R306 |
| 108 °C | 226 °F | B/120; ISO R306 | |
| Flammability, UL94 | V-0 @Thickness 0.800 mm |
V-0 @Thickness 0.0315 in |
Users viewing this material also viewed the following:
- S&E Specialty Polymers GA-1021-CJ PVC
- MarkeTech H-2 Honeycomb Ceramic
- Solvay Specialty Polymers Kalix® 9945 HFFR Polyamide, High Performance (HPPA), 45% Glass Fiber
- Saint-Gobain Norton® Fluorglas® Chemfilm® R167 Extruded Expanded PTFE Film (0.008" thick)
- A. Schulman POLYBATCH™ Green 3015 Concentrate Based In Polyethylene
- Universal Wire Works 4043 (AMS 4190) Aluminum Alloy Filler Metal
- A. Schulman LB502-01 High Molecular Weight, High-Density Polyethylene Copolymer
- TSE Industries Millathane® 5004 Millable Polyurethane Elastomer, Hardness 65A
- Bisalloy Steels BisPlate 500 Thickness 6-100 mm
Copyright © lookpolymers.com All Rights Reserved