- Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 122 °C
Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 122 °C Product List
Thermal PropertiesTips: 30 items are displayed at most.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) |
122
°C @Thickness 3.18 mm |
252
°F @Thickness 0.125 in |
Unannealed; ASTM D648 |
|
PolyOne Maxxam™ PD 20 TF Black Polypropylene, Unspecified (PP, Unspecified)
PolyOne's Maxxam™ family of polypropylene- and polyethylene-based products covers a wide range of applications, markets and performance requirements. Standard grades are compounded with calcium car..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 122 °C | 252 °F | 120°C/h; ISO 75/1 |
|
Polykemi AB SCANFILL FOIL ABYX52C1 PP/PE, Thermoforming Grade
Information provided by Polykemi AB
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 122 °C | 252 °F | ASTM D648 |
|
PolyMirae Moplen HP640N Injection Molding Grade Polypropylene
Moplen HP640N is the polypropylene homopolymer manufactured by PMC under the license of BASELL using the Spheripol process. Moplen HP640N is a homopolymer particularly suitable for injection molding..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
122
°C @Thickness 3.20 mm |
252
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics Lexan® HFD1711 PC Copolymer
25 MFR LEXAN High Flow Ductile Copolymer
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
122
°C @Thickness 3.20 mm |
252
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics Lexan® HPF1 PC Copolymer
25 MFR LEXAN High Flow Ductile Copolymer Healthcare Grade
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 122 °C | 252 °F | 120°C/h; ISO 75/1 |
|
Polykemi AB POLYfill PPH T4030 Polypropylene Homopolymer, Mineral Reinforced
Information provided by Polykemi AB
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
122
°C @Thickness 3.20 mm |
252
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics LNP LUBRICOMP MX91206 PP
LNP* Lubricomp* MX91206 is a compound based on Polypropylene containing proprietary fillers. Added feature of this grade is: Wear Resistant.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 122 °C | 252 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
|
SABIC Innovative Plastics Xylex HX7409HP PC+POLYESTER (Europe-Africa-Middle East)
Low flow, polycarbonate/Polyester alloy; contains mold release. For medical devices and pharmaceutical applications. Healthcare management of change (MoC), biocompatible (ISO 10993 or USP Class VI)..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 122 °C | 252 °F | ISO 75 |
|
Teijin Multilon DN-1520B Filler Reinforced Type, Halogen-Free Flame Resistant PC/ABS Polymer Alloy
Halogen-free flame retardant PC/ABS polymer alloy, and is also antimony-free. It has improved stiffness through the addition of 20 % filler. Improved stiffness and high fluidity realizes a thin wall..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 122 °C | 252 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
|
SABIC Innovative Plastics LNP THERMOCOMP MH0500C PP
LNP* THERMOCOMP* MH0500C is a compound based on Polypropylene resin. Added feature of this material is: High Specific Gravity.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 122 °C | 252 °F | ASTM D648 |
|
ScanTube PTFE Tubing
Information provided by ScanTube, Inc.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 122 °C | 252 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
|
SABIC Innovative Plastics NORYL PX0844 PPE+PS
PPE+PS blend. Unfilled. UL94 HB rated. Low water absorption. Hydrolytic stability. Dimensional stability.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
122
°C @Thickness 3.17 mm |
252
°F @Thickness 0.125 in |
ISO 75 |
|
A. Schulman FORMION™ FI 233 15% Mineral Reinforced Ionomer / Nylon Alloy
DescriptionFormion® FI 233 is an injection molding grade, 15% mineral reinforced Ionomer / Nylon alloy, which has been formulated for high scratch resistance, heat resistance and high stiffness. A..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 122 °C | 252 °F | ASTM D648 |
|
Plastics Group Polifil® RMT-30 30% Talc-Reinforced Polypropylene, High Impact
Polifil® RMT series compounds are high impact polypropylenes reinforced with asbestos-free talc. In addition to high impact strength, they possess a high flex modulus and high heat deflection resis..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
122
°C @Thickness 3.17 mm |
252
°F @Thickness 0.125 in |
ISO 75 |
|
A. Schulman FORMION™ FI 233 15% Mineral Reinforced Ionomer / Nylon Alloy
DescriptionFormion® FI 233 is an injection molding grade, 15% mineral reinforced Ionomer / Nylon alloy, which has been formulated for high scratch resistance, heat resistance and high stiffness. A..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 122 °C | 252 °F | ASTM D648 |
|
A. Schulman VOLOY™ 461 Glass Reinforced, Flame Retardant PBT Alloy
Information provided by A. Schulman.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
122
°C @Thickness 3.17 mm |
252
°F @Thickness 0.125 in |
ISO 75 |
|
A. Schulman FORMION™ FI 233 15% Mineral Reinforced Ionomer / Nylon Alloy
DescriptionFormion® FI 233 is an injection molding grade, 15% mineral reinforced Ionomer / Nylon alloy, which has been formulated for high scratch resistance, heat resistance and high stiffness. A..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 122 °C | 252 °F | ISO 75-1/-2 |
|
Covestro Bayblend® T65 Polycarbonate + ABS
General purpose injection molding gradeVicat/B 120 temperature = 120 °Cgood low temperature impact strengthPreprocessingMax. Water content
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 122 °C | 252 °F | ASTM D648 |
|
Aclo Accutech Polypropylene Homopolymer HP0334M30CL Mica Reinforced Coupled |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 122 °C | 252 °F | ASTM D648 |
|
Aclo Accutech Polypropylene Homopolymer HP0336W30L Wollastonite Reinforced |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 122 °C | 252 °F | ASTM D648 |
|
Carmel Olefins CAPILENE® G 70 TF Polypropylene Homopolymer
Description: CAPILENE® G 70 TF is a nucleated polypropylene homopolymer intended for sheet extrusion and thermoforming applications. This grade exhibits high stiffness, high gloss, good contact t..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 122 °C | 252 °F | |
|
BASF Luranyl® KR 2404 Polyphenylene Ether + Styrene-Butadiene Blend
Base grade with high heat deformation resistance and a balanced combination of stiffness and toughness. Uses include: steering-wheel covers and heater controls.Data was collected by ISO methods and..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 122 °C | 252 °F | ASTM D648 |
|
Aclo Accutech Polypropylene Homopolymer HP0339T20L1 Talc Reinforced |
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
122
°C @Thickness 3.20 mm |
252
°F @Thickness 0.126 in |
unannealed; ASTM D 648 |
|
SABIC Innovative Plastics Lexan® EXRL0681 PC Copolymer
25 MFR LEXAN High Flow Ductile CopolymerThis data was supplied by SABIC-IP for the Americas region.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
122
°C @Thickness 3.20 mm |
252
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics Lexan® HFD1731 PC Copolymer (Asia Pacific)
25 MFR LEXAN High Flow Ductile Copolymer UV-stabilized, available in transparent colors only
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
122
°C @Thickness 3.20 mm |
252
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics Lexan® ML1661 PC Copolymer (Asia Pacific)
Medium-flow impact-modified light-shielding high-flow-ductile PC copolymer. Available in white color only.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 122 °C | 252 °F | ISO 75-2 |
|
Borealis Bormod™ HF955MO Polypropylene Homopolymer for Injection Molding
Bormod HF955MO is a high modulus polypropylene homopolymer. Bormod HF955MO is especially developed within the proprietary Borstar technology. The grade utilizes the unique Borstar reactor design c..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 122 °C | 252 °F | 120°C/h; ISO 75/1 |
|
Polykemi AB POLYfill PPH TS2040 Polypropylene Homopolymer, Mineral Reinforced
Information provided by Polykemi AB
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
122
°C @Thickness 3.20 mm |
252
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics Lexan® HFD1711 PC Copolymer (Europe-Africa-Middle East)
25 MFR LEXAN High Flow Ductile Copolymer
|
|||