Clariant Renol 6608-LLT Nylon 66, High Impact Modified, Lubricated, Low Temp Impact
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Impact Grade |
| Manufacturer | Clariant |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Clariant Renol 6608-LLT Nylon 66, High Impact Modified, Lubricated, Low Temp Impact.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by Clariant Masterbatches
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.09 g/cc | 0.0394 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.014 - 0.019 cm/cm | 0.014 - 0.019 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 42.1 MPa | 6100 psi | ASTM D638 |
| Elongation at Yield | 60 % | 60 % | ASTM D638 |
| Flexural Yield Strength | 51.7 MPa | 7500 psi | ASTM D790 |
| Flexural Modulus | 1.52 GPa | 220 ksi | ASTM D790 |
| Izod Impact, Notched | 5.34 J/cm @Temperature -40.0 °C |
10.0 ft-lb/in @Temperature -40.0 °F |
ASTM D256 |
| 9.08 J/cm @Temperature 22.8 °C |
17.0 ft-lb/in @Temperature 73.0 °F |
ASTM D256 | |
| Gardner Impact | 12.2 J @Temperature -40.0 °C |
9.00 ft-lb @Temperature -40.0 °F |
ASTM D3673 |
| 38.0 J @Temperature 22.8 °C |
28.0 ft-lb @Temperature 73.0 °F |
ASTM D3673 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 71.1 °C | 160 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 266 - 288 °C | 510 - 550 °F | |
| Mold Temperature | 65.6 - 93.3 °C | 150 - 200 °F | |
| Dry Time | 2 - 4 hour @Temperature 79.4 °C |
2 - 4 hour @Temperature 175 °F |
to ensure moisture content is less than 0.2% |
| Injection Pressure | 4.96 - 8.27 MPa | 720 - 1200 psi | Secondary |
| 8.27 - 13.8 MPa | 1200 - 2000 psi | Initial | |
| Back Pressure | 0.345 - 1.72 MPa | 50.0 - 250 psi | |
| Shot Size | 30 - 80 % | 30 - 80 % | |
| Screw Speed | 20 - 100 rpm | 20 - 100 rpm |
Users viewing this material also viewed the following:
- Karina E CAK 85-48/1-F Black PVC Compound
- Huntsman Euredur 43 S Cycloaliphatic Amine
- MetalTek J92110 15-5 PH® Precipitation Hardening Steel
- Latrobe Knocorâ„¢ Hot Work Tool Steel
- Westlake Elevate™ DA528AA 18.5% Ethylene Vinyl Acetate Copolymer
- Dow DOWLEX™ IP-41 High Density Polyethylene
- Braskem LL5800N LLDPE Blown Film Extrusion Polyethylene Copolymer
- Arkema Group LOTADER® 3200 Terpolymer Ethylene - Acrylic Ester - Maleic Anhydride
- CeramTec B 40 Alumina, 99.1%
Copyright © lookpolymers.com All Rights Reserved