Clariant PA131 Nylon 66, Highly Impact Modified
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Impact Grade |
| Manufacturer | Clariant |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Clariant PA131 Nylon 66, Highly Impact Modified.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by Clariant Masterbatches
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.08 g/cc | 1.08 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.020 cm/cm | 0.020 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 44.8 MPa | 6500 psi | ASTM D638 |
| Flexural Yield Strength | 66.2 MPa | 9600 psi | ASTM D790 |
| Flexural Modulus | 1.72 GPa | 250 ksi | ASTM D790 |
| Izod Impact, Notched | 7.74 J/cm @Temperature 22.8 °C |
14.5 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 215 °C | 419 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 71.0 °C | 160 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 266 - 293 °C | 510 - 560 °F | |
| Mold Temperature | 65.6 - 93.3 °C | 150 - 200 °F | |
| Dry Time | 2 - 4 hour @Temperature 79.4 °C |
2 - 4 hour @Temperature 175 °F |
to ensure moisture content is less than 0.2% |
| Injection Pressure | 4.96 - 8.27 MPa | 720 - 1200 psi | Secondary |
| 8.27 - 13.8 MPa | 1200 - 2000 psi | Initial | |
| Back Pressure | 0.345 - 1.72 MPa | 50.0 - 250 psi | |
| Shot Size | 30 - 80 % | 30 - 80 % | |
| Screw Speed | 20 - 100 rpm | 20 - 100 rpm |
Users viewing this material also viewed the following:
- LyondellBasell Petrothene® NA271009 Medium Density Polyethylene
- A. Schulman POLYBATCH™ Grey LL80316/3 Concentrate Based In LLDPE
- PlastxWorld CEVIAN® VGR10 10% GF ABS
- Goodfellow Havar® High-Strength Non-Magnetic Cobalt-Base Alloy
- Tra-Con Tra-Bond 2248 High Temperature Epoxy Staking Adhesive
- Cossa Polimeri ESTACARB 1060 V0 HF Flame Retardant Polycarbonate
- AK Steel Aluminized Carbon Steel, Commercial Steel (CS Type B), Standard Grade
- Lushan PR320 Adhesive Resin for Aluminum Plastic Composite Pipe
- Multibase Multibatch® ME 50024 Anti-blocking Masterbatch
Copyright © lookpolymers.com All Rights Reserved