Clariant 66G43HLS-Black Nylon 66, 43% Glass Fiber Reinforced, Heat Stabilized, Lubricated
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 40% Glass Fiber Filled |
| Manufacturer | Clariant |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Clariant 66G43HLS-Black Nylon 66, 43% Glass Fiber Reinforced, Heat Stabilized, Lubricated.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by Clariant Masterbatches
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.46 g/cc | 0.0527 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0020 - 0.0060 cm/cm | 0.0020 - 0.0060 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 165 MPa | 24000 psi | ASTM D638 |
| Elongation at Yield | 4.0 % | 4.0 % | ASTM D638 |
| Flexural Yield Strength | 234 MPa | 34000 psi | ASTM D790 |
| Flexural Modulus | 11.0 GPa | 1600 ksi | ASTM D790 |
| Izod Impact, Notched | 0.854 J/cm @Temperature 22.8 °C |
1.60 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 257 °C | 494 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 253 °C | 487 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 249 - 282 °C | 480 - 540 °F | |
| Middle Barrel Temperature | 254 - 288 °C | 490 - 550 °F | |
| Front Barrel Temperature | 260 - 293 °C | 500 - 560 °F | |
| Nozzle Temperature | 266 - 299 °C | 510 - 570 °F | |
| Melt Temperature | 260 - 293 °C | 500 - 560 °F | |
| Mold Temperature | 79.4 - 135 °C | 175 - 275 °F | |
| Dry Time | 2 - 4 hour @Temperature 79.4 °C |
2 - 4 hour @Temperature 175 °F |
to avoid degradation of mechanical properties |
| Injection Pressure | 4.96 - 8.27 MPa | 720 - 1200 psi | Secondary |
| 8.27 - 13.8 MPa | 1200 - 2000 psi | Initial | |
| Back Pressure | 0.172 - 0.345 MPa | 25.0 - 50.0 psi | |
| Shot Size | 30 - 80 % | 30 - 80 % | |
| Screw Speed | 75 rpm | 75 rpm |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics LNP FARADEX AS003 ABS (Asia Pacific)
- Shandong Dongyue Shenzhou New Material Co CHF085 Perfluorosulfonic Acid Ion-Exchange Resin (PFSA)
- Teknor Apex Telcar® TL-1446G Thermoplastic Elastomer
- A. Schulman PP 1259 Polypropylene Medium Impact Polypropylene
- A. Schulman FORMION™ FI 396 Ionomer
- Dow 5E16S Polypropylene Homopolymer Resin
- Fainplast Compounds GS 75/T Flexible PVC, Injection Molding for Footwear
- Arlon 0.029" (0.7366 mm) Flexible Heater Silicone with Fiberglass Substrate (55579A028)
- Polyram RamShine PAS703 ASA, UV Stabilized
Copyright © lookpolymers.com All Rights Reserved